Porous calcium phosphate ceramics based on coating of calcium sulfate salt and preparation method of porous calcium phosphate ceramics

A technology of porous ceramics and calcium sulfate, which is applied in the field of bioceramics, can solve the problems of pore diameter, pore structure, unsatisfactory pore distribution, poor osteoinductive performance, and unfavorable new bone growth, etc., to achieve enhanced osteoinductive performance and pore parameters Ideal, the effect of improving mechanical properties

Pending Publication Date: 2019-09-27
陶合体科技(苏州)有限责任公司
View PDF12 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Although the preparation of calcium sulfate-calcium phosphate into a porous structure improves its biological performance, the pore parameters of these porous composite ceramics, including pore diameter, pore structure, and pore distribution, are not ideal, and the osteoinductive performance is not good, which is not conducive to new bone growth
Moreover, evenly mixing calcium sulfate and calcium phosphate, such a combination may also lead to the disintegration of the composite ceramics due to the rapid degradation of calcium sulfate after the prepared ceramics are implanted in the body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Porous calcium phosphate ceramics based on coating of calcium sulfate salt and preparation method of porous calcium phosphate ceramics
  • Porous calcium phosphate ceramics based on coating of calcium sulfate salt and preparation method of porous calcium phosphate ceramics
  • Porous calcium phosphate ceramics based on coating of calcium sulfate salt and preparation method of porous calcium phosphate ceramics

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0036] The invention provides a porous ceramic, which uses calcium sulfate and calcium phosphate as raw materials, and coats the calcium sulfate on the surface of the calcium phosphate to form a porous structure with random appearance. After the present invention is implanted in the human body or animal body, it can enhance the osteoinductive function and maintain sufficient mechanical strength for a long time, thereby facilitating the smooth growth of new bone. In the porous ceramics designed by the present invention, the pore pattern of at least one dimensional direction in the three-dimensional space direction is regular (such as triangle, square, rhombus, rectangle, hexagon, circle, ellipse or their combined shapes), and The distance from the center to the side of the pores is 50-2000 microns, and all the pores are interconnected.

[0037] The preparation process of this kind of porous ceramics is introduced below. The present invention mainly obtains porous ceramics throu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses porous calcium phosphate ceramics based on coating of calcium sulfate salt. Calcium phosphate is taken as a substrate, andthe surface of the calcium phosphate is coated with the calcium sulfate salt to form a porous structure with arbitrary shapes; the hole types of holes in at least one dimension of directions are regular in the three-dimensional space directions in the porous structure, and the distances between the centers and edges of the holes are 50 to 2000 micrometers, and all the holes are interpenetrating. In addition, the invention further provides a preparation method of the porous ceramics. According to the designed porous ceramics, the quickly-degraded calcium sulfate salt is on the surface, and the slowly-degraded calcium phosphate are inside, so after the ceramics are implanted into a body, a gradient degradation processcan be formed, so that the porous ceramics are endowed with very high osteogenic activity, and the ceramics can maintain enough mechanical strength in a given period. Therefore, the designed porous ceramics have very high osteogenic activity, and the risk of rapid disintegration after implantation of the ceramics in the early and middle periods is also reduced.

Description

technical field [0001] The invention relates to the technical field of bioceramics, in particular to a calcium phosphate porous ceramic coated with calcium sulfate salt and a preparation method thereof. Background technique [0002] Processing calcium phosphate ceramics into a porous structure to endow and improve the biological functions of calcium phosphate ceramics has always been a research topic for hard tissue defect repair materials. For this reason, porous calcium phosphate ceramics with different pore sizes and pore structures and corresponding preparation methods have been disclosed so far. Nevertheless, the bioactivity of porous calcium phosphate ceramics prepared based on the current method is not satisfactory. In particular, the osteoinductivity of current porous calcium phosphate ceramics is relatively weak. [0003] In order to improve the osteoinductivity of porous calcium phosphate, a more conventional clinical method is to combine bone growth factors with...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/85C04B38/00A61L27/10A61L27/12A61L27/56A61L27/58C04B35/447
CPCC04B41/85C04B41/5014C04B41/009C04B38/0003A61L27/10A61L27/12A61L27/56A61L27/58A61L2430/02C04B41/4535C04B35/447
Inventor 洪友良
Owner 陶合体科技(苏州)有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com