A kind of polyamide composite material with good tactility and easy encapsulation and preparation method thereof
A composite material and polyamide technology, applied in the field of polyamide materials, can solve the problems of low efficiency, high cost, large operation workload, etc., and achieve the improvement of surface polarity, good adhesion, and good tear resistance. Effect
Active Publication Date: 2021-04-13
上海日之升科技有限公司
View PDF10 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, such materials are often related to the nylon matrix. Once the matrix of the reinforced nylon product changes, the general production needs to be adapted through the adjustment of the elastomer formula. The operation workload is large, the efficiency is low, and the cost is high.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0033] Put the other components except glass fiber into the high mixer according to the ratio in Table 1, mix for 5-10 minutes, and then discharge to obtain the mixture, and add it from the main feeding port of the twin-screw extruder, and the glass fiber is fed from the side Then control the processing temperature of the twin-screw extruder to 200-260°C, the screw speed to 180-600 rpm, and put the mixture in the twin-screw extruder to extrude and granulate to obtain the product.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Property | Measurement | Unit |
---|---|---|
melting point | aaaaa | aaaaa |
melting point | aaaaa | aaaaa |
Login to view more
Abstract
The invention relates to a polyamide composite material with good touch feeling and easy encapsulation and a preparation method thereof. The material comprises the following components in parts by weight: 25-75 parts of PA6 resin; 15-50 parts of glass fiber; 5-15 parts of styrene copolymer ; 2-8 parts of compatibilizer; 3-10 parts of polar modifier; 0.2-0.5 parts of antioxidant; Graft copolymer; when preparing, weigh other components except glass fiber according to the mass fraction and mix them in a high-speed mixer, then put them into the main feeding port of the twin-screw extruder, and the glass fiber is fed from the side feeding port Add, extrude and granulate. The polyamide composite material with good touch and easy encapsulation obtained in the present invention has the characteristics of good surface touch, wear resistance, easy encapsulation, etc., and can be widely used in fields such as electric tools, sports equipment, electronic appliances and the like that require encapsulation injection molding.
Description
technical field [0001] The invention relates to the technical field of polyamide materials, in particular to a polyamide composite material with good tactility and easy encapsulation and a preparation method thereof. Background technique [0002] Polyamide has ideal chemical resistance, processability and heat resistance, and is the first of the five engineering plastics, among which PA66 and PA6 are the most widely used. Unmodified polyamide has low strength, high water absorption, and poor dimensional stability. Adding a certain amount of inorganic reinforcing materials can significantly improve these properties. The most common is that the addition of glass fiber can significantly improve the mechanical properties of nylon materials. Tools and other engineering components are widely used, but due to their high hardness and rough surface, when they are held and used for a long time, they will cause discomfort due to contact and friction. At present, the more common method ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L77/02C08L25/12C08L87/00C08L51/06C08L51/00C08K9/06C08K7/14
CPCC08L77/02C08L2205/035C08L25/12C08L87/005C08L51/06C08L51/00C08K9/06C08K7/14
Inventor 徐东东张强陈超王刚郭建鹏
Owner 上海日之升科技有限公司
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap