A kind of coating ink for ink-jet printing based on composite particle modification of multi-level structure and its preparation method and application

A composite particle, inkjet printing technology, applied in the direction of dyeing, textile and papermaking, etc., can solve the problems of complex preparation process, and achieve the effect of reducing the degree of infiltration, bright colors and clear patterns

Active Publication Date: 2022-04-01
浙江海印数码科技有限公司
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its preparation process is more complex

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of coating ink for ink-jet printing based on composite particle modification of multi-level structure and its preparation method and application
  • A kind of coating ink for ink-jet printing based on composite particle modification of multi-level structure and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of preparation method of ink-jet printing coating type ink that is modified based on the composite particle of multi-level structure, comprises the following steps:

[0032] (1) Dissolve zirconium isopropoxide in ethanol, then add polyvinyl alcohol aqueous solution with a mass concentration of 2%, stir at room temperature for 20 minutes at a speed of 1000 rpm, then add dropwise urea solution, and stir and mix at 40-50°C for 2 hours , to obtain a zirconium sol; wherein, the mass ratio of zirconium isopropoxide, polyvinyl alcohol, and urea is 4:0.026:0.2; dropwise adding a graphene oxide solution with a mass concentration of 1% in the zirconium sol, 3000rpm after the addition ends Stir at low temperature for 30 minutes, filter, wash the solid and dry it in vacuum at 80°C for 2h, then place it in a muffle furnace for calcination at 300-400°C for 3h, and then use the trap reduction method for reduction to obtain graphene nanosheet package Nano zirconia composite part...

Embodiment 2

[0038] A kind of preparation method of ink-jet printing coating type ink that is modified based on the composite particle of multi-level structure, comprises the following steps:

[0039] (1) Dissolve zirconium isopropoxide in ethanol, then add polyvinyl alcohol aqueous solution with a mass concentration of 2%, stir at room temperature for 20 minutes at a speed of 1000 rpm, then add dropwise urea solution, and stir and mix at 40-50°C for 2 hours , to obtain a zirconium sol; wherein, the mass ratio of zirconium isopropoxide, polyvinyl alcohol, and urea is 4:0.045:0.2; dropwise adding a graphene oxide solution with a mass concentration of 1-5% in the zirconium sol, the addition ends Finally, stir at 3000rpm for 60min, filter, wash the solid and vacuum dry it at 80°C for 2h, then place it in a muffle furnace for calcination at 300-400°C for 4h, and then use the trap reduction method to reduce it to obtain graphene nanoparticles. Sheet-coated nano-zirconia composite particles, the...

Embodiment 3

[0045] A kind of preparation method of ink-jet printing coating type ink that is modified based on the composite particle of multi-level structure, comprises the following steps:

[0046] (1) Dissolve zirconium isopropoxide in ethanol, then add polyvinyl alcohol aqueous solution with a mass concentration of 2%, stir at room temperature for 20 minutes at a speed of 1000 rpm, then add dropwise urea solution, and stir and mix at 40-50°C for 2 hours , make zirconium sol; Wherein, the mass ratio of zirconium isopropoxide, polyvinyl alcohol, urea is 4: 0.03: 0.2; Dropwise in zirconium sol, mass concentration is the graphene oxide solution of 2%, 3000rpm after dropping Stir at low temperature for 40 minutes, filter, wash the solid and dry it in vacuum at 80°C for 2 hours, then place it in a muffle furnace for calcination at 300-400°C for 3.5 hours, and then reduce it by trap reduction method to obtain graphene nanosheets Coated nano-zirconia composite particles, the mass ratio of gra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The present invention provides a multi-level structure based composite particle modified inkjet printing coating ink, which comprises the following components in parts by weight: 3-9 parts of color paste, 5-8 parts of modified multi-level structure composite particles part, 0.1-0.6 part of surfactant, 0.3-0.5 part of ethylene glycol, 1-3 part of polyvinyl alcohol, 0.15-0.25 part of pH regulator, 10-20 part of deionized water; The particles are nano-zirconia composite particles coated with graphene nanosheets, the particle size is 60-80nm, and the surface is modified by polymer. The paint-type ink for inkjet printing disclosed by the invention has good stability and is suitable for inkjet printing of various fabrics. After inkjet printing, the pattern of the fabric is clear, the softness is good, the color fastness is high, and the mechanical properties of the fabric are also good. Improved.

Description

Technical field: [0001] The invention relates to a digital printing process, in particular to a coating-type ink for ink-jet printing based on composite particle modification of a multi-level structure and a preparation method and application thereof. Background technique: [0002] With the diversification and development of all aspects of the world, people's spiritual culture and aesthetic needs have been greatly improved. In order to meet the requirements of small batch production, flower patterns, and different performances of printed fabrics, different printing technologies for textiles have also emerged as the times require. pregnancy. There are different classification methods for textile printing, the most common of which are divided by different printing equipment, including: roller printing, flat screen printing, rotary screen printing, transfer printing and inkjet printing, etc. Among them, digital inkjet printing is due to With the advantages of low pollution, lo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06P5/30D06P1/673D06P1/52D06P1/651D06P1/48
CPCD06P5/30D06P1/673D06P1/48D06P1/5257D06P1/525D06P1/5228D06P1/65118
Inventor 宋水友宋丽娜
Owner 浙江海印数码科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com