High-temperature-resistant flame-retardant silicone rubber and preparation method thereof
A technology of silicone rubber and high temperature resistance, applied in the field of high temperature resistant flame retardant silicone rubber and its preparation, can solve the problem that silicone rubber cannot have excellent flame retardancy and high temperature resistance at the same time, and achieve excellent mechanical properties and excellent high temperature resistance. and flame retardant performance, the effect of strong operability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0035] A kind of high-temperature-resistant and flame-retardant silicone rubber proposed by the present invention comprises the following components in parts by weight: 100 parts of vinyl-terminated silicone rubber raw rubber, 40 parts of white carbon black, 30 parts of filler, and 10 parts of flame retardant , 3 parts of structural control agent, 2 parts of heat-resistant agent, 0.5 part of coupling agent and 0.1 part of release agent;
[0036] Among them, the molecular weight of the vinyl-terminated silicone rubber raw rubber is 500,000 to 900,000, and the vinyl content is 0.03% to 3.0%. Further, the molecular weight and vinyl content of the vinyl-terminated silicone rubber raw rubber can be selected from one of them. or multiple combinations;
[0037] For example: 600,000 vinyl content 0.04% raw rubber 75phr is used in conjunction with 600,000 vinyl content 0.23% raw rubber 25phr;
[0038] For example: 85 phr of 800,000 molecular weight raw rubber with 0.04% vinyl content,...
Embodiment 2
[0067] A kind of high-temperature-resistant and flame-retardant silicone rubber proposed by the present invention comprises the following components in parts by weight: 100 parts of vinyl-terminated silicone rubber raw rubber, 50 parts of white carbon black, 50 parts of filler, and 20 parts of flame retardant , 5 parts of structural control agent, 4 parts of heat-resistant agent, 1 part of coupling agent and 0.6 part of release agent;
[0068] Among them, the molecular weight of the vinyl-terminated silicone rubber raw rubber is 500,000 to 900,000, and the vinyl content is 0.03% to 3.0%. Further, the molecular weight and vinyl content of the vinyl-terminated silicone rubber raw rubber can be selected from one of them. or multiple combinations;
[0069] For example: 600,000 vinyl content 0.04% raw rubber 75phr is used in conjunction with 600,000 vinyl content 0.23% raw rubber 25phr;
[0070] For example: 85 phr of 800,000 molecular weight raw rubber with 0.04% vinyl content, 1...
Embodiment 3
[0099] A kind of high-temperature-resistant and flame-retardant silicone rubber proposed by the present invention comprises the following components in parts by weight: 100 parts of vinyl-terminated silicone rubber raw rubber, 60 parts of white carbon black, 70 parts of filler, and 30 parts of flame retardant , 7 parts of structural control agent, 5 parts of heat-resistant agent, 2 parts of coupling agent and 1 part of release agent;
[0100] Among them, the molecular weight of the vinyl-terminated silicone rubber raw rubber is 500,000 to 900,000, and the vinyl content is 0.03% to 3.0%. Further, the molecular weight and vinyl content of the vinyl-terminated silicone rubber raw rubber can be selected from one of them. or multiple combinations;
[0101] For example: 600,000 vinyl content 0.04% raw rubber 75phr is used in conjunction with 600,000 vinyl content 0.23% raw rubber 25phr;
[0102] For example: 85 phr of 800,000 molecular weight raw rubber with 0.04% vinyl content, 10...
PUM
Property | Measurement | Unit |
---|---|---|
Specific surface area | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com