Protective coating applied to surface of solar panel bracket and preparation method thereof

A technology for solar panels and protective coatings, applied in coatings, polyester coatings, epoxy resin coatings, etc., can solve problems such as poor aging resistance, poor acid and alkali resistance, and achieve good acid and alkali resistance, Acid and alkali resistance and anti-aging properties are improved, and the effect of strong acid and alkali resistance

Inactive Publication Date: 2019-03-15
安徽兆拓新能源科技有限公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the acid and alkali resistance is not good, and the aging resistance is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] This embodiment relates to a protective coating applied to the surface of a solar panel support, comprising the following raw materials in parts by weight: 20 parts of thermosetting fluorocarbon resin, 13 parts of glycerol alkyd resin, 17 parts of acrylic resin, and 15 parts of modified epoxy resin , 6 parts of modified sepiolite, 2 parts of nano-titanium dioxide, 1 part of sodium petroleum sulfonate, 2 parts of modified mica powder, 0.3 parts of multi-walled carbon nanotubes, 1 part of antioxidant, 2 parts of light stabilizer and 30 parts of solvent share,

[0036] The preparation method of described modified sepiolite is as follows:

[0037] (1) Mix sepiolite and water and pour it into a hydrothermal kettle, and add a surfactant. Under the conditions of temperature 200°C and pressure 2MPa, heat preservation and pressure stirring reaction, discharge, filter to obtain a filter cake, put The filter cake is mixed with 7% hydrochloric acid, stirred and reacted, and then f...

Embodiment 2

[0053] This embodiment relates to a protective coating applied to the surface of a solar panel support, comprising the following raw materials in parts by weight: 30 parts of thermosetting fluorocarbon resin, 18 parts of glycerol alkyd resin, 26 parts of acrylic resin, and 25 parts of modified epoxy resin , 13 parts of modified sepiolite, 4 parts of nano-titanium dioxide, 3 parts of sodium petroleum sulfonate, 5 parts of modified mica powder, 0.8 parts of multi-walled carbon nanotubes, 2 parts of antioxidant, 4 parts of light stabilizer and 50 parts of solvent share,

[0054] The preparation method of described modified sepiolite is as follows:

[0055] (1) Mix sepiolite and water and pour it into a hydrothermal kettle, and add a surfactant. Under the conditions of temperature 240°C and pressure 5MPa, heat-preserve and pressurize, stir and react, discharge, filter, and obtain a filter cake. The filter cake is mixed with 13% hydrochloric acid by mass fraction, stirred and reac...

Embodiment 3

[0071] This embodiment relates to a protective coating applied to the surface of a solar panel support, comprising the following raw materials in parts by weight: 23 parts of thermosetting fluorocarbon resin, 14 parts of glycerol alkyd resin, 20 parts of acrylic resin, and 18 parts of modified epoxy resin , 7 parts of modified sepiolite, 2.5 parts of nano-titanium dioxide, 1.6 parts of sodium petroleum sulfonate, 3 parts of modified mica powder, 0.4 parts of multi-walled carbon nanotubes, 1.4 parts of antioxidant, 2.8 parts of light stabilizer and 35 parts of solvent share.

[0072] Wherein, the preparation method of described modified sepiolite is as follows:

[0073] (1) Mix sepiolite and water and pour it into a hydrothermal kettle, and add a surfactant. Under the conditions of temperature 220°C and pressure 4MPa, heat preservation and pressure stirring reaction, discharge, filter to obtain a filter cake, put The filter cake is mixed with 10% hydrochloric acid by mass frac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a protective coating applied to the surface of a solar panel bracket. The protective coating applied to the surface of the solar panel bracket is prepared from the following raw materials in parts by weight: 20 to 30 parts of thermosetting fluorocarbon resin, 13 to 18 parts of glycerin alkyd resin, 17 to 26 parts of acrylic resin, 15 to 25 parts of modified epoxy resin, 6 to 13 parts of modified sepiolite, 2 to 4 parts of nano-titania, 1 to 3 parts of petroleum sodium sulphonate, 2 to 5 parts of modified mica powder, 0.3 to 0.8 part of multi-walled carbon nano-tubes, 1to 2 parts of an antioxidant, 2 to 4 parts of a light stabilizer and 30 to 50 parts of a solvent. According to the protective coating applied to the surface of the solar panel bracket provided by theinvention, the prepared coating has good adhesion force, strong acid resistance and alkaline resistance, and excellent anti-aging performance by controlling the types and the proportions of the raw materials.

Description

technical field [0001] The invention belongs to the technical field of solar panel supports, and in particular relates to a protective coating applied on the surface of a solar panel support and a preparation method thereof. Background technique [0002] The solar bracket is mainly used to support and fix the solar panel. Because it is exposed to the outside for a long time, it is necessary to have good corrosion resistance. At the same time, the weather is cold and the temperature is low. Fracture or frostbite or damage to the surface of the stent. [0003] The invention patent of application publication number CN107474671A discloses a coating for solar support, which is formed by spraying the coating on the solar support after stirring evenly, and drying naturally for 90-120 minutes; the coating includes the following raw materials: propylene glycol, ethyl alcohol Glycol, glycerol, modified PTFE emulsion, silicone acrylic emulsion, ethyl acetate, deionized water, leveling...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D127/12C09D167/08C09D133/04C09D163/00C09D7/62C09D7/61
CPCC08K2003/2241C08K2201/011C08L2201/08C08L2203/204C08L2205/035C09D7/61C09D7/62C09D127/12C08L67/08C08L33/04C08L63/00C08K13/06C08K9/02C08K9/04C08K3/34C08K3/041C08K3/22
Inventor 陆志鹏
Owner 安徽兆拓新能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap