UV (ultraviolet) optical adhesive

A technology of optical glue and photopolymerization initiator, which is applied in the direction of adhesives, adhesive types, polyurea/polyurethane adhesives, etc., can solve problems such as easy scratches, general adhesion, and poor fluidity during installation, and achieve production The effect of improving efficiency, improving yield rate, and increasing coating speed

Inactive Publication Date: 2019-05-10
苏州宝瑞德纳米光学材料有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The UV optical glue used in the existing microprism anti-glare film UV coating process is mostly a relatively viscous glue with poor fluidity at room temperature. After curing, the adhesion to PET and PC films is average, and the glue is relatively brittle after molding. The tip of the structure is easy to break, and it is easy to cause scratches and other defects when customers install it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • UV (ultraviolet) optical adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] 30 parts by weight of modified polyurethane acrylate resin, 15 parts by weight of modified epoxy acrylate resin, 15 parts by weight of 1,6-hexanediol diacrylate, 20 parts by weight of acrylamide Marlin, 15 parts by weight of OPPEA, 2 parts by weight Parts of 1-hydroxycyclohexyl-phenyl ketone, 2 parts by weight of 2,4,6,-trimethylbenzoyl-diphenylphosphine oxide, and 1 part of adhesion promoter.

Embodiment 2

[0022] 20 parts by weight of modified polyurethane acrylate resin, 20 parts by weight of modified epoxy acrylate resin, 15 parts by weight of 1,6-hexanediol diacrylate, 20 parts by weight of acrylamide Marlin, 20 parts by weight of OPPEA, 2 parts by weight Parts of 1-hydroxycyclohexyl-phenyl ketone, 2 parts by weight of 2,4,6,-trimethylbenzoyl-diphenylphosphine oxide, and 1 part of adhesion promoter.

Embodiment 3

[0024] 20 parts by weight of modified polyurethane acrylate resin, 20 parts by weight of modified epoxy acrylate resin, 15 parts by weight of 1,6-hexanediol diacrylate, 20 parts by weight of acrylamide Marlin, 20 parts by weight of OPPEA, 2 parts by weight Parts of 1-hydroxycyclohexyl-phenyl ketone, 2 parts by weight of 2,4,6,-trimethylbenzoyl-diphenylphosphine oxide, and 0.5 parts of adhesion promoter.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses UV (ultraviolet) optical adhesive, made from, by weight, 30-60 parts of an acrylate oligomer, 30-50 parts of an acrylate monomer, 1-4 parts of a photopolymerization initiator,and 3-5 parts of an adhesion promotion aid. The UV optical adhesive has the advantages that the finished adhesive has reliable indexes, the yield is increased, fewer defects are shown to customers, mobility and curing speed of the adhesive are increased, and coating speed is increased so that production efficiency is improved.

Description

technical field [0001] The invention relates to the field of microprism anti-glare film and plate manufacturing, in particular to UV optical glue used in the microprism anti-glare film UV coating process. Background technique [0002] The UV optical glue used in the existing microprism anti-glare film UV coating process is mostly a relatively viscous glue with poor fluidity at room temperature. After curing, the adhesion to PET and PC films is average, and the glue is relatively brittle after molding. The tip of the structure is easy to break, and it is easy to cause scratches and other defects when customers install it. Contents of the invention [0003] The purpose of the present invention is to provide a UV optical glue, which increases the fluidity and curing speed of the glue, so that the coating speed can be increased, thereby improving the production efficiency. [0004] To achieve the above object, the technical solution of the present invention is [0005] A kin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J175/14C09J163/10C09J11/06
Inventor 周志凯朱方明
Owner 苏州宝瑞德纳米光学材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap