An acoustic emission detection and metal component technology, which is applied in material analysis using acoustic emission technology, processing response signals of detection, and analysis of solids using sonic/ultrasonic/infrasonic waves, etc. Time and other problems, to achieve the effect of convenient extraction, increased signal-to-noise ratio, and easy identification

Active Publication Date: 2019-06-18
CHINA SPECIAL EQUIP INSPECTION & RES INST
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

(2) When Hmax is constant, as the frequency of the alternating magnetic field increases, the acoustic emission signal output by the material in unit time increases, and the MAE signal intensity gradually increases, but the adjacent signals overlap gradually. resulting in a decrease in the signal-to-noise ratio; it can be seen that increasing the strength and frequency of the alternating magnetic field can only improve the strength and signal ratio of the MAE signal to a certain extent
The acquisition of suitable conditions requires trial debugging of multiple parameters (such as magnetic field strength, magnetic field frequency, electromagnetic yoke core size and coil turns, nominal diameter of enameled wire, etc.), which is time-consuming and laborious, and requires on-site testing under working conditions. cause great inconvenience

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magneto-acoustic emission detection method for creep damage of ferromagnetic metal member
  • Magneto-acoustic emission detection method for creep damage of ferromagnetic metal member
  • Magneto-acoustic emission detection method for creep damage of ferromagnetic metal member

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] 1) Place the self-made U-shaped electromagnetic yoke and the acoustic emission sensor in the central area of ​​the 1Cr5Mo steel sample that has not been subjected to the creep test in a relatively fixed position.

[0042] 2) Load a triangular wave voltage signal with a periodic symmetry of 50% to the coil of the U-shaped electromagnetic yoke. The frequency of the signal is 10 Hz. The voltage signal is generated by a function generator and input to the coil after being amplified 10 times by a power amplifier. Since the MAE signal is generated under the alternating magnetic field excited by the triangular wave voltage signal with a symmetry of 50%, the 1Cr5Mo steel sample generates two identical MAE signals within one magnetization period, that is, the frequency of the MAE signal is equal to the frequency of the alternating magnetic field double.

[0043] Use the function generator to increase the peak-to-peak value of the output voltage signal from 0.1Vpp with a gradient...

Embodiment 2

[0057] Same as the member to be tested and the detection steps described in Embodiment 1, only the steps of adjusting the magnetomotive force are different, as follows:

[0058] By adjusting the nominal diameter of the coil enameled wire to obtain a "T" shaped envelope, the number of turns of the U-shaped electromagnetic yoke coil is 800 turns, and the nominal diameter of the enameled wire for making the coil is 0.04mm, and the standard Enameled wires with diameters of 0.08mm, 0.12mm, 0.16mm, 0.2mm, 0.25mm, 0.31mm, 0.35mm, 0.4mm, 0.45mm, 0.5mm, 0.55mm, 0.60mm, 0.64mm, 0.69mm and 0.72mm are used instead An enameled wire with a nominal diameter of 0.04mm is wound on a magnetic core with a coil having the same number of turns. Keep the voltage signal unchanged, collect the MAE signal and the corresponding coil current under the coils wound by enameled wires of various nominal diameters, and find that the MAE signal of the "T"-shaped envelope is generated when the nominal diameter...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a magneto-acoustic emission detection method for the creep damage of a ferromagnetic metal member. Triangular wave voltage signals with the symmetry of 50% is used for generating an excitation magnetic field, a loading voltage is increased in an ascending order until a magneto-acoustic emission signal having a fusiform envelope is obtained, and a corresponding voltage peakvalue is recorded; with triangular wave signals with the symmetry of 0% or 100%, voltage signals being equal to or higher than the voltage peak value are used for generating an excitation magnetic field and a magneto-acoustic emission signal having T-shaped envelope is obtained by improving the magnetomotive force of the coil; and then an average peak value of the magneto-acoustic emission signals corresponding to triangular voltage right-angle sides in multiple cycles is calculated and the average value is used as a characteristic parameter for measuring the stress state, creep or fatigue damage degree of a ferromagnetic metal member.

Description

technical field [0001] The invention belongs to the technical field of nondestructive detection of material damage, and in particular relates to a magnetoacoustic emission detection method for creep damage of ferromagnetic metal components. Background technique [0002] Magneto acoustic emission (MAE for short) refers to the phenomenon of acoustic emission produced by ferromagnetic metal materials due to changes in the magnetic domain structure under the action of an alternating magnetic field. For the detection principle of MAE technology, please refer to the attached figure 1 : An alternating current or voltage is applied to both ends of the coil of the U-shaped electromagnetic yoke, and the coil generates an alternating magnetic field to repeatedly magnetize the ferromagnetic metal member that forms a magnetic circuit with the yoke. Due to the anisotropy of the magnetic crystal, the irreversibility of the magnetic domain wall Displacement, the generation and annihilation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N29/04G01N29/14G01N29/44G01N29/46
Inventor 沈功田沈永娜高广兴张文君
Owner CHINA SPECIAL EQUIP INSPECTION & RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap