Ceramic glaze which is easy to clean and is not easy to oil

A ceramic glaze, easy-to-clean technology, applied in the field of ceramic glaze, can solve the problems of difficulty in cleaning, difficult to remove, yellow glaze, etc., and achieves the effect of good easy-to-clean effect, reduced production cost, and broad market prospects.

Active Publication Date: 2019-01-11
景德镇富玉青花玲珑陶瓷有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The smoothness of the glazed surface of the existing ceramic utensils is not very ideal. After a period of use, it will be found that the glazed surface is easily contaminated with dirt, oil stains, etc., and the glazed surface "hides dirt and dirt", and cleaning needs the assistance of detergent ; After using for a long time, you will find that the glaze surface will turn yellow and is not easy to remove, and the glaze surface will also appear dull. At this time, the glaze surface is more likely to be contaminated with dirt and difficult to clean. Therefore, the market urgently needs a low-cost Convenient high-quality easy-to-clean ceramic glaze

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic glaze which is easy to clean and is not easy to oil

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of ceramic glaze that is easy to clean and not easy to be stained with oil, the mass percentage of its raw material composition is:

[0023] Bottom glaze: porcelain stone glaze powder 26%, albite 14%, limestone 3%, wollastonite 6%, Fuzhou kaolin 14%, Sanbaopeng porcelain stone 5%, Qimen porcelain stone 5%, quartz 15%, carbonic acid Magnesium 2%, dolomite 5%, barium carbonate 5%;

[0024] Surface glaze: porcelain stone glaze fruit powder 40%, lithium feldspar 18%, talc 13%, Fuzhou kaolin 6%, Sanbaopeng porcelain stone 6%, Qimen porcelain stone 6%, quartz 5%, zinc oxide 2%, lithium carbonate 2%, 2% dolomite, plus 10% titanium oxide powder.

[0025] The bottom glaze is prepared according to the following procedures: after the bottom glaze raw materials are mixed evenly, put them into a ball mill for ball milling, and pass through a 150-mesh sieve with a sieve residue of 0.2%, and apply it on the surface of the ceramic body according to a thickness of 1.2mm, and the...

Embodiment 2

[0028] A kind of ceramic glaze that is easy to clean and not easy to be stained with oil, the mass percentage of its raw material composition is:

[0029] Bottom glaze: Porcelain powder 33%, albite 12%, limestone 4%, wollastonite 8%, Fuzhou kaolin 10%, Sanbaopeng porcelain stone 8%, Qimen porcelain stone 7%, quartz 10%, carbonic acid Magnesium 4%, dolomite 2%, barium carbonate 2%;

[0030] Surface glaze: porcelain stone glaze fruit powder 31%, lithium feldspar 15%, talc 6%, Fuzhou kaolin 7%, Sanbaopeng porcelain stone 8%, Qimen porcelain stone 8%, quartz 7%, zinc oxide 4%, lithium carbonate 8%, 6% dolomite, plus 12% titanium oxide powder.

[0031] The bottom glaze is prepared according to the following procedures: after the bottom glaze raw materials are mixed evenly, put them into a ball mill for ball milling, and pass through a 150-mesh sieve with a sieve residue of 0.2%, and apply it on the surface of the ceramic body according to a thickness of 1.2mm, and then Carry out ...

Embodiment 3

[0034] A kind of ceramic glaze that is easy to clean and not easy to be stained with oil, the mass percentage of its raw material composition is:

[0035] Bottom glaze: porcelain stone glaze powder 30%, albite 10%, limestone 5%, wollastonite 5%, Fuzhou kaolin 11%, Sanbaopeng porcelain stone 6%, Qimen porcelain stone 10%, quartz 12%, carbonic acid Magnesium 4%, dolomite 4%, barium carbonate 3%;

[0036] Surface glaze: porcelain stone glaze fruit powder 34%, lithium feldspar 10%, talc 9%, Fuzhou kaolin 6%, Sanbaopeng porcelain stone 10%, Qimen porcelain stone 9%, quartz 9%, zinc oxide 4%, lithium carbonate 5%, dolomite 4%, plus 15% titanium oxide powder.

[0037] The bottom glaze is prepared according to the following procedures: after the bottom glaze raw materials are mixed evenly, put them into a ball mill for ball milling, and pass through a 150-mesh sieve with a sieve residue of 0.2%, and apply it on the surface of the ceramic body according to a thickness of 1.2mm, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses ceramic glaze which is easy to clean and is not easy to oil. The ceramic glaze comprises, by mass, bottom glaze: 25-35% of porcelain glaze stone powder, 10-15% of albite, 3-6%of limestone, 5-10% of wollastonite, 10-15% of Fuzhou kaolin, 5-10% of Sanbaopeng porcelain stone, 5-10% of Qimen porcelain stone, 10-15% of quartz, 2-6% of magnesium carbonate, 2-6% of dolomite and 2-6% of barium carbonate, and overglaze: 30-40% of porcelain glaze stone powder, 10-18% of lithium feldspar, 5-15% of talc, 6-8% of Fuzhou kaolin, 6-12% of Sanbaopeng porcelain stone, 6-10% of Qimen porcelain stone, 5-10% of quartz, 2-6% of zinc oxide, 2-8% of lithium carbonate, 2-6% of dolomite and 10-15% of additive titanium oxide powder. Through bottom glaze and surface glaze preparation, bottomglaze application, primary high temperature glaze burning, surface glaze application and secondary high temperature glaze burning, the product is obtained. The ceramic glaze product has a good glazesurface, good cleanability, a low production cost and broad market prospects.

Description

technical field [0001] The invention belongs to the field of inorganic non-metallic materials (ceramics), and in particular relates to a ceramic glaze which is easy to clean and not easy to be stained with oil. Background technique [0002] With the development of society, the improvement of people's living conditions, people's pursuit of beauty and higher requirements for healthy life, hotels, hotels and families have higher and higher requirements for sanitary ceramics. The smoothness of the glazed surface of the existing ceramic utensils is not very ideal. After a period of use, it will be found that the glazed surface is easily contaminated with dirt, oil stains, etc., and the glazed surface "hides dirt and dirt", and cleaning needs the assistance of detergent ; After using for a long time, you will find that the glaze surface will turn yellow and is not easy to remove, and the glaze surface will also appear dull. At this time, the glaze surface is more likely to be cont...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/00C04B41/89
CPCC03C8/00C04B41/52C04B41/89C04B41/5022C04B41/4539
Inventor 吕雅婷
Owner 景德镇富玉青花玲珑陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap