Preparation method of copper plating brightening agent

A technology of brightener and copper plating, which is applied in the field of preparation of brightener for copper plating, can solve problems such as low brightness and slow light output speed, and achieve the effects of increasing dispersion, increasing brightness, and improving the effect of rapid crystallization

Active Publication Date: 2019-08-16
江西鹏凯环保工程设备有限公司
View PDF12 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Technical problem to be solved by the present invention: Aiming at the problems of slow light emitting speed and low brightness of current copper-plating brighteners, the present invention provides a preparation method of copper-plating brighteners

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] The preparation method of described catalyst is:

[0032] A. The mixture and ethanol solution were ultrasonically oscillated for 20 minutes according to the mass ratio of 1:5-7, then added acetic acid solution to adjust the pH to 2.0-2.5, left to age for 10 hours, spray-dried, and collected the dry matter;

[0033] B. Ball mill the dry matter, collect the ball milled matter, put the ball milled matter and concentrated sulfuric acid into the reaction kettle according to the mass ratio of 3:6-8 for mixing, then add urea with 10-15% of the ball-milled matter, and use nitrogen protection, Stir and react at 125-130°C for 20h;

[0034] C. After the stirring reaction is completed, use sodium hydroxide solution to adjust the pH to 8.0, add auxiliary materials with a mass of 10% to 15% of the ball-milled material, stir, discharge, freeze-dry, and freeze-dried material and synergist by mass ratio 2 ~ 5:7 mixed to get the catalyst.

[0035] The initiator is any one of sodium per...

Embodiment 1

[0043] The additive is formed by mixing cardanol and sorbitol at a mass ratio of 9:2.

[0044] The mixture is formed by mixing epichlorohydrin and ethylene oxide solution at a mass ratio of 5:12.

[0045] The additive is a mixture of alanine and tyrosine in a mass ratio of 5:3.

[0046] The mixture is formed by mixing tetrabutyl titanate and titanium tetrachloride in a mass ratio of 7:2.

[0047] The auxiliary material is ammonium bicarbonate.

[0048] The synergist is urea.

[0049] The preparation method of catalyst is:

[0050] A. The mixture and ethanol solution were ultrasonically oscillated for 20 minutes according to the mass ratio of 1:5, then acetic acid solution was added to adjust the pH to 2.0, left to age for 10 hours, spray-dried, and the dry matter was collected;

[0051]B. Ball-mill the dry matter, collect the ball-milled matter, put the ball-milled matter and concentrated sulfuric acid into the reaction kettle at a mass ratio of 3:6 for mixing, then add ur...

Embodiment 2

[0062] The additive is formed by mixing cardanol and sorbitol in a mass ratio of 8:2.

[0063] The mixture is formed by mixing epichlorohydrin and ethylene oxide solution at a mass ratio of 4:11.

[0064] The additive is a mixture of alanine and tyrosine in a mass ratio of 4:2.

[0065] The mixture is formed by mixing tetrabutyl titanate and titanium tetrachloride in a mass ratio of 7:3.

[0066] The auxiliary material is ammonium bicarbonate.

[0067] The synergist is urea.

[0068] The preparation method of described catalyst is:

[0069] A. The mixture and ethanol solution were ultrasonically oscillated for 20 minutes at a mass ratio of 1:6, then acetic acid solution was added to adjust the pH to 2.3, left to age for 10 hours, spray-dried, and the dry matter was collected;

[0070] B. Ball-mill the dry matter, collect the ball-milled matter, put the ball-milled matter and concentrated sulfuric acid into the reaction kettle at a mass ratio of 3:7 for mixing, then add ure...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of a copper plating brightening agent, and belongs to the technical field of additives for copper plating. Firstly, sodium hydroxide is used for activating chitosan to improve the activity, and is mixed with sorbitol and anacardol; through use of the mixture and through mixing, the chitosan and epoxy chloropropane are cross-linked to improve the bridging capacity; meanwhile, the anacardol is used as raw materials, and is combined with the modified chitosan; then, sulfamic acid is used to form an anacardol type anionic active agent under the catalyst effect; and meanwhile, acrylamide is polymerized to form polymerized acrylamide, which is combined on biomass negative ions. Products are used for absorbing copper ions in use; under the effect of the modified chitosan, the growth of crystal nucleuses is accelerated; and dodecylbenzene sulfonic acid is used for improving the dispersivity, so that the growth speed of grains is lower than the growth speed of the crystal nucleuses, the crystal refining is improved, and the brightening effect is improved.

Description

technical field [0001] The invention relates to a preparation method of a brightener for copper plating, which belongs to the technical field of additives for copper plating. Background technique [0002] Copper is a metal with a purplish red luster, which has ductility, good electrical conductivity and thermal conductivity. The copper plating is beautiful rose color, the nature of copper is soft, easy to polish, copper plating is often used as nickel plating, tin plating, chrome plating , silver-plated and gold-plated bottom layer to improve the bonding force between the metal of the body and the surface coating; it can reduce the pores of the coating and improve the anti-corrosion performance of the coating; in some cases, copper-plated steel parts can replace copper parts to save copper. For decorative chrome plating, the original copper thin nickel plating is often used to save nickel metal. Copper plating is also used to prevent carburization, nitriding and cyanidation ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C25D3/38
CPCC25D3/38
Inventor 梁生
Owner 江西鹏凯环保工程设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap