A kind of porous sulfur/carbon composite material and its preparation method and lithium-sulfur battery application

A carbon composite material, carbon composite technology

Active Publication Date: 2021-06-22
DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The utilization rate of sulfur is low, and the utilization rate of active sulfur is very low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Weigh 8g of sublimated sulfur, place it in a closed reactor A with a volume of 5L, heat it to 150°C, and react for 5h; raise the temperature of the reactor to 500°C, and keep the internal temperature of the reactor at 500°C. The sulfur vapor in the reactor A is sprayed into the reactor B by nitrogen at a pressure of 0.5 MPa, and the diameter of the nozzle is 0.1 mm. In addition, the carbon disulfide emulsion dispersed with 10% activated carbon was atomized into particles of 20 μm at a temperature of 20°C and sprayed into reactor B at the same time, and 0.05% by mass of six Chloroparaxylene. Control the amount of emulsion sprayed into container B and the flow rate of sulfur vapor sprayed into container B. The mass ratio of emulsion to sulfur vapor is 200:1, so as to achieve the contact between sulfur vapor and organic solvent droplets containing carbon materials The temperature was 45°C. Collect the prepared solid material, extract it with carbon disulfide, dry the obt...

Embodiment 2

[0031] Weigh 4g of precipitated sulfur, place it in a closed reactor A with a volume of 5L, heat it to 140°C, and react for 5h; raise the temperature of the reactor to 700°C, and keep the internal temperature of the reactor at 700°C. The sulfur vapor in the reactor A is sprayed into the reactor B by nitrogen at a pressure of 0.5 MPa, and the diameter of the nozzle is 0.2 mm. In addition, the carbon disulfide emulsion dispersed with 20% activated carbon was atomized into 20 μm particles at a temperature of 25°C, and sprayed into reactor B at the same time, and 0.1% by mass of olefin was added to the dispersant carbon disulfide. Propyl bromide. Control the amount of emulsion sprayed into container B and the flow rate of sulfur vapor sprayed into container B, the mass ratio of emulsion to sulfur vapor is 100:1, so as to achieve the contact between sulfur vapor and organic solvent droplets containing carbon materials The temperature was 45°C. Collect the prepared solid material,...

Embodiment 3

[0033] Weigh 8g of refined sulfur, place it in a closed reactor A with a volume of 5L, heat it to 150°C, and react for 5h; raise the temperature of the reactor to 600°C, and keep the internal temperature of the reactor at 600°C. The sulfur vapor in the reactor A is sprayed into the reactor B by nitrogen at a pressure of 0.8 MPa, and the diameter of the nozzle is 0.2 mm. In addition, the carbon disulfide emulsion dispersed with 10% activated carbon was atomized into 20 μm particles at a temperature of 30°C, and sprayed into reactor B at the same time, and 0.1% by mass of olefin was added to the dispersant carbon disulfide. Propyl Chloride. Control the amount of emulsion sprayed into container B and the flow rate of sulfur vapor sprayed into container B, the mass ratio of emulsion to sulfur vapor is 100:1, so as to achieve the contact between sulfur vapor and organic solvent droplets containing carbon materials The temperature was 45°C. Collect the prepared solid material, ext...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a porous sulfur / carbon composite material and a preparation method, and the application of the prepared porous sulfur / carbon composite material as a positive electrode lithium-sulfur battery. The preparation scheme is as follows: 1) Melt solid sulfur at low temperature for a certain period of time to liquefy the sulfur and undergo ring-opening fusion reaction of S8; 2) Raise the temperature to gasify the liquid sulfur, and spray the gasified sulfur into the sealed reactor at high speed 3) Spray the pre-prepared low-temperature organic solvent dispersion of carbon into the closed reactor at the same time, so that the high-temperature sulfur vapor is quenched, and a composite solid material of sulfur and carbon is formed during the quenching process; 4 ) Separating porous sulfur / carbon solids and organic solvents and extracting them to prepare high-purity porous sulfur / carbon composites; 5) preparing porous sulfur / carbon composites into electrode materials that can be used for lithium-sulfur battery cathodes after high-speed ball milling . The material can be used to prepare the positive electrode of lithium-sulfur batteries, and exhibits excellent electrochemical performance.

Description

technical field [0001] The invention belongs to the field of chemical power sources, and relates to a method for preparing a sulfur cathode material, in particular to a method for preparing a high-performance porous sulfur / carbon composite material. Background technique [0002] Social development has an increasing demand for energy storage technology. Lithium-sulfur batteries have high theoretical specific capacity (1675mAh / g) and theoretical energy density (2600Wh / kg), which may meet new battery energy storage systems (such as portable electronic devices, electric vehicles, electrochemical energy storage stations) in the future. It has broad application potential and has become a research hotspot of high specific energy secondary batteries. [0003] Elemental sulfur is an insulator of electrons and ions, and its electronic and ion conductivity is extremely poor. At the same time, the dissolution of lithium polysulfide, a product of lithium discharge, leads to serious capa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/36H01M4/38H01M4/587H01M10/052
CPCY02E60/10
Inventor 陈剑郭德才
Owner DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com