All-steel radial truck tire tread formula rubber compound, and preparation method and tire thereof

A radial tire and tread technology, applied in the field of all-steel truck radial tire tread compound and preparation

Inactive Publication Date: 2019-06-04
CHAOYANG LONG MARCH TIRE
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a kind of all-steel radial truck tire tread compound compound and preparation method and tire, to solve the existing all-steel truck radial tire that proposes in the above-mentioned background technology for truck, bus tire, tire rolling resistance Energy consumption accounts for 15% of fuel consumption, every 3% reduction in rolling resistance can reduce fuel consumption by 1%, and the contribution of tread to rolling resistance is 54% in the compound formula of different parts of the tire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • All-steel radial truck tire tread formula rubber compound, and preparation method and tire thereof
  • All-steel radial truck tire tread formula rubber compound, and preparation method and tire thereof
  • All-steel radial truck tire tread formula rubber compound, and preparation method and tire thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035]

[0036] In this embodiment, the denominator batching and final batching process of the sizing material preparation method:

[0037] Master refining process:

[0038] 1) Add smoked sheet RSS3# plasticizing rubber, highly dispersed white carbon black, super silane coupling agent, and other masterbatch powders except zinc oxide, press the top bolt to keep

[0039] 2) Raise the top bolt to add carbon black, press the top bolt to raise the temperature of the rubber to 90-120°C;

[0040] 3) Raise the top bolt and add zinc oxide;

[0041] 4) Press the top bolt to heat up the rubber material to

[0042] 5) Press the top bolt to make the rubber Constant temperature mixing Degumming;

[0043] 6) the sizing material is discharged to the lower auxiliary machine mill for pounding glue, and the second mill is cut off for three times, and the second mill is automatically stirred for 1.5 minutes, and the third mill is delivered to go out;

[0044] Final refining process: ...

Embodiment 2

[0048]

[0049] In the present embodiment, the denominator mixing and final mixing process of the compound preparation method are the same as in Example 1

[0050] The low-rolling resistance all-steel radial truck tire tread compound performance test made with the formula of this embodiment

[0051]

[0052] The test data is as follows:

[0053] Embodiment and comparative example tire machine tool and actual vehicle test parameters (tire specification 12R22.518 (L)-288)

[0054]

[0055] The rubber compound formulated in this example has good processing performance in the production process, high processing safety, stable geometric dimensions of the extruded semi-finished product, no return phenomenon, and fully meets the conditions for batch industrial production. The 12R22.5LM288 tire produced using the rubber compound of this example has passed the American SmartWay rolling resistance certification. The tire has excellent fuel consumption and handling performance ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an all-steel radial truck tire tread formula rubber compound and a preparation method and a tire thereof. The all-steel radial truck tire tread formula rubber compound comprises the following basic formula composition (by mass): 100 parts of natural rubber, 40.0-60.0 parts of high-dispersion white carbon black, 1.0-10.0 parts of high-structure wear-resistant carbon black,3.0-7.0 parts of super silane, 1.5-4.0 parts of an activator, 1.0-2.5 parts of an anti-aging agent 1, 0.5-2.0 parts of an anti-aging agent 2, 1.0-3.0 parts of an anti-aging agent 3, 2.0-3.0 parts of aplasticizer, 3.0-5.0 parts of an activator zinc oxide, 1.0-2.0 parts of a vulcanizing agent S, 1.0-2.5 parts of an accelerant, 2.0-4.0 parts of a synergist, and 0.1-0.3 part of an anti-scorching agent CTP. In comparison with the prior art, the invention has the following beneficial effects: by use of the tire thread formula, various physical and mechanical properties of the rubber compound and high speed and durability of the tire can meet the requirements of normal use; and the produced tire has excellent fuel consumption and controllability, and has good controllability, low rolling resistance, high mileage and long service life and is fuel-saving and environmentally-friendly in actual truck loading and use process.

Description

technical field [0001] The invention relates to the technical field of production of all-steel radial truck tires, in particular to an all-steel radial truck tire tread formula compound, a preparation method and a tire. Background technique [0002] Tires are an important safety component of automobiles, and the tire industry is one of the important areas of national economic development. The rolling resistance and wet grip performance of tires, related to the environmental protection and safety performance of tires, have been included in the labeling laws of tires by many countries Among them, the rolling resistance of the tire is closely related to the carbon dioxide emission of the vehicle. [0003] Tires have low rolling resistance and low fuel consumption, which can greatly reduce vehicle carbon dioxide emissions. The improvement of the anti-wet skid performance of the tire reflects that the tire does not slip in rainy days, has shorter braking distance and better dama...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L7/00C08K3/36C08K3/04C08K3/22C08K5/548C08K13/02B60C1/00
CPCY02T10/86
Inventor 张文广李春波王晶程谟伟王友权
Owner CHAOYANG LONG MARCH TIRE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com