High-strength anti-deformation corrugated paper box and production technology

A technology of corrugated box and production process, which is applied in the field of corrugated box, can solve the problem of low strength of corrugated box, and achieve the effect of simple structure, increased service life and increased structural strength

Inactive Publication Date: 2019-08-09
伟岸包装制品(苏州)有限公司
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Aiming at the deficiencies of the prior art, the present invention provides a high-strength anti-deformation corrugated box and its production process, which solves the problem of low strength of the existing corrugated box

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength anti-deformation corrugated paper box and production technology
  • High-strength anti-deformation corrugated paper box and production technology
  • High-strength anti-deformation corrugated paper box and production technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] A production process of a high-strength anti-deformation corrugated box, comprising the following steps:

[0057] A: Raw material pretreatment: Put waste paper, bamboo stalks and wheat straws into a pulverizer to process into scraps, then dissociate the scraps into fibers, and then filter and screen to remove impurities in the fibers;

[0058] B: Beating: Pour the crushed fiber into the refiner, add silica, vinyl acetate, polyethylene fiber and water, the ratio of silica, vinyl acetate, polyethylene fiber is 1:1: 5. Then beat the pulp to obtain a uniformly mixed pulp, and then place the pulp for 0.5 hours, and the concentration of the pulp is 5-10%;

[0059] C: Enzymolysis: Cool the fiber slurry to 20°C, add amylase and acid-base regulator, the enzyme activity of amylase is 1.8 million U / g, the enzymolysis treatment time is 1h, and the pH of the slurry is controlled at 4 ;

[0060] D: Preparation of paper: use a paper machine to dehydrate the fiber slurry and press it...

Embodiment 2

[0068] A production process of a high-strength anti-deformation corrugated box, comprising the following steps:

[0069] A: Raw material pretreatment: Put waste paper, bamboo stalks and wheat straws into a pulverizer to process into scraps, then dissociate the scraps into fibers, and then filter and screen to remove impurities in the fibers;

[0070] B: Beating: Pour the crushed fiber into the refiner, add silica, vinyl acetate, polyethylene fiber and water, the ratio of silica, vinyl acetate, polyethylene fiber is 1:1: 5. Then beat the pulp to obtain a uniformly mixed pulp, then place the pulp for 1 hour, and the concentration of the pulp is 8%;

[0071] C: Enzymolysis: Cool the fiber slurry to 30°C, add amylase and acid-base regulator, the enzyme activity of amylase is 1.8 million U / g, the enzymolysis treatment time is 1.5h, and the pH of the slurry is controlled at 5;

[0072] D: Preparation of paper: use a paper machine to dehydrate the fiber slurry and press it into sha...

Embodiment 3

[0080] A production process of a high-strength anti-deformation corrugated box, comprising the following steps:

[0081] A: Raw material pretreatment: Put waste paper, bamboo stalks and wheat straws into a pulverizer to process into scraps, then dissociate the scraps into fibers, and then filter and screen to remove impurities in the fibers;

[0082] B: Beating: Pour the crushed fiber into the refiner, add silica, vinyl acetate, polyethylene fiber and water, the ratio of silica, vinyl acetate, polyethylene fiber is 1:1: 5. Then beat the pulp to obtain a uniformly mixed pulp, then place the pulp for 2 hours, and the concentration of the pulp is 10%;

[0083] C: Enzymolysis: Cool the fiber slurry to 40°C, add amylase and acid-base regulator, the enzyme activity of amylase is 1.8 million U / g, the enzymolysis treatment time is 2 hours, and the pH of the slurry is controlled at 6 ;

[0084] D: Preparation of paper: use a paper machine to dehydrate the fiber slurry and press it in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength anti-deformation corrugated paper box, and relates to technical fields related to corrugated paper boxes. The paper box comprises a bottom plate, side plates are fixedly connected on the bottom plate, a top plate is fixedly connected to the top ends of the side plates, a support is arranged between the bottom plate and the side plates, and the bottom plate and the side plates are fixedly connected through the support. First reinforcing ribs are fixedly connected between the bottom plate and the side plates, and second reinforcing ribs are fixedly connected between the side plates and the top plate. The invention further discloses a production technology of the high-strength anti-deformation corrugated paper box. The production technology comprises the following steps of A, raw material preprocessing; B, pulping; C, enzymolysis; D, paper preparation, E, heat treatment; F, gluing; G, corrugated paper board preparation; H, line pressing; I, printing; J, assembling. Through the arrangement of the support, the first reinforcing ribs and the second reinforcing ribs, the compression resistance of the eight corners of the corrugated paper box can beenhanced, the corrugated paper box is prevented from deforming, and the corrugated paper box is simple in structure, low in manufacturing cost and long in service life.

Description

technical field [0001] The invention relates to the related technical field of corrugated cartons, in particular to a high-strength anti-deformation corrugated carton and a production process. Background technique [0002] Corrugated cardboard is die-cut, creasing, nailed or glued to make corrugated boxes. Corrugated carton is the most widely used packaging product, and its consumption has always been the first among all kinds of packaging products. Including calcium plastic corrugated box. For more than half a century, corrugated boxes have gradually replaced wooden boxes and other transportation packaging containers due to their superior performance and good processing performance, and have become the main force of transportation packaging. In addition to protecting the goods and facilitating storage and transportation, it also plays the role of beautifying and promoting the goods. [0003] With the continuous increase of market demand, the scale of corrugated box produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21C5/00D21H17/68D21F11/00D21H27/40D21H27/10D21H11/14D21H11/12B31F1/20B31B50/00B31B50/88B65D5/44B32B29/08B32B3/28B32B29/00B32B9/00B32B9/04B32B17/02B32B3/12B32B17/12
CPCB31F1/20B32B3/12B32B3/28B32B5/02B32B5/26B32B9/00B32B9/04B32B9/047B32B17/067B32B29/002B32B29/08B32B2262/101B32B2262/106B32B2307/306B32B2307/3065B32B2307/558B32B2307/714B32B2439/62B65D5/441B31B50/00B31B50/88D21C5/00D21C5/005D21F11/00D21H11/12D21H11/14D21H17/68D21H27/10D21H27/40
Inventor 王飞
Owner 伟岸包装制品(苏州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com