Airgel self-suspension soilless cultivation substrate, preparation method and soilless cultivation device

A soilless culture substrate, soilless culture technology, applied in soilless culture, planting substrates, botanical equipment and methods, etc., can solve the problems of uncontrollable substrate moisture content, high density, water loss, etc., and achieve convenient planting and cultivation. , Simple operation, easy to operate effect

Active Publication Date: 2022-03-18
安徽科昂新材料科技有限公司
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention solves the following technical problems in the prior art: the current soilless culture substrate has high density, serious water loss, and can't control the moisture content of the substrate at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Airgel self-suspension soilless cultivation substrate, preparation method and soilless cultivation device
  • Airgel self-suspension soilless cultivation substrate, preparation method and soilless cultivation device

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0050] The preparation method of the above-mentioned airgel self-suspension soilless culture substrate, specifically, comprises the following steps:

[0051] (1) Disperse the airgel powder, water, and surface wetting agent in a certain proportion using a high-speed disperser to a uniform dispersion;

[0052] (2) Add a viscosifier to the dispersion prepared in (1) and mix evenly with a mixer to form an airgel self-suspension soilless cultivation substrate.

[0053] Preferably, the density of the airgel self-suspension soilless cultivation substrate prepared in the step (2) is between 0.3-0.8 g / ml, and the surface water contact angle is >120°.

[0054] In step (1), the dispersing and stirring speed of the high-speed disperser is 900-1500rp, and the dispersing time is 30-120 minutes.

[0055] In step (2), the stirring speed of the stirrer is between 120~500rpm, and the stirring time is between 30~120 minutes

[0056] The soilless culture device that utilizes the airgel that the...

Embodiment 1

[0062] A kind of preparation method of airgel self-suspension soilless cultivation substrate, its steps are as follows:

[0063] (1) Disperse 20 parts by weight of silica airgel powder, 80 parts of water, and 0.1 part of sodium dodecylsulfonate at 1400 rpm for 60 minutes using a highly dispersing machine, wherein the particle size of silica airgel powder Between 10 and 50 μm, the surface water contact angle is 145°, and the density is 0.05g / ml

[0064] (2) Add 2 parts by weight of sodium alginate to the dispersion prepared in (1), and stir for 30 minutes with a horizontal mixer to obtain an airgel self-suspension soilless cultivation substrate.

Embodiment 2

[0066] A kind of preparation method of airgel self-suspension soilless cultivation substrate, its steps are as follows:

[0067] (1) Disperse 10 parts by weight of silica airgel powder, 90 parts of water, and 0.05 part of sodium dodecylsulfonate at 1400 rpm for 60 minutes using a highly dispersing machine, wherein the particle size of silica airgel powder Between 10 and 50 μm, the surface water contact angle is 145°, and the density is 0.05g / ml

[0068] (2) Add 3 parts by weight of sodium alginate to the dispersion prepared in (1), and stir for 30 minutes with a horizontal mixer to obtain an airgel self-suspension soilless cultivation substrate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an airgel self-suspension soilless cultivation substrate, relates to the field of soilless cultivation substrates, and comprises the following raw materials by weight: 1-30 parts of airgel powder, 70-99 parts of water 0.05-0.1 part of surface wetting agent and 2-10 parts of tackifier. The present invention can effectively increase and control the water content of the matrix by adding airgel powder in the matrix, and at the same time cooperate with the effect of the surface wetting agent in the components to improve the interfacial compatibility between the airgel powder and other components , improve the stability of the overall structure of the matrix, and also disclose a preparation method in the present invention, which is simple and easy to operate, and does not produce any waste or pollutants during the production process, which is green and environmentally friendly. The invention also discloses a soilless cultivation device. The soilless cultivation device prepared by using the airgel self-suspension soilless cultivation substrate has a simple structure, no pollution and is convenient for planting and cultivating plants.

Description

technical field [0001] The invention belongs to the field of cultivation substrates, and in particular relates to a soilless cultivation substrate, a preparation method and a soilless cultivation device. Background technique [0002] Soilless cultivation refers to the technology of cultivating crops and seedlings using artificially configured substrates instead of natural soil. At present, soilless cultivation technology has been applied to seedlings, flowers, fruits and vegetables, which is a water-saving and economical method. Advanced cultivation technology that saves fat and labor. The characteristics and advantages of soilless cultivation technology have been familiar and recognized by the majority of researchers and producers. [0003] At present, soilless culture substrates are divided into inorganic substrates, organic substrates and mixed substrates. Such as ceramsite, peat, foam, perlite, sawdust, etc. are used as substrates for soilless cultivation. However, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A01G31/02A01G24/00A01G24/10A01G24/15A01G24/20A01G24/30
CPCA01G31/02A01G24/10A01G24/15A01G24/20A01G24/00A01G24/30Y02P60/21
Inventor 张尚权
Owner 安徽科昂新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap