High-wear-resistant flame-retardant fabric and preparation method thereof

A flame retardant fabric, high wear resistance technology, applied in the field of textile fabrics, can solve the problems of poor flame retardant performance, poor wear resistance, short service life, etc., achieve good dispersion compatibility, excellent wear resistance, improve The effect of mechanical properties

Pending Publication Date: 2020-04-10
ZHEJIANG SHENGLI TEXTILE CO LTD
View PDF12 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] 1. Poor flame retardant performance;
[0008] 2. Poor wear resistance, easy to be scratched, resulting in short service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-wear-resistant flame-retardant fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065]A high wear-resistant and flame-retardant fabric, the high wear-resistant and flame-retardant fabric is made of high wear-resistant and flame-retardant fibers through a knitting process;

[0066] The high wear-resistant flame-retardant fiber is made of raw materials including the following parts by weight:

[0067] 70-78 parts of polyethylene terephthalate,

[0068] 16-20 parts of polypentamethylene adipate,

[0069] 10-14 parts of phenylene ether silicone rubber,

[0070] 1.8 to 2.2 parts of graphene nanosheets,

[0071] 2 to 3 parts of glass fiber,

[0072] 2 to 3 parts of fumed silica,

[0073] 3-5 parts of dispersant,

[0074] 4-6 parts of chitosan sodium phosphate.

[0075] Preferably, the high wear-resistant flame-retardant fiber is made of raw materials including the following parts by weight:

[0076] 74 parts of polyethylene terephthalate,

[0077] 18 parts of polypentamethylene adipate,

[0078] 12 parts of phenylene ether silicone rubber,

[0079] Na...

Embodiment 2

[0096] A high wear-resistant and flame-retardant fabric, the high wear-resistant and flame-retardant fabric is made of high wear-resistant and flame-retardant fibers through a knitting process;

[0097] The high wear-resistant flame-retardant fiber is made of raw materials including the following parts by weight:

[0098] 70 parts of polyethylene terephthalate,

[0099] 16 parts of polypentamethylene adipate,

[0100] 10 parts of phenylene ether silicone rubber,

[0101] 1.8 parts of nano-graphene sheets,

[0102] 2 parts glass fiber,

[0103] Fumed silica 2 parts,

[0104] 3 parts of dispersant,

[0105] Chitosan Sodium Phosphate 4 parts.

[0106] The high wear-resistant and flame-retardant fiber also includes the following raw materials in parts by weight: 2 parts of oxidized polyethylene.

[0107] The high wear-resistant and flame-retardant fiber also includes the following raw materials in parts by weight: 8 parts of polyurethane elastomer.

[0108] The glass fiber...

Embodiment 3

[0118] A high wear-resistant and flame-retardant fabric, the high wear-resistant and flame-retardant fabric is made of high wear-resistant and flame-retardant fibers through a knitting process;

[0119] The high wear-resistant flame-retardant fiber is made of raw materials including the following parts by weight:

[0120] 78 parts of polyethylene terephthalate,

[0121] 20 parts of polypentamethylene adipate,

[0122] 14 parts of phenylene ether silicone rubber,

[0123] 2.2 parts of nano-graphene sheets,

[0124] 3 parts glass fiber,

[0125] Fumed silica 3 parts,

[0126] 5 parts of dispersant,

[0127] Chitosan Sodium Phosphate 6 parts.

[0128] The high wear-resistant and flame-retardant fiber also includes the following raw materials in parts by weight: 4 parts of oxidized polyethylene.

[0129] The high wear-resistant and flame-retardant fiber also includes the following raw materials in parts by weight: 12 parts of polyurethane elastomer.

[0130] The glass fibe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-wear-resistant flame-retardant fabric which is prepared from high-wear-resistant flame-retardant fibers through a knitting process. The high-wear-resistant flame-retardant fibers are prepared from the raw materials in parts by weight: 70-78 parts of polyethylene terephthalate, 16-20 parts of poly (adipic acid-1,5-diaminopentane), 10-14 parts of phenyl ether siliconerubber, 1.8-2.2 parts of nano-graphene sheets, 2-3 parts of glass fibers, 2-3 parts of fumed silica, 3-5 parts of a dispersant and 4-6 parts of polysaccharide sodium phosphate. The high-wear-resistantflame-retardant fabric prepared by selecting layers of raw materials, the content of each raw material is optimized, and the high-wear-resistant flame-retardant fabric prepared from the high-wear-resistant flame-retardant fibers through the knitting process is good in flame retardancy, excellent in wear resistance, free of odor, soft in hand feeling and good in resilience.

Description

technical field [0001] The invention relates to the technical field of textile fabrics, in particular to a highly wear-resistant and flame-retardant fabric and a preparation method thereof. Background technique [0002] Fabric is the material used to make clothing. As one of the three elements of clothing, fabrics can not only interpret the style and characteristics of clothing, but also directly affect the color and shape of clothing. Among them, functional fabrics refer to fabrics with certain special properties and uses, such as waterproof, windproof, breathable, moisture-permeable, warm, oil-proof, easy to decontaminate, anti-bacterial and deodorizing, anti-ultraviolet, anti-static, anti-radiation, Anti-flame retardant, high temperature resistance, acid and alkali resistance and other functions. The functional fabrics on the market are mainly clothing fabrics, which are mostly used in outdoor sportswear and high-end casual wear. Among the new functional textile materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F8/14D01F8/12D01F8/16D01F1/07D01F1/10D04B1/16D04B21/00
CPCD01F1/07D01F1/10D01F8/12D01F8/14D01F8/16D04B1/16D04B21/00
Inventor 姚云松
Owner ZHEJIANG SHENGLI TEXTILE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com