Condensation type organic silicon resin aerogel and preparation method thereof

A silicone and condensation-type technology, applied in the field of condensation-type silicone resin airgel and its preparation, can solve the problems of inability to prepare condensation-type silicone resin airgel, long distance of active groups, and high degree of hydroxyl reaction , to achieve the effect of low overall cost, realization of cross-linking degree and simple reaction process

Active Publication Date: 2020-02-11
AEROSPACE INST OF ADVANCED MATERIALS & PROCESSING TECH
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there is no public report on the use of commercial hydroxyl-terminated silicone resins to prepare condensation-type silicone resin aerogels at home and abroad. The content is less, and the distance between the active groups (-OH) between the molecules is relatively long, and it often takes several hours above 200°C to cure the resin
However, the preparation of condensation-type silicone resin airgel needs to prepare a wet gel in the solution first, and the hydroxyl content in the solution will be lower, which makes it difficult for the commercialized hydroxyl-terminated silicone resin to solidify in the solution to form a wet gel, and then cannot Preparation of Condensed Silicone Resin Airgel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Condensation type organic silicon resin aerogel and preparation method thereof
  • Condensation type organic silicon resin aerogel and preparation method thereof
  • Condensation type organic silicon resin aerogel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] 1. Dissolve 200g of Dowsil RSN 0806 (the solid content of the product itself is 50%, and the solvent is a mixed solvent of toluene and xylene), 5g of ethyl orthosilicate and 0.6g of dibutyltin dilaurate in 800g of ethyl acetate, stir at room temperature for 30min, and pour After standing in the mold, after the reaction system gels, it is aged at room temperature for 24 hours to obtain a condensation type silicone resin wet gel.

[0045] 2. Perform solvent replacement on the condensed silicone resin wet gel obtained in step 1, soak it repeatedly with cyclohexane for 3 times, and then perform supercritical CO 2 Dry, and dry at 40°C and 15MPa for 8 hours to obtain a condensation-type silicone resin airgel.

[0046] 3. Perform post-curing treatment on the airgel prepared in step 2. The treatment conditions are 60° C. for 1 hour, 80° C. for 1 hour, 100° C. for 1 hour, and 120° C. for 1 hour.

[0047] The density of the condensation type silicone resin airgel obtained in thi...

Embodiment 2

[0050] Except that the mass of tetraethyl orthosilicate added is 20g, the preparation conditions and process of the condensation type silicone resin airgel are the same as in Example 1, and the density of the airgel is 0.18g / cm 2 .

Embodiment 3

[0052] Except that the mass of tetraethyl orthosilicate added is 30g, the preparation conditions and process of the condensation type silicone resin airgel are the same as in Example 1, and the density of the airgel is 0.2g / cm 2 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides condensation type organic silicon resin aerogel and a preparation method thereof. Under the catalysis of a gel catalyst, condensation polymerization reaction is performed by hydroxyl-terminated silicon resin and a siloxane crosslinking agent, and after gelation and aging, wet gel is obtained by solvent replacement, supercritical drying and post-curing treatment. According tothe condensation type organic silicon resin aerogel and the preparation method thereof, by introducing the siloxane crosslinking agent and the gel catalyst into a solution of the hydroxyl-terminatedsilicon resin, condensation type organic silicon resin wet gel with a crosslinked network structure is prepared, then condensation type organic silicon resin aerogel is prepared by solvent replacement, supercritical drying and post-curing, and the technical problem that in prior art, condensation type silicon resin aerogel cannot be prepared due to the fact that the wet gal cannot be prepared fromcommercial hydroxyl-terminated silicon resin is solved.

Description

technical field [0001] The invention relates to a condensation type silicone resin airgel and a preparation method thereof, belonging to the technical field of airgel preparation. Background technique [0002] Airgel is a kind of highly dispersed solid nanomaterial with colloidal particles or polymer molecules aggregated into a nanoporous network structure. It has the characteristics of low density, high specific surface area, and low thermal conductivity. It is used in aerospace vehicle thermal control systems, Civil insulation and other fields have very broad application prospects. [0003] Condensed silicone resin is a polyorganosiloxane with a highly cross-linked network structure. The main chain structure is alternately connected with silicon and oxygen atoms, and the side chain is connected with organic groups. Therefore, it has the dual characteristics of organic resin and inorganic material. . Due to its excellent heat resistance, cold resistance, electrical insula...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J9/28C08G77/44C08L83/10
CPCC08J9/28C08G77/44C08J2205/026C08J2205/042C08J2201/0502C08J2383/10
Inventor 刘韬刘圆圆张恩爽郭慧徐春晓李文静杨洁颖赵英民张昊
Owner AEROSPACE INST OF ADVANCED MATERIALS & PROCESSING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products