Anti-static terrace water-based paint and preparation method thereof

An anti-static and flooring technology, applied in anti-fouling/underwater coatings, conductive coatings, paints containing biocides, etc., can solve the problems of poor, easy to gather static ions, weather resistance and environmental protection, and achieve simple operation Effect

Inactive Publication Date: 2020-01-10
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems that current floor coatings tend to gather static ions and have poor weather resistance and environmental protection, the present invention provides an antistatic floor water paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-static terrace water-based paint and preparation method thereof
  • Anti-static terrace water-based paint and preparation method thereof
  • Anti-static terrace water-based paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Embodiment 1: According to the ratio of the above-mentioned embodiment 1, in the material preparation tank, add water-based mixed resin, place it under the high-speed disperser, start the high-speed disperser, and add 65% of the formula amount evenly and slowly under 800r / min stirring Solvent, deionized water, dispersant, modified polyurethane high polymer wetting agent and 65% defoaming agent in the formulation amount, and stirred for 15 minutes. Under stirring at 1000r / min, add polyether siloxane copolymer wetting agent, leveling agent and anti-scratch additive, and stir for 10 minutes. Under stirring at 1200r / min, add water-based nano hardening powder, conductive materials, and functional fillers, and stir for 20 minutes to control the fineness below 15 μm. Add the thickener under stirring at 800r / min, and stir for 25min to make component A. According to the above ratio, add epoxy curing agent into the material preparation tank, place it under the high-speed dispers...

Embodiment 2

[0043]Embodiment 2: According to the ratio of the above-mentioned embodiment 2, in the material preparation tank, add water-based mixed resin, place it under the high-speed disperser, start the high-speed disperser, and add 70% of the formula amount evenly and slowly under 700r / min stirring Solvent, deionized water, dispersant, modified polyurethane high polymer wetting agent and 70% defoaming agent in the formulation amount, and stirred for 13 minutes. Under stirring at 900r / min, add polyether siloxane copolymer wetting agent, leveling agent, anti-scratch additive, and stir for 8 minutes. Under stirring at 1100r / min, add water-based nano hardening powder, conductive materials, and functional fillers, and stir for 18 minutes to control the fineness below 20 μm. Add the thickener under stirring at 700r / min, and stir for 20min to make component A. According to the above ratio, add epoxy curing agent into the material preparation tank, place it under the high-speed disperser, st...

Embodiment 3

[0044] Embodiment 3: According to the proportioning of the above-mentioned embodiment 3, in the material preparation tank, add the water-based mixed resin, place it under the high-speed disperser, start the high-speed disperser, and under 900r / min stirring, evenly and slowly add 75% of the formula amount Solvent, deionized water, dispersant, modified polyurethane high polymer wetting agent and 75% defoaming agent in the formulation amount, and stirred for 13 minutes. Under stirring at 800r / min, add polyether siloxane copolymer wetting agent, leveling agent, and anti-scratch additive, and stir for 8 minutes. Under stirring at 1000r / min, add water-based nano hardening powder, conductive materials, and functional fillers, and stir for 18 minutes to control the fineness below 20 μm. Add the thickener under stirring at 700r / min, and stir for 20min to make component A. According to the above ratio, add epoxy curing agent into the material preparation tank, place it under the high-s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of water-based paint, in particular to an anti-static terrace water-based paint and a preparation method thereof. The anti-static terrace water-based paint comprisesthe following components: a water-based mixed resin, an epoxy curing agent, a solvent, deionized water, a waterborne nano hardening powder, a conductive material, a filler, an anti-scratching aid, adispersing agent, a wetting agent, an antifoaming agent, a leveling agent and a thickener, has good antistatic performance, good weather resistance and impact resistance, high hardness, water resistance, oil resistance and extremely low VOC content, and contains no benzene series substances, free formaldehyde, or heavy metals.

Description

technical field [0001] The invention relates to the field of water-based paint, in particular to an antistatic floor water paint and a preparation method thereof. Background technique [0002] As a green product, water-based floor coatings are gradually replacing solvent-based floor coatings, and are widely used in the floor coating of production plants, office buildings, warehouses, and laboratories in the pharmaceutical, food, hospital, textile, chemical, and electronics industries. It is suitable for the first floor, basement, underground parking lot and other relatively humid environments. [0003] Because the surface of organic materials in floor coatings is very easy to accumulate static ions, the use in some specific places such as hospitals, biochemical products companies, polymer laboratories, etc. is limited. In addition, water-based floor coatings usually use epoxy resin as the main film-forming substance, which has poor weather resistance and shortens its servic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D5/24C09D175/02C09D163/02C09D5/16C09D7/20
CPCC08K2003/085C08K2201/001C08K2201/011C08L2201/04C08L2205/035C09D5/1687C09D5/24C09D7/20C09D175/02C08L63/00C08L75/04C08L83/12C08K13/06C08K3/36C08K9/10C08K3/04C08K3/08C08K7/00C08K3/34
Inventor 程璐李幕英胡中源董立志
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap