Inorganic composite material with properties of low carbon steel and preparation method thereof

An inorganic composite material and low carbon steel technology, applied in the field of concrete materials, can solve the problems of compressive strength only reaching 170-230Mpa, the activity cannot be fully exerted, and the performance index cannot reach low carbon steel, etc. Better cushioning effect, longer stress time and lower elastic modulus

Active Publication Date: 2021-11-09
NANJING UNIV OF SCI & TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Ordinary low-carbon steel has poor corrosion resistance, and it often needs to be galvanized on the surface and sprayed with anti-rust resin on the surface for corrosion protection.
These surface protection methods will gradually corrode and peel off the surface protection layer as the service time of low carbon steel components prolongs, and the maintenance and repair costs are high.
Highway anti-collision guardrails made of ordinary low-carbon steel, high-speed rail sound barrier trough steel keels, external marble light steel keels for buildings, light steel roof trusses for public parking lots, steel structures for architectural urban sculptures, etc. Wet cycle makes the corrosion resistance of ordinary low carbon steel aggravated, which brings safety hazards
[0004] Reactive powder (RPC) materials have the characteristics of high durability, corrosion resistance, and fire resistance, but most of the existing RPC materials prepared by using active mineral admixtures (such as silica fume, quartz powder) adopt natural curing or dry heat curing. , which leads to the failure of the activity of the internal mineral admixture to be fully exerted, the compressive strength can only reach 170-230Mpa, and the bending strength is roughly 30-60MPa (An Mingzhe, Wang Qingsheng, Ding Jiantong. The preparation principle of active powder concrete and application prospects [J]. Building Technology, 2001,32(1):15-16.), the performance indicators have failed to reach the level of low carbon steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inorganic composite material with properties of low carbon steel and preparation method thereof
  • Inorganic composite material with properties of low carbon steel and preparation method thereof
  • Inorganic composite material with properties of low carbon steel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] In this embodiment, the raw materials are composed of: cement: silica fume: fly ash: water reducing agent: water: quartz sand=1:0.3:0.62:0.03:0.24:1.1, the calcium-silicon ratio is 0.75, and the long steel fiber volume ratio is 7%, short steel fiber 1%.

[0055] In the first step, put 671.5g of quartz sand, 183.2g of silica fume and 378.5g of fly ash into a mixer and stir for 2 to 3 minutes. After the mixture is evenly stirred, add (30%) 44.0g of ice water to moisten the mineral material and stir for 2 ~3min. Mix the remaining 102.6g of ice water and 18.3g of water reducer evenly, put 610.5g of cement and the remaining ice water into the stirring pot in turn, and stir the mixture for 6 to 10 minutes. After the material forms a slurry, add 420g of long steel fiber and short Steel fiber 60g, stir for 1-2 minutes, until the steel fiber is evenly distributed in the cement mortar.

[0056] In the second step, put the composite mortar of the first step into a triple mold of...

Embodiment 2

[0061] The composition of raw materials in this example is: cement: silica fume: fly ash: water reducer: water: quartz sand = 1:0.35:0.60:0.04:0.23:1.0, the calcium-silicon ratio is controlled at 0.72, and the volume ratio of long steel fibers 4%, short steel fiber 2%.

[0062] In the first step, put 630g of quartz sand, 220.5g of silica fume and 378g of fly ash into a mixer and stir for 2 to 3 minutes. After the mixture is evenly stirred, add (30%) 43.5g of ice water to moisten the mineral material and stir for 2 to 3 minutes. . Mix the remaining 101.4g of ice water and 25.2g of water reducer evenly, put 630g of cement and the remaining ice water into the mixing pot and stir for 6-10 minutes, after the materials form a slurry, add 240g of long steel fibers and 120g of short steel fibers , Stir for 1 to 2 minutes until the steel fibers are evenly distributed in the cement mortar.

[0063] In the second step, put the composite mortar of the first step into a triple mold of 40...

Embodiment 3

[0068] The composition of raw materials in this example is: cement: silica fume: fly ash: water reducer: water: quartz sand = 1:0.3:0.62:0.03:0.24:1.1, the calcium-silicon ratio is controlled at 0.75, and the volume ratio of long steel fibers 5%, short steel fiber 2%.

[0069]In the first step, put 671.5g of quartz sand, 183.2g of silica fume and 378.5g of fly ash into a mixer and stir for 2 to 3 minutes. After the mixture is evenly stirred, add (30%) 44.0g of ice water to moisten the mineral material and stir for 2 ~3min. Mix the remaining 102.6g of ice water and 18.3g of water reducer evenly, put 610.5g of cement and the remaining ice water into the stirring pot and stir for 6-10 minutes, after the materials form a slurry, add 300g of long steel fibers, short steel fibers 120g, stir for 1-2 minutes until the steel fibers are evenly distributed in the cement mortar.

[0070] In the second step, put the composite mortar of the first step into a triple mold of 40*40*160mm, ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an inorganic composite material with the properties of low-carbon steel and a preparation method thereof. The inorganic composite material includes 100 parts by weight of cement, 30-40 parts of silica fume, 55-65 parts of fly ash, 90-110 parts of quartz sand, 2-4 parts of water reducer, 22-24 parts of water Parts, short steel fiber volume addition 1-3%, 12-20mm long steel fiber volume addition 3-8%, after the mortar is vibrated into a mold, it is demoulded and cured in a water bath at a temperature of 20-90°C for 1-3 days. Inorganic composite materials were obtained by curing in saturated steam at 200°C for 12-24 hours. The inorganic composite material of the present invention has high strength and high toughness similar to low-carbon yield strength, and also has the characteristics of corrosion resistance, low thermal conductivity and electromagnetic insulation that low-carbon steel does not have, and has good fire resistance at the same time. The strength is maintained above 85% at 400°C, which can effectively compensate for the poor fire resistance of carbon steel materials. It can be widely used in the field of prefabricated structures replacing low carbon steel, armor protection and anti-penetration engineering, nuclear power plant engineering and other fields.

Description

technical field [0001] The invention relates to an inorganic composite material with the properties of low-carbon steel and a preparation method thereof, belonging to the technical field of concrete materials. Background technique [0002] Low-carbon steel has the characteristics of 235-345MPa elastic limit strength, high plasticity and toughness, and has been widely used and developed in steel structure engineering. However, steel is easy to rust in a humid environment, especially in a corrosive medium, which seriously affects its durability. Moreover, the fire resistance of the steel structure is poor. As the temperature increases, the strength decreases. The strength changes little within 250°C. After 300°C, the strength gradually decreases, and the strength drops to zero when it reaches 450-650°C. Therefore, it is necessary to find a new type of material that not only has the high strength and high toughness of low-carbon steel structure, but also has the corrosion resi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04
CPCC04B28/04C04B2201/50C04B18/146C04B14/06C04B18/08C04B2103/302C04B22/002C04B14/48
Inventor 崔崇黄炎琦崔晓昱
Owner NANJING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap