Method for catalyzing glycolide polymerization by binuclear chiral amino imine magnesium complex

A technology of amine imine magnesium and complexes, which is applied in the field of catalytic glycolide polymerization, can solve problems such as metal residues, and achieve the effects of low cost, meeting market demands, and various catalyst structure changes.

Active Publication Date: 2019-04-26
TAISHAN MEDICAL UNIV
View PDF12 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, one problem that still needs to be solved is that there will inevitably be metal residues in the products made by metal complex catalysts, and it is almost impossible to completely remove these residues from the polymer, so low-toxicity magnesium complexes become More promising catalysts, especially when polymers are used in the field of biomedicine, such catalysts are even more important

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for catalyzing glycolide polymerization by binuclear chiral amino imine magnesium complex
  • Method for catalyzing glycolide polymerization by binuclear chiral amino imine magnesium complex
  • Method for catalyzing glycolide polymerization by binuclear chiral amino imine magnesium complex

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The structural formula of the ligand used is the above formula (A), where R is hydrogen, and the reaction process is as follows: under a nitrogen atmosphere, slowly add 5 mL of benzyl alcohol tetrahydrofuran solution (2.0 mol / L) to an equimolar amount of Mg( n Bu) 2 Hexane solution (2.0 mol / L, 5 mL) was reacted for 1 hour, 2.14 g of the ligand was dissolved in 25 mL of dry toluene, and added to Mg( n Bu) 2 In the reaction mixture with benzyl alcohol, after adding, the reaction liquid was naturally raised to room temperature, and then heated to 60 ° C for 3 hours. After the reaction was completed, the solvent was vacuum-dried, and the residue was washed with dry n-hexane, filtered, and then the product was collected and dried. Weighed to obtain 3.05 g of solid, the yield was 83.4%.

Embodiment 2

[0036] The structural formula of the ligand used is the above formula (A), where R is a methyl group, and the reaction process is as follows: under a nitrogen atmosphere, slowly add 5 mL of benzyl alcohol tetrahydrofuran solution (2.0 mol / L) to an equimolar amount of Mg( n Bu) 2 Hexane solution (2.0 mol / L, 5 mL) was reacted for 1 hour, 2.64 g of the ligand was dissolved in 25 mL of dry toluene, and added to Mg( n Bu) 2and benzyl alcohol reaction mixture, after adding, the reaction liquid was naturally raised to room temperature, and then heated to 40 ° C for 10 hours, after the reaction was completed, the solvent was vacuum-dried, and the residue was washed with dry n-hexane, filtered, and then the product was collected and dried Weighed to obtain 3.33 g of solid, the yield was 84.5%.

Embodiment 3

[0038] The structural formula of the ligand used is the above formula (A), where R is ethyl, and the reaction process is as follows: under a nitrogen atmosphere, slowly add 5 mL of benzyl alcohol tetrahydrofuran solution (2.0 mol / L) to an equimolar amount of Mg( n Bu) 2 Hexane solution (2.0 mol / L, 5 mL) was reacted for 1 hour, 2.92 g of the ligand was dissolved in 30 mL of dry toluene, and added to Mg( n Bu) 2 In the reaction mixture with benzyl alcohol, after the addition, the reaction liquid was naturally raised to room temperature, and then heated to 50°C for 6 hours. After the reaction was completed, the solvent was vacuum-dried, and the residue was added to dry n-hexane to filter and washed with dry n-hexane. , the product was collected and dried and weighed to obtain 3.66 g of solid, with a yield of 86.6%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for catalyzing glycolide polymerization by a binuclear chiral amino imine magnesium complex. The method comprises following steps: the binuclear chiral amino imine magnesium complex is taken as a catalyst, glycolide is taken as a raw material, glycolide polymerization is catalyzed under the anhydrous and anaerobic conditions and under protection of gas, and polyglycollide is obtained; the catalyst is the binuclear chiral amino imine magnesium complex. A glycolide ring-opening polymerization is performed by adopting own developed binuclear chiral amino imine magnesium complex as the catalyst, a preparation method of the catalyst is simple, the cost is low, the structure is diversified, metal-center magnesium coordinates with N,N atoms of ligands, catalytic activity is high, a promoter is not needed, the reaction rate is high, and a polymer has narrow molecular weight distribution and controllable molecular weight.

Description

technical field [0001] The invention relates to a method for catalyzing the polymerization of glycolide, in particular to a method for catalyzing the polymerization of glycolide by using a dinuclear chiral amine imine magnesium complex. Background technique [0002] With the enhancement of people's awareness of environmental protection, the development of degradable biomaterials that can reduce environmental pollution has become one of the important research fields of polymer materials. Polylactone is a biodegradable, green and environment-friendly polymer material, and it has attracted more and more attention as a substitute for petroleum products. In the natural living environment, waste polylactone materials can be completely decomposed into small molecules by microorganisms in the soil. Because polyester is non-toxic, non-irritating, and has good biocompatibility, it is widely used in medical and environmental protection fields, such as surgical sutures, packaging, drug...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G63/83C08G63/08
CPCC08G63/08C08G63/823
Inventor 顿爱社张春菊侯海峰王洪宾姚伟张海东于广福孙丰刚
Owner TAISHAN MEDICAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com