Problems solved by technology

[0004] Aiming at the problem of poor forming caused by large gaps and misalignment in the actual production welding process of armor steel butt joints of medium and thick plates, the present invention proposes a laser swing welding method for armor steel of medium and thick plates

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A laser swing welding method for medium-thick armor steel
  • A laser swing welding method for medium-thick armor steel
  • A laser swing welding method for medium-thick armor steel

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0019] Specific implementation mode one: combine Figures 1 to 3 Describe this embodiment mode, a kind of medium and thick plate armor steel laser swing welding method of this embodiment mode, it is to carry out according to the following steps:

[0020] Step 1: smoothing the parts to be welded of the workpiece, and grinding or cleaning the surfaces on both sides of the workpiece after processing;

[0021] Step 2: fix the workpiece to be welded after grinding or cleaning on the welding fixture, add a formed base plate at the bottom of the gap, leave a protrusion in the middle of the base plate, and fix it at the edge of the base plate;

[0022] Step 3: Set the process parameters: the laser power of bottom welding is 2kW~3kW, the defocus amount is +5~+15mm, the laser swing range is 1~8mm, the swing frequency is 0~5Hz, and the shielding gas is pure argon. The shielding gas flow rate is 10L / min~40L / min, the welding speed is 0.3~1.2m / min; the laser power for filling welding is 1....

specific Embodiment approach 2

[0024] Specific implementation mode two: combination Figures 1 to 3 This embodiment is described. The difference between this embodiment and the first embodiment is that the workpiece to be welded is a butt joint of 6252 armored steel with a thickness of 12 mm.

[0025] Others are the same as in the first embodiment.

specific Embodiment approach 3

[0026] Specific implementation mode three: combination Figures 1 to 3 This embodiment will be described. The difference between this embodiment and the first embodiment is that the welding wire is GM120 welding wire with a diameter of 1.2 mm.

[0027] Others are the same as in the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

A laser swing welding method for medium-thick armor steel, which relates to the field of material processing engineering. The present invention aims at the problem of poor forming caused by large gaps and misalignment of medium-thick armor steel butt joints in the actual production welding process. The present invention It is designed to weld the butt joints of medium and thick plates. The laser swing welding method is used. The mechanical swing and pre-formed bottom plate are used for welding during bottom welding, and the galvanometer scanning swing laser is used for wire filling welding during filling welding. The invention is applied to the field of armor welding of medium and thick plates.

Description

technical field [0001] The invention belongs to the field of material processing engineering, and in particular relates to a laser swing welding method for medium-thick plate armor steel. Background technique [0002] The wheeled infantry fighting vehicles and tracked vehicles undertaken by our country's existing military enterprises are all large and complex weapons and equipment, and many parts on them are permanently connected by welding structure. The welding methods currently used mainly include manual arc welding, tungsten argon arc welding (TIG), CO 2 Gas arc welding, MIG / MAG welding, etc. However, traditional welding methods are likely to cause problems such as large welding deformation, unstable quality, difficulty in controlling welding stress, and difficulty in ensuring weld quality and appearance consistency. Laser welding is an advanced welding technology with fast heating and The cooling speed and narrow heat-affected zone have become one of the best methods ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K26/21B23K26/08B23K26/14B23K26/60
CPCB23K26/08B23K26/14B23K26/21B23K26/60B23K2103/04
Inventor 雷正龙黎炳蔚冯和永孙虎赵孟颖万鹏高金良冯文韬
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com