Functional ramie fiber fabric and preparation method

A hemp fiber and functional technology, which is applied in the field of functional hemp fiber fabrics and preparations, can solve the problems of unstable fabric functionality, complex production process, and unscientific and reasonable, and achieve good anti-mold and antibacterial properties, unique style, The effect of improving textile performance and wearing performance

Inactive Publication Date: 2019-02-15
东莞青柳新材料有限公司
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in actual production, the fabric structure design and raw material preparation are usually not scientific and reasonable, which makes the production process complicated and inefficient, resulting in unstable or even degraded functionality of the fabric.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] A preparation method of functional hemp fiber fabric comprises the following steps:

[0025] (1) Selection of fabric components: including ramie fiber, polyester fiber, bamboo fiber and colored cotton fiber; the proportion of the fabric component is: 40% of ramie fiber, 20% of polyester fiber, 10% of bamboo fiber and 30% of colored cotton fiber %; the fineness of the fabric components is: ramie fiber 8.8dtex, polyester fiber 1.8dtex, bamboo fiber 2.0dtex and colored cotton fiber 2.2dtex;

[0026] (2) Spinning section process: the spinning section process mainly includes the following procedures: mixing, carding, drawing, roving and spun yarn operations, blending the ramie fiber and polyester fiber into warp yarn, blending bamboo fiber and colored cotton fiber into weft yarn; among them, the cylinder speed of the carding process is 200-220r / min, the licker-in speed is 600-650r / min, the doffer speed is 15r / min, and the cover plate speed is 155-160mm / min; The mode of draf...

Embodiment 1

[0042] The preparation process of the composite polyester fiber of the present invention is as follows:

[0043] S1, 0.7g of CuCl 2 2H 2 O was added to 35mL of N,N-dimethylformamide solution, stirred evenly to obtain solution A; then 0.8g thiourea was added to 35mL of N,N-dimethylformamide solution, stirred evenly to obtain solution B ; then carbon nanotubes, CuO nanoparticles and 1g of polyvinylpyrrolidone were added to solution B, fully stirred to obtain solution C; then solution C was slowly added to solution A, stirred for 60min to obtain solution D, and solution D Put it into a polytetrafluoroethylene reactor, react at 190°C for 2 hours, cool down naturally, and wash the product with deionized water and ethanol to obtain the first powder;

[0044] S2, 0.7g of CuCl 2 2H 2 O was added to 35mL of N,N-dimethylformamide solution, stirred evenly to obtain solution A1; then 0.8g thiourea was added to 35mL of N,N-dimethylformamide solution, stirred evenly to obtain solution B...

Embodiment 2

[0049] The preparation process of the composite polyester fiber of the present invention is as follows:

[0050] S1, 0.7g of CuCl 2 2H 2 O was added to 35mL of N,N-dimethylformamide solution, stirred evenly to obtain solution A; then 0.8g thiourea was added to 35mL of N,N-dimethylformamide solution, stirred evenly to obtain solution B ; then carbon nanotubes, CuO nanoparticles and 1g of polyvinylpyrrolidone were added to solution B, fully stirred to obtain solution C; then solution C was slowly added to solution A, stirred for 60min to obtain solution D, and solution D Put it into a polytetrafluoroethylene reactor, react at 190°C for 2 hours, cool down naturally, and wash the product with deionized water and ethanol to obtain the first powder;

[0051] S2, 0.7g of CuCl 2 2H 2 O was added to 35mL of N,N-dimethylformamide solution, stirred evenly to obtain solution A1; then 0.8g thiourea was added to 35mL of N,N-dimethylformamide solution, stirred evenly to obtain solution B...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a functional ramie fiber fabric and a preparation method. The functional ramie fiber fabric comprises following components including ramie fiber, polyester fibers, natural bamboo fiber and colored cotton fiber, wherein the polyester fibers are sheath-core composite polyester fibers, each sheath-core composite polyester fiber comprises a sheath layer and a core layer, eachcore layer has a circular cross section and is covered with the corresponding sheath layer, each sheath layer comprises PET polyester and first polyester masterbatches, and each core layer comprises PET polyester and second polyester masterbatches; the first polyester masterbatches are obtained by mixing and granulating first powder and polyester slices, and the second polyester masterbatches areobtained by mixing and granulating second powder and the polyester slices.

Description

technical field [0001] The present application relates to the technical field of fabrics, in particular to a functional hemp fiber fabric and a preparation method thereof. Background technique [0002] In modern social life, the role of clothing is far more than cold and warm, but requires multiple functions and performances, especially moisture absorption, breathability, antibacterial, skin-friendly, etc., which can improve people's wear health indicators. [0003] Hemp fiber is a moisturizing fiber taken from plant stems or leaves. It has good strength and is a natural cellulose fiber. It has the advantages of fast moisture absorption and dehumidification, and good air permeability. However, the elongation of the hemp fiber is small, the cohesion force is small, and the stiffness of the fiber is relatively large, so it is difficult to spin, and the short fleece with high rigidity produced by spinning is prone to itching. Due to the limitations of single fabric fibers in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D01D5/34D01F8/14D01F1/10D03D15/217D03D15/283D03D15/37D03D15/47D03D15/50D03D15/54
CPCD01D5/34D01F1/106D01F8/14D03D15/00D10B2501/00D10B2201/08D10B2201/10D10B2201/02D10B2331/04D10B2401/13
Inventor 不公告发明人
Owner 东莞青柳新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com