Gypsum-based ceramic tile adhesive and preparation method thereof

A technology of adhesives and ceramic tiles, which is applied in the field of building materials, can solve the problems of adhesive hollowing and falling off, and achieve the effects of reducing environmental pressure, increasing waste utilization, and shortening construction time

Inactive Publication Date: 2019-11-29
贵州蓝图磷石膏环保科技有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problems existing in the existing ceramic tile adhesives, the purpose of the present invention is to provide a gypsum-based ceramic tile adhesive that can effectively solve the problem of hollowing and falling off of cement-based ceramic tile adhesives.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gypsum-based ceramic tile adhesive and preparation method thereof
  • Gypsum-based ceramic tile adhesive and preparation method thereof
  • Gypsum-based ceramic tile adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] This embodiment provides a gypsum-based ceramic tile adhesive including gypsum components, sand components, retarder components, anti-sagging components, waterproofing agent components, water-reducing agent components, water-retaining agent components and enhanced thickeners Components, wherein the gypsum component uses phosphogypsum; the sand component uses 40-140 mesh sand; water-repellent; the water-reducing agent component is polycarboxylate water-reducer; the water-retaining agent component is hydroxypropyl methylcellulose ether; the thickener component is vinyl acetate-ethyl polymer, and the latex powder; the weight percentages of each component are as follows:

[0028]

Embodiment 2

[0030] This embodiment provides a gypsum-based ceramic tile adhesive including gypsum components, sand components, retarder components, anti-sagging components, waterproofing agent components, water-reducing agent components, water-retaining agent components and enhanced thickeners Components, wherein the gypsum component uses phosphogypsum; the sand component uses 40-140 mesh sand; water-repellent; the water-reducing agent component is polycarboxylate water-reducer; the water-retaining agent component is hydroxypropyl methylcellulose ether; the thickener component is vinyl acetate-ethyl polymer, and the latex powder; the weight percentages of each component are as follows:

[0031]

Embodiment 3

[0033] This embodiment provides a gypsum-based ceramic tile adhesive including gypsum components, sand components, retarder components, anti-sagging components, waterproofing agent components, water-reducing agent components, water-retaining agent components and enhanced thickeners Components, wherein the gypsum component uses phosphogypsum; the sand component uses 40-140 mesh sand; water-repellent; the water-reducing agent component is polycarboxylate water-reducer; the water-retaining agent component is hydroxypropyl methylcellulose ether; the thickener component is vinyl acetate-ethyl polymer, and the latex powder; the weight percentages of each component are as follows:

[0034]

[0035]

[0036] The gypsum components used in Embodiment 1, Embodiment 2, and Embodiment 3 can also use other gypsum powders that meet the 3.0 grade standard for building gypsum, such as desulfurized gypsum.

[0037] The 40-140 mesh medium sand used in Embodiment 1, Embodiment 2, and Embod...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a gypsum-based ceramic tile adhesive and a preparation method thereof. The adhesive comprises a gypsum component, a sand component, a retarder component, an anti-sag component,a waterproof agent component, a water reducing agent component, a water retaining agent component and a reinforcing thickening agent component. The absolute dry tensile bonding strength of the adhesive can reach 1.0 MPa and can reach more than 0.56 MPa after 24 hours of immersion. The gypsum-based ceramic tile adhesive meeting the standard of common cement-based ceramic tile adhesives is preparedfrom low-strength gypsum powder as a binding material, an aggregate and an additive, so that the defects of the cement-based ceramic tile adhesives are effectively overcome; the industrial byproductgypsum is wider in application, and the gypsum-based ceramic tile adhesive follows the thought of national resource recycling economy, and expands the advantages of gypsum.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a gypsum-based ceramic tile adhesive and a preparation method thereof. Background technique [0002] With the development of industrial technology, the development of domestic chemical companies is booming, and the benefits they bring are immeasurable, but the impact on the environment cannot be underestimated. Desulfurization gypsum produced by desulfurization in power plants, phosphogypsum produced by phosphoric acid in phosphating plants, etc. are all industrial waste residues. Long-term landfills will occupy a large amount of land and pollute the environment. At present, the accumulation of industrial by-product gypsum in China has reached hundreds of millions. tons, so the treatment of gypsum needs to be solved urgently. [0003] The main component of gypsum is calcium sulfate dihydrate, a resource that can be recycled. After dehydration at a certain temperatu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14
CPCC04B28/14C04B28/143C04B2111/00637C04B14/06C04B2103/22C04B24/38C04B24/42C04B2103/302C04B2103/0057C04B24/383C04B14/068
Inventor 付伯平李军陈小平刘永杨再祥何金泉石吉鑫雷勇
Owner 贵州蓝图磷石膏环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com