Asphalt pavement heat-reflecting coating and preparation method thereof

A heat-reflective coating, asphalt pavement technology, applied in the direction of reflection/signal coating, coating, road, etc., to achieve the effect of convenient construction, reduced drop, and good strength

Inactive Publication Date: 2019-11-12
上海南信公路建设有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Traditional heat reflective coatings for asphalt pavement cannot withstand the strong impact of frequent braking and starting of vehicles at road intersections. High-strength asphalt pavement heat-reflective coating for special load impact

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Asphalt pavement heat-reflecting coating and preparation method thereof
  • Asphalt pavement heat-reflecting coating and preparation method thereof
  • Asphalt pavement heat-reflecting coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0043]

[0044] The preparation method of asphalt pavement heat reflective coating of the present invention, it comprises the steps:

[0045] (1), adding nano-titanium dioxide into the first water-based epoxy resin and stirring to obtain the first mixture;

[0046] (2), adding nano silicon dioxide into the first mixture and stirring to obtain the second mixture;

[0047] (3), adding iron oxide red, dispersant and matting agent into the second mixture in turn and stirring to obtain the third mixture;

[0048] (4), the second water-based epoxy resin is added to the third mixture and stirred to obtain a water-based epoxy resin coating;

[0049] (5) Brush the water-based epoxy resin paint on the surface of the asphalt pavement to obtain a coating. Within 10 minutes after the brushing is completed, spread the anti-slip agent on the surface of the coating and shape it.

[0050] Wherein, in step (1), the stirring time may be 2±0.5 min, preferably 2 min.

[0051] In step (2), the...

Embodiment 1

[0056] The asphalt pavement heat reflective coating of the present embodiment comprises the following components:

[0057]

[0058]

[0059] The preparation method of the asphalt pavement heat reflective coating of the present embodiment comprises the following steps:

[0060] (1), first add 94g of nano-titanium dioxide into 1000g of the first water-based epoxy resin and fully stir for 2min to obtain the first mixture;

[0061] (2), then add 47g of nano silicon dioxide into the first mixture and fully stir for 1min to obtain the second mixture;

[0062] (3), then add 94g of red iron oxide, 35.25g of dispersant and 23.5g of matting agent into the second mixture in sequence and fully stir for 2min to obtain the third mixture;

[0063] (4), finally the second water-based epoxy resin of 500g is added in the third mixture and fully stirred for 2min to obtain a uniformly dispersed water-based epoxy resin coating;

[0064](5), the water-based epoxy resin coating is evenly bru...

Embodiment 2

[0076] The asphalt pavement heat reflective coating of the present embodiment comprises the following components:

[0077]

[0078] The preparation method of the asphalt pavement heat reflective coating of the present embodiment comprises the following steps:

[0079] (1), first add 94g of nano-titanium dioxide into 1000g of the first water-based epoxy resin and fully stir for 2min to obtain the first mixture;

[0080] (2), then add 47g of nano silicon dioxide into the first mixture and fully stir for 1min to obtain the second mixture;

[0081] (3), then add 94g of red iron oxide, 35.25g of dispersant and 23.5g of matting agent into the second mixture in sequence and fully stir for 2min to obtain the third mixture;

[0082] (4), finally the second water-based epoxy resin of 500g is added in the third mixture and fully stirred for 2min to obtain a uniformly dispersed water-based epoxy resin coating;

[0083] (5), the water-based epoxy resin coating is evenly brushed on the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Widthaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an asphalt pavement heat-reflecting coating and a preparation method thereof. The asphalt pavement heat-reflecting coating includes first water-borne epoxy resin, second water-borne epoxy resin, nanometer titania, nanosilicon dioxide, iron oxide red, a flatting agent, a dispersant and an anti-skid agent. Compared with traditional asphalt pavement heat-reflecting coatings, the asphalt pavement heat-reflecting coating has higher strength, adhesive capacity and durability, thus the asphalt pavement heat-reflecting coating can be applied to asphalt pavements of urban road intersections to resist the impact effect of the vehicle load, the pavement temperature in summer can be effectively lowered, track diseases are reduced, and thus the service lives of the asphalt pavements are prolonged; and by controlling the coating thicknesses with different asphalt pavement gradation types to reduce decreasement of the coating on an original pavement pore structure, meanwhile,a microcosmic anti-skid structure is provided by spreading the anti-skid agent, the anti-skid performance is good, and thus the traffic safety is ensured.

Description

technical field [0001] The invention belongs to the technical field of road engineering, and in particular relates to an asphalt pavement heat reflective coating and a preparation method thereof, and more particularly relates to an asphalt pavement solar heat reflective coating used at urban road intersections and a preparation method thereof. Background technique [0002] Rutting, moving, and wrapping are typical diseases of asphalt pavement in the intersection area, and the root cause is that the shear strength of asphalt concrete cannot adapt to the special working conditions of the asphalt pavement in the intersection area. In the intersection area, the vehicle behavior and road load characteristics are significantly different from the general road surface: heavily channelized traffic, frequent braking and starting, slow vehicle speed, and long parking time. This special working condition makes the asphalt pavement in the intersection area bear extremely heavy traffic lo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D5/33C09D7/61E01C7/32
CPCC08K2003/2241C08K2003/2272C08K2201/011C08L2205/025C09D5/004C09D163/00C09D7/61C09D7/67C09D7/69E01C7/32C08L63/00C08K3/22C08K3/36
Inventor 乔志刚孙军鞠英明
Owner 上海南信公路建设有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More