A smokeless and sulfur-free fireworks speed regulator and its preparation method

A technology of sulfur fireworks and speed regulation, which is applied in the direction of offensive equipment, explosive processing equipment, non-explosive/non-thermal agent components, etc. It can solve the problems of inconspicuous speed regulation effect, unfavorable environmental protection, and low heat absorption, etc., and achieve significant Economic benefits and social benefits, less steps, no three wastes discharge effect

Active Publication Date: 2020-12-01
BEIJING INSTITUTE OF TECHNOLOGYGY +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patent CN104860787A discloses a burning rate regulator formula in its summary of the invention, including one or more of starch, stearic acid, and fatty acid esters. Under normal circumstances, a small amount of smoke will be generated when burning, which is not conducive to environmental protection
The burning rate regulator disclosed in the patent CN107619364A contains iron oxide, manganese oxide, octyl ferrocene, and cattosine, wherein octyl ferrocene and cattosine will generate smoke during the discharge process, which is not conducive to environmental protection
The burning rate regulator disclosed in the patent CN106187655A is a nano-metal oxide, including nano-copper oxide, nano-nickel oxide, nano-nickel oxide, and nano-titanium dioxide. not obvious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A smokeless and sulfur-free fireworks speed regulator and its preparation method
  • A smokeless and sulfur-free fireworks speed regulator and its preparation method
  • A smokeless and sulfur-free fireworks speed regulator and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A smokeless and sulfur-free fireworks speed regulator, the mass percentages of its components are as follows:

[0025]

[0026] 25g of pseudoboehmite powder, 25g of basic zinc carbonate powder and 15g of calcium bicarbonate powder are fully stirred and mixed in a dry powder mixer to obtain mixed powder A; in the stirring state, 33g of dicyandiamide and 2g of rosin are sequentially mixed Add it into 170g of ethanol, and stir continuously for 30 minutes to obtain the mixed solution B; under the stirring state, slowly add the mixed solution B to the mixed powder A, after the addition is completed, raise the temperature to 50°C, and continue to stir until the material becomes a uniform mud mass The resulting uniform gelatinous mass with moderate hardness is granulated with a twin-screw granulator, and vacuum-dried at 60°C for 12 hours to obtain the crude product of smokeless and sulfur-free fireworks speed regulator; After the rough product of the smokeless and sulfur-fr...

Embodiment 2

[0028] A smokeless and sulfur-free fireworks speed regulator, the mass percentages of its components are as follows:

[0029]

[0030]

[0031] 560g of pseudo-boehmite powder, 540g of basic zinc carbonate powder and 200g of calcium bicarbonate powder were fully stirred and mixed in a dry powder mixer to obtain mixed powder A; in the stirring state, 600g of dicyandiamide and 100g of rosin were sequentially mixed Add it into 4000g of ethanol, and continue stirring for 45 minutes to obtain a mixed solution B; under stirring, slowly add the mixed solution B to the mixed powder A, after the addition is completed, heat up to 55°C, and continue to stir until the material becomes a uniform mud mass The resulting uniform gelatinous mass with moderate hardness is granulated with a twin-screw granulator, and vacuum-dried at 60°C for 12 hours to obtain the crude product of smokeless and sulfur-free fireworks speed regulator; After the crude product of the smoke-free and sulfur-free ...

Embodiment 3

[0033] A smokeless and sulfur-free fireworks speed regulator, the mass percentages of its components are as follows:

[0034]

[0035] 3kg pseudo-boehmite powder, 3kg basic zinc carbonate powder and 1kg calcium bicarbonate powder were fully stirred and mixed in a dry powder mixer to obtain mixed powder A; under stirring state, 2.5kg dicyandiamide, 0.5kg Add rosin to 15kg of ethanol in sequence, and after continuous stirring for 60 minutes, mixed solution B is obtained; under stirring state, slowly add mixed solution B to mixed powder A, after adding, heat up to 55°C, and continue stirring until the material becomes uniform Sludge; the resulting soft and hard moderate uniform micelles are granulated with a twin-screw granulator, and vacuum-dried at 60°C for 12 hours to obtain the crude product of smokeless and sulfur-free fireworks speed regulator; the obtained After the crude product of the smokeless and sulfur-free fireworks speed-regulating agent is lightly crushed, pass ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a smoke-free and sulfur-free firework speed regulator and a preparation method thereof, and belongs to the field of environment-friendly pyrotechnic compositions. The preparation method comprises the following steps: S1, weighing pseudo-boehmite powder, basic zinc carbonate powder, calcium bicarbonate powder, dicyandiamide and rosin according to a mass ratio in a formula;fully stirring and mixing the pseudo-boehmite powder, the basic zinc carbonate powder and the calcium bicarbonate powder in a dry powder mixer to obtain mixed powder A; sequentially adding dicyandiamide and rosin into ethyl alcohol under stirring to obtain a mixed solution B; slowly adding the mixed solution B into the mixed powder A under stirring, raising the temperature after addition, continuing stirring until the material becomes a mud pie with moderate hardness, granulating and drying the mud pie to obtain a crude smoke-free and sulfur-free firework speed regulator, and carrying out crushing and sieving to obtain the smoke-free and sulfur-free firework speed regulator. According to the method, calcium carbonate powder and magnesium carbonate powder are adopted as main components, thedecomposition product is gas and does not contain sulfur, the process is simple, and no three wastes are discharged in the production process.

Description

technical field [0001] The invention relates to a smokeless and sulfur-free fireworks speed regulator and a preparation method thereof, belonging to the field of environment-friendly pyrotechnics. Background technique [0002] Since ancient times, China has had the tradition of setting off fireworks on festivals. The display of fireworks adds a festive atmosphere to the festival. However, in recent years, due to the continuous growth of consumption, the lack of environmental protection awareness and the impact of the surge of manufacturers, a large number of fireworks have been set off, and the toxic and harmful gases and dust particles produced have a very serious impact on human body functions. Setting off a large number of fireworks in a short period of time will bring great pollution to the environment, and also threaten the safety of people's lives and properties. [0003] Firework speed regulator is an important part of pyrotechnics, which can absorb heat and decompos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C06B23/00C06B21/00
CPCC06B21/0066C06B23/00
Inventor 刘吉平方祝青吉伟生于保藏李琪军刘克普周天驰
Owner BEIJING INSTITUTE OF TECHNOLOGYGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com