High-rubber asphalt master batch and low-temperature environmental-friendly production process thereof

A production process and asphalt technology, applied in the field of high-rubber asphalt masterbatch and its low-temperature environmental protection production process, can solve the problems of high temperature viscosity of modified asphalt, substandard environmental emission indicators, easy settling of asphalt, etc., and achieve good aging resistance performance. , shorten the production cycle, enhance the effect of compatibility

Active Publication Date: 2019-05-28
JIANGSU BAOLI INT INVESTMENT CO LTD +2
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The "high-adhesive asphalt masterbatch" described in the present invention aims to solve the problems of high shear temperature, strong odor, and substandard environmental emission indicators in the traditional production process of high-adhesive asphalt, and at the same time solve the problems in the field of high-viscosity composite modified asphalt. Generally, rubber powder is not desulfurized and degraded due to high desulfurization cost, and the particles are relatively coarse, which leads to easy sedimentation in asphalt, high-temperature viscosity of modified asphalt, and the problem of limiting the amount of SBS; and realize the environmental protection of the product in terms of technology and equipment , stable, high-performance and low-cost production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-rubber asphalt master batch and low-temperature environmental-friendly production process thereof
  • High-rubber asphalt master batch and low-temperature environmental-friendly production process thereof
  • High-rubber asphalt master batch and low-temperature environmental-friendly production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] (1) Mix 50 parts by mass of 30-mesh 900in tire vulcanized rubber powder and 10 parts by mass of furfural oil in a pre-development tank, and degrade and develop for 5 hours.

[0046] (2) Add 40 parts by mass of Ssangyong 70#A grade matrix asphalt purchased from S-Oil to the pre-development tank pump, and transport the pre-development tank material to the reactor through the screw pump, and pass the model SYJZM02-30 / 0.2 type The homogeneous colloid mill is used for shear blending for 2 hours, and then the mixture is sent to the decay tank for 3-5 days, and the target viscosity at 135°C is 1-2 Pa·s to obtain a high-glue asphalt masterbatch.

[0047] (3) 8 parts by mass of high-glue asphalt masterbatch and 9 parts by mass of star-shaped SBS (mass average molecular weight: 120,000) purchased from Yueyang Petrochemical were blended with 80 parts by mass of road petroleum asphalt through a colloid mill, and the temperature was kept at 160°C Until the SBS is completely swollen....

Embodiment 2

[0050] (1) Mix 10 parts by mass of 100-mesh 1000in tire vulcanized rubber powder and 10 parts by mass of aromatic oil in a pre-development tank, and degrade and develop for 3 hours.

[0051] (2) Add 80 parts by mass of Ssangyong 70#A grade matrix asphalt purchased from S-Oil to the pre-development tank pump, and transport the pre-development tank material to the reactor through the screw pump, and pass the model SYJZM02-30 / 0.2 type The homogeneous colloid mill is used for shear blending for 2 hours, and then the mixture is sent to the decay tank for 3-5 days, and the target viscosity at 135°C is 1-2 Pa·s to obtain a high-glue asphalt masterbatch.

[0052] (3) 32 parts by mass of high-glue asphalt masterbatch and 1 part by mass of star-shaped SBS (mass average molecular weight: 300,000) purchased from Yueyang Petrochemical were blended with 66.8 parts by mass of road petroleum asphalt through a colloid mill, and the temperature was kept at 190°C Until the SBS is completely swol...

Embodiment 3

[0055] (1) Mix 25 parts by mass of 80-mesh 1100in tire vulcanized rubber powder and 5 parts by mass of shale oil in a pre-development tank, and degrade and develop for 3 hours.

[0056] (2) Add 70 parts by mass of Ssangyong 70#A grade matrix asphalt purchased from S-Oil to the pre-development tank pump, and transport the pre-development tank material to the reactor through the screw pump, and pass the model SYJZM02-30 / 0.2 type The homogeneous colloid mill is sheared and blended for 1 hour, and then the mixture is sent to the decay tank for 3-5 days, and the target viscosity at 135°C is 1-2 Pa·s to obtain a high-glue asphalt masterbatch.

[0057] (3) 15 parts by mass of high-adhesive asphalt masterbatch and 5 parts by mass of star-shaped SBS (mass average molecular weight: 300,000) purchased from Yueyang Petrochemical were blended with 78.5 parts by mass of road petroleum asphalt through a colloid mill, and the temperature was kept at 190°C Until the SBS is completely swollen. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-rubber asphalt master batch and a low-temperature environmental-friendly production process thereof. A raw material is prepared from the following ingredients in percentage by weight: 10 to 50 parts of vulcanized rubber powder, 5 to 15 parts of deconstruction agents and 40 to 80 parts of substrate asphalt. The high-rubber asphalt master batch is prepared by the following steps of firstly performing desulfurization degradation on vulcanized rubber powder; then, adding the substrate asphalt; performing blending to obtain a homogeneous blended material. By using the high-rubber asphalt master batch provided by the invention, the problems of great smell, substandard discharge and the like in the subsequent asphalt product production process can be effectively solved; the problem of asphalt and rubber powder performance reduction due to a conventional production method of obtaining the modified asphalt by degrading vulcanized rubber powder into asphalt at thehigh temperature above 200 DEG C through long-time shearing can be solved; the production period is shortened; the cost is reduced; in addition, the original crosslinking macromolecular reticular structure in the vulcanized rubber powder becomes smaller; a small number of chain type materials can be formed; the system sol content is increased; in the subsequent processing process, the substance exchange between the rubber powder and asphalt is facilitated; the compatibility and the stability are improved.

Description

technical field [0001] The invention relates to the field of asphalt material improvement, in particular to a high-glue asphalt masterbatch and a low-temperature environment-friendly production process thereof. Background technique [0002] With the rapid growth of modern traffic flow and the frequent occurrence of extreme climates, higher requirements are put forward for modified asphalt; especially high-grade pavements such as heavy-duty traffic pavement, steel bridge deck pavement and drainage asphalt pavement require the use of high-grade Performance modified bitumen. Among them, adding high content of SBS is an effective way to achieve high performance of modified asphalt, but high content of SBS modified asphalt has problems such as difficult stability, difficult processing and high cost. Rubber asphalt has excellent crack resistance and can reduce the black pollution of waste tires, but the process is complicated, the performance is unstable, and harmful gases will b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L53/02C08L91/00C08L19/00C08K3/14C08K3/06C08K3/04C08J3/22
CPCC08J3/22C08J11/18C08K3/04C08K3/06C08K3/14C08L17/00C08L19/00C08L53/02C08L91/00C08L95/00Y02W30/62
Inventor 徐思田周文彬周文婷王仕峰陶红朱亚琴陈加干
Owner JIANGSU BAOLI INT INVESTMENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com