Hemp seed oil-based double-crosslinkable resin monomer molecule and preparation method thereof

A technology of hemp seed oil and double cross-linking is applied in the preparation of carboxylate, chemical instruments and methods, preparation of organic compounds, etc., which can solve the problems of high volatility, complex formula, high content of toxic components, and achieve high hardness. , high-strength effect

Active Publication Date: 2019-05-31
INST OF CHEM IND OF FOREST PROD CHINESE ACAD OF FORESTRY
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The technical problem to be solved: the traditional double cross-linked resin has the disadvantages of complicated formula, high volatility, and high content of toxic components. In order to improve its shortcomings, the present invention provides a hemp seed oil-based double cross-linked resin monomer molecule and its preparation method, the product can be cross-linked and cured with epoxy resin, and the prepared resin material has the characteristics of strong rigidity and high hardness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hemp seed oil-based double-crosslinkable resin monomer molecule and preparation method thereof
  • Hemp seed oil-based double-crosslinkable resin monomer molecule and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The hemp seed oil is hydrolyzed to obtain unsaturated hemp seed oleic acid, which is then mixed evenly with m-xylene-4-sulfonic acid and formic acid accounting for 0.5% of the hemp seed oil mass, and added dropwise within 30 minutes. Hempseed oleic acid quality 35% hydrogen peroxide, react at 40 ℃ for 2h, the collected hydroxyl-containing hempseed oleic acid and tetrabutylammonium bisulfate accounting for 1% of the hydroxyl-containing hempseed oleic acid quality React with 2,4-dinitrophenol, which accounts for 0.5‰ of the mass of hempseed acid containing hydroxyl groups, and glycidyl methacrylate in an equimolar ratio of hydroxyl groups in unsaturated hempseed oil containing hydroxyl groups at 90°C 4h, obtain polyhydroxy hemp seed oil-based monomer, then polyhydroxy hemp seed oil-based monomer and maleic anhydride react 5h at 60 DEG C according to the mol ratio of hydroxyl:maleic anhydride=1:1, obtain hemp seed Hempseed oil-based double cross-linked resin monomer.

Embodiment 2

[0020] The hemp seed oil is hydrolyzed to obtain unsaturated hemp seed oleic acid, which is mixed evenly with m-xylene-4-sulfonic acid and formic acid accounting for 1.3% of the mass of hemp seed oil, and added dropwise within 30 minutes. Hempseed oleic acid quality 82.5% hydrogen peroxide, at 60 ° C for 3.5h, the collected hydroxyl-containing hempseed oleic acid and triethylbenzyl that accounted for 0.5% of the hydroxyl-containing hempseed oleic acid quality Ammonium chloride and hydroquinone accounting for 1‰ of the mass of hempseed acid containing hydroxyl groups, and glycidyl methacrylate in an equimolar ratio of hydroxyl groups in unsaturated hempseed acid containing hydroxyl groups were reacted at 118°C for 2h , to obtain the polyhydroxy hemp seed oil-based monomer, then react the polyhydroxy hemp seed oil-based monomer with maleic anhydride at 85°C for 2h according to the molar ratio of hydroxyl:maleic anhydride=1:1, to obtain the hemp seed Kernel oil based double cross...

Embodiment 3

[0022]The hemp seed oil is hydrolyzed to obtain unsaturated hemp seed oleic acid, which is then mixed evenly with m-xylene-4-sulfonic acid and formic acid accounting for 0.8% of the hemp seed oil mass, and added dropwise within 30 minutes. 45% hydrogen peroxide of hemp seed oleic acid quality, react 4h at 50 ℃, will collect the hemp seed oleic acid containing hydroxyl and account for 1% tetrabutyl hydrogen sulfate of the hemp seed oleic acid quality containing hydroxyl Ammonium, 2,6-dinitro-p-cresol accounting for 0.8‰ of the mass of the hydroxyl-containing hempseed oleic acid, and glycidyl methacrylate in an equimolar ratio to the hydroxyl groups in the hydroxyl-containing unsaturated hempseed oleic acid The ester was reacted at 108°C for 3h to obtain the polyhydroxy hempseed oil-based monomer, and then the polyhydroxyhempseed oil-based monomer and maleic anhydride were mixed at 70°C according to the molar ratio of hydroxyl:maleic anhydride=1:1 After reacting for 4 hours, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Provided are a hemp seed oil-based double-crosslinkable resin monomer molecule and a preparation method thereof. Firstly, unsaturated hemp seed oil is enabled to be subjected to hydrolysis reaction toprepare unsaturated hemp seed oil acid, then the unsaturated hemp seed oil acid reacts with a proper amount of catalyst, an oxygen carrier formic acid and hydrogen peroxide to obtain hydroxyl-containing unsaturated hemp seed oil acid, the hydroxyl-containing unsaturated hemp seed oil acid reacts with a proper amount of catalyst, a polymerization inhibitor and glycidyl methacrylate to obtain a polyhydroxy hemp seed oil-based monomer,and the prepared polyhydroxy hemp seed oil-based monomer reacts with a proper amount of maleic anhydride to obtain the hemp seed oil-based double-crosslinkable resin monomer molecule. The hemp seed oil is selected as a raw material to prepare a multi-crosslinking resin monomer product, environment-friendly resources are fully utilized, the product can carry outdouble crosslinking reaction, and the cured product has excellent mechanical strength.

Description

technical field [0001] The invention belongs to the field of double-crosslinked curing systems in the field of macromolecules, and in particular relates to a hemp seed oil-based double-crosslinked resin monomer molecule and a preparation method thereof. Background technique [0002] In recent years, with the emergence of problems such as environmental pollution and the shortage of non-renewable resources, people have paid more and more attention to natural products. Biomass raw materials are not only rich in sources, renewable, but also cheap and biodegradable. Vegetable oils and fats contain a large amount of unsaturated fatty acids, such as oleic acid, linoleic acid, and oleic acid. Unsaturated fatty acids can undergo various types of chemical reactions such as halogenation, oxidation, hydrogenation, deoxygenation, polymerization, degradation, etc. At present, oil is widely used in the manufacture of paints, inks, emulsifiers, lubricants, etc., and a variety of oil-based...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07C69/732C07C67/00
Inventor 李守海易靖李梅夏建陵张燕杨小华陈瑶丁呈祥
Owner INST OF CHEM IND OF FOREST PROD CHINESE ACAD OF FORESTRY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com