A kind of high early strength type non-alkali liquid accelerator and its preparation method and application

An early-strength, quick-setting agent technology, applied in the field of building material admixtures, can solve the problems of shortening the initial and final setting time of cement, reducing shotcrete, and only compressive strength, so as to facilitate the realization of industrialized large-scale production and improve the early Strength, the effect of improving the compressive strength

Active Publication Date: 2021-09-24
GUANGZHOU INSTITUTE OF BUILDING SCIENCE CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The addition of fluoride can significantly shorten the initial and final setting time of cement, and reduce the rebound of shotcrete. However, the biggest problem faced by this type of accelerator is that the early strength is low, and the compressive strength of some products in one day is even only 2~ 3MPa, seriously endangering construction safety

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high early strength type non-alkali liquid accelerator and its preparation method and application
  • A kind of high early strength type non-alkali liquid accelerator and its preparation method and application
  • A kind of high early strength type non-alkali liquid accelerator and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A high-early-strength non-alkali liquid quick-setting agent is composed of the following raw materials in weight percentage.

[0035] Polyaluminum sulfate: 40%,

[0036] Metakaolin: 10%,

[0037] Nano silica sol: 15%,

[0038] N,N-Dimethylethanolamine: 6%,

[0039] Organic acids: 4%,

[0040] Thickener: 0.05%,

[0041] Dispersant: 0.05%,

[0042] Water: 24.9%

[0043] The above-mentioned raw materials are prepared according to the above-mentioned preparation method to obtain a high-early-strength type alkali-free liquid accelerator.

Embodiment 2

[0045] A high-early-strength non-alkali liquid quick-setting agent is composed of the following raw materials in weight percentage.

[0046] Polyaluminum Sulfate: 55%,

[0047] Metakaolin: 5%,

[0048] Nano silica sol: 5%,

[0049] Diethylene glycol amine: 4%,

[0050] Organic acids: 3%,

[0051] Thickener: 0.01%,

[0052] Dispersant: 0.01%,

[0053] Water: 27.98%.

[0054] The above-mentioned raw materials are prepared according to the above-mentioned preparation method to obtain a high-early-strength type alkali-free liquid accelerator.

Embodiment 3

[0056] A high-early-strength non-alkali liquid quick-setting agent is composed of the following raw materials in weight percentage. Polyaluminum sulfate: 50%,

[0057] Metakaolin: 8%,

[0058] Nano silica sol: 10%,

[0059] N-Methyldiethanolamine: 3%,

[0060] Organic acid: 1%,

[0061] Thickener: 0.03%,

[0062] Dispersant: 0.02%,

[0063] Water: 27.95%.

[0064] The above-mentioned raw materials are prepared according to the above-mentioned preparation method to obtain a high-early-strength type alkali-free liquid accelerator.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
particle diameteraaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-early-strength non-alkali liquid quick-setting agent and its preparation method and application, belonging to the technical field of building material admixtures. The quick-setting agent is composed of the following raw materials in weight percent: 40-50% of polyaluminum sulfate, 5-10% of metakaolin, 5-15% of nano-silica sol, 3-6% of alcohol amine, 1-4 % of organic acid, 0.01-0.05% of thickener, 0.01-0.05% of dispersant, and the balance is water. On the basis of meeting the national standard "Accelerator for Shotcrete" (GB / T35159-2017), the accelerator can also effectively improve the compressive strength of cement mortar in one day, reaching more than 20MPa, and some cement mortar can resist compression in one day The strength can even reach above 25MPa.

Description

technical field [0001] The invention relates to the technical field of building material admixtures, in particular to a high-early-strength alkali-free liquid accelerator and its preparation method and application. Background technique [0002] Accelerator, as an indispensable admixture in shotcrete construction, plays an important role in accelerating the setting and hardening of cement and reducing the rebound of shotcrete. It is widely used in tunnel construction and rapid repair of mortar. With the continuous advancement of infrastructure construction at home and abroad, the amount of accelerators is increasing. However, there are various types of accelerators currently used in engineering. Powder accelerators are the earliest accelerators put into use. Although they are cheap and have good coagulation-accelerating effects, they are seriously polluted by dust and poor in environmental protection during construction. Promote apps. [0003] With the emergence of the wet ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/38C04B103/12
CPCC04B40/0039C04B2103/12C04B22/148C04B22/00C04B22/06C04B24/122C04B24/04C04B24/383C04B2103/302
Inventor 顾本庆陈小龙钟开红孙申美熊旭峰
Owner GUANGZHOU INSTITUTE OF BUILDING SCIENCE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com