Flame-retardant material for textiles and preparation method thereof

A technology for flame retardant materials and textiles, applied in the field of flame retardants, can solve problems such as poor compatibility and easy precipitation, and achieve the effects of enhanced reactivity, low solubility, and increased specific surface area

Inactive Publication Date: 2019-12-20
SHIFANG CHANGFENG CHEM CO LTD
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is: in order to solve the problems of poor compatibility, hygroscopicity, and easy precipitation between ordinary ammonium polyphosphate flame retardants and organic polymer materials, the present invention provides a flame retardant material for textiles and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant material for textiles and preparation method thereof
  • Flame-retardant material for textiles and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] a kind of like figure 1 The preparation method of the flame retardant material used for textiles is characterized in that, specifically, the steps are as follows:

[0028] (1) Preparation of siloxane resin coating agent:

[0029] Add 5 parts of solvent trimethylhydroxysilane and 3 parts of methanol into the reactor, and start stirring after the addition is complete. Then slowly add 7.5 parts of siloxane resin, namely dimethyldichlorosilane. Continue stirring, turn on the electric heater, slowly raise the temperature to 75°C, and keep stirring for 1.5 hours. Add 0.15 parts of curing agent 4,4-diaminophenylmethane into the reactor, stir for another 15 minutes, stop stirring, and turn off the electric heater. After the coating agent is prepared, it is reserved for use in the next process. Prepare the silicone resin coating agent through the above operating procedures;

[0030] (2) Coating modification of ammonium polyphosphate (APP):

[0031] Add 85 parts of general-...

Embodiment 2

[0036] a kind of like figure 1 The preparation method of the flame retardant material used for textiles is characterized in that, specifically, the steps are as follows:

[0037] (1) Preparation of siloxane resin coating agent:

[0038] Add 6.5 parts of solvent trimethylhydroxysilane and 3 parts of ethanol into the reactor, and start stirring after the addition. Then slowly add 7 parts of siloxane resin, namely vinyl triethoxysilane. Continue to stir, turn on the electric heater, slowly raise the temperature to 73°C, and keep stirring for 2.0 hours. Add 0.2 parts of curing agent triethylenetetramine into the reactor, stir for another 16 minutes, stop stirring, and turn off the electric heater. After the coating agent is prepared, it is reserved for use in the next process. The silane resin coating agent is prepared through the above operating procedure.

[0039] (2) Coating modification of ammonium polyphosphate (APP):

[0040] Add 88 parts of general-type ammonium polyp...

Embodiment 3

[0045] a kind of likefigure 1 The preparation method of the flame retardant material used for textiles is characterized in that, specifically, the steps are as follows:

[0046] (1) Preparation of siloxane resin coating agent:

[0047] Add 8 parts of solvent trimethylhydroxysilane and 3 parts of methanol into the reactor, and start stirring after the addition is complete. Then slowly add 3 parts of aminosilane resin and 5 parts of methacryloxysilane resin. Continue to stir, turn on the electric heater, slowly raise the temperature to 79°C, and keep stirring for 4.5 hours. Add 0.1 part of curing agent 4,4-diaminophenylmethane and 0.2 part of triethylamine into the reactor, stir for another 20 minutes, stop stirring, and turn off the electric heater. After the coating agent is prepared, it is reserved for use in the next process. The siloxane resin encapsulating agent was prepared through the above operating procedures.

[0048] (2) Coating modification of ammonium polyphosp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a flame-retardant material for textiles and a preparation method, and relates to the technical field of flame retardants. The flame-retardant material for the textiles comprises, by weight, 85-90 parts of ammonium polyphosphate and 5-10 parts of a siloxane coating agent, wherein the siloxane coating agent comprises, by weight, 5-8 parts of siloxane resin, 5-8 parts of a solvent and 0.1-0.3 part of a curing agent. By means of the material, an ammonium polyphosphate flame-retardant product and a textile material have good phase solubility so that the flame retardants canfully exert the flame-retardant effect. The material can be used for flame retarding of decorative fabrics, and the flame-retardant performance can reach the level B1; the material can be used for flame retarding of protective clothing fabrics, and the flame-retardant performance can reach the level B.

Description

technical field [0001] The invention relates to the technical field of flame retardants, which are used for flame retardant of textile products, and more specifically relate to a flame retardant material used for textiles and a preparation method. Background technique [0002] Textiles are a product made of textile fibers through processing and weaving. They are divided into two categories: woven fabrics and knitted fabrics. China is one of the earliest countries in the world to produce textiles. The main producing areas are Puyuan in Zhejiang and Qinghe in Hebei. [0003] With the development of modern science and technology and the progress of the textile industry, the types of textiles continue to increase, and their application scope continues to expand and extend to all aspects of people's production and life. However, textile materials are generally flammable or combustible, which can easily cause fire accidents. According to statistics, more than 20% of the fire acci...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F1/07C08K9/10C08K3/32
CPCC08K3/32C08K9/10C08K2003/323D01F1/07
Inventor 刘泽祥杨劲松杨滨
Owner SHIFANG CHANGFENG CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com