Ultra-low carbon steel coil for ultra-thin casing of oil filter and manufacturing method thereof

An oil filter and ultra-low carbon steel technology, applied in the field of metal material manufacturing, to achieve the effect of reducing inclusion blisters, uniform deformation, and reducing orange peel effect

Active Publication Date: 2021-10-01
新余钢铁股份有限公司 +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide an ultra-low carbon steel coil for an ultra-thin casing of an oil filter and a manufacturing method thereof to produce ultra-low carbon steel with a thinner thickness range in view of the deficiencies in the prior art Coil, the ultra-low carbon steel coil has higher strength, higher ductility, uniform structure and performance, no cracking in stamping, no tensile strain lines, uniform deformation of deep-drawing circular parts, no or reduced stress Ear defects and other advantages, the ultra-thin range of 0.30-0.44mm thick meets the pressure-bearing and deformation-resistant requirements of the ultra-thin shell of the oil filter. At the same time, the production process of the ultra-low carbon steel coil is simple, easy to operate, and high in production efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultra-low carbon steel coil for ultra-thin casing of oil filter and manufacturing method thereof
  • Ultra-low carbon steel coil for ultra-thin casing of oil filter and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] This embodiment produces an ultra-low carbon steel coil with a thickness of 0.44 mm for an ultra-thin casing of an oil filter, and the ultra-low carbon steel coil:

[0061] S1, through converter smelting, RH furnace refining, continuous casting into slabs with the following weight percentages: C: 0.0048%, Si: 0.019%, Mn: 0.46%, P: 0.012%, S: 0.008%, Al: 0.046%, Ti: 0.066%, N: 0.0028%, the rest is Fe and other unavoidable impurities;

[0062] S2, hot rolling: the slab is heated to 1190°C, the heating time is 175min, the soaking time is 41min, and then the hot-rolled plate is obtained through rough rolling and finish rolling, and the finish rolling temperature is 910-938°C, and then the The hot-rolled sheet is subjected to laminar cooling, and coiled into a hot-rolled coil after cooling at a coiling temperature of 591 to 630°C;

[0063] S3, cold rolling: pickling, rolling, cold rolling reduction rate 86.25%;

[0064] S4, annealing treatment: the temperature of the soaking...

Embodiment 2

[0067] This embodiment produces an ultra-low carbon steel coil with a thickness of 0.33 mm for an ultra-thin casing of an oil filter, and the ultra-low carbon steel coil:

[0068] S1, through converter smelting, RH furnace refining, continuous casting into slabs with the following weight percentages: C: 0.0030%, Si: 0.015%, Mn: 0.53%, P: 0.010%, S: 0.005%, Al: 0.070%, Ti: 0.070%, N: 0.0025%, the rest is Fe and other unavoidable impurities;

[0069] S2, hot rolling: the slab is heated to 1204°C, the heating time is 177min, the soaking time is 45min, and then the hot-rolled plate is obtained through rough rolling and finish rolling, and the finish rolling temperature is 915-924°C, and then the The hot-rolled sheet is subjected to laminar cooling, and coiled into a hot-rolled coil after cooling at a coiling temperature of 591-620°C;

[0070] S3, cold rolling: pickling, rolling, cold rolling reduction rate 88.0%;

[0071] S4, annealing treatment: the temperature of the soaking s...

Embodiment 3

[0074] This embodiment produces an ultra-low carbon steel coil with a thickness of 0.30mm for an ultra-thin casing of an oil filter, and the ultra-low carbon steel coil:

[0075] S1, through converter smelting, RH furnace refining, continuous casting into slabs with the following weight percentages: C: 0.0038%, Si: 0.016%, Mn: 0.50%, P: 0.008%, S: 0.003%, Al: 0.060%, Ti: 0.082%, N: 0.0020%, the rest is Fe and other unavoidable impurities;

[0076] S2, hot rolling: the slab is heated to 1210°C, the heating time is 180min, the soaking time is 50min, and then the hot-rolled plate is obtained through rough rolling and finish rolling, and the finish rolling temperature is 920-930°C, and then the The hot-rolled sheet is subjected to laminar cooling, and coiled into a hot-rolled coil after cooling, with a coiling temperature of 592-610°C;

[0077] S3, cold rolling: pickling, rolling, cold rolling reduction rate 88.46%;

[0078] S4, annealing treatment: the temperature of the soakin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
surface roughnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ultra-low carbon steel coil plate for an ultra-thin casing of an oil filter and a manufacturing method thereof. The chemical composition of the ultra-low carbon steel coil plate by weight percentage is: C: 0.0028-0.0050%, Si: ≤ 0.030%, Mn: 0.45~0.55%, P: ≤0.012%, S: ≤0.008%, Al: 0.045~0.080%, Ti: 0.065~0.085%, N: ≤0.0030%; Finish rolling to obtain a hot-rolled sheet, with a coiling temperature of 590-630 °C; then cold-rolling the hot-rolled coil, the cold rolling reduction rate is 80-90%, the annealing temperature is 700-760 °C, and the flat elongation is 1.0-2.0% + drawing Straightening the elongation rate of 0.03-0.10% to obtain an ultra-low carbon steel coil with a thickness of 0.30-0.44mm, its properties: Rel 220-270MPa, Rm 330-390MPa, hardness 54-60HR30T, elongation A 80 ≥40%. The product has higher strength, better ductility, uniform structure and properties, good isotropic homogeneity, good deep-drawing performance, no ear-making, and can completely replace the traditional 0.50-0.70mm thick specification material to meet automotive Parts thinning and lightweight requirements.

Description

technical field [0001] The invention relates to the technical field of metal material manufacturing, in particular to the technical field of cold-rolled steel strip manufacturing, in particular to an ultra-low carbon steel coil for an ultra-thin casing of an oil filter and a manufacturing method thereof. Background technique [0002] The oil filter is composed of a shell and a paper filter element, the paper filter element is inside the shell, and the shell is sealed with a threaded cover. The dirty oil pumped by the oil pump enters from 4 to 10 small holes reserved on the threaded cover plate, pushes the one-way valve at the opening of the oil filter and enters the periphery of the filter element, and after being filtered by the filter element, the clean oil enters the middle of the filter element , and then discharged from the oil outlet in the middle of the threaded cover plate to lubricate each movement pair of the car. The oil filter is mainly used to remove impurities...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/14C21D8/02
CPCC21D8/0226C21D8/0236C21D8/0273C22C38/004C22C38/02C22C38/04C22C38/06C22C38/14
Inventor 吴洪周云平马鹏飞夏雪生周杨金大华黄涛彭冲杨源华王振基吕乐易新平王婷华万伟杨同利徐细华周凌峰胥建平
Owner 新余钢铁股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com