Modified plastic particles with stable mechanical properties and preparation process

A technology of mechanical properties and plastic particles, applied in the field of modified plastic particles and preparation technology, can solve the problems of reduced wear resistance, easy aging of epoxy plastics, affecting the use of epoxy plastic products, etc., and achieves long service life and good quality. Promote the application value and market competitiveness, and the effect of good overall quality

Inactive Publication Date: 2019-01-08
界首市鑫豪塑胶有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although epoxy plastics have the advantages of strong adhesion, good chemical stability, and good mold resistance, but with the continuous improvement of design and use requirements, the existing commercially available epoxy plastics can n

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A plastic granule with stable mechanical properties, made of the following substances in parts by weight:

[0024] 110 parts of epoxy resin, 23 parts of butyl benzyl phthalate, 10 parts of lanthanum sulfate, 8 parts of samarium phosphate, 12 parts of tributyl phosphate, 7 parts of stearic acid, 9 parts of higher alcohol fatty acid ester complex, 28 parts of modified fillers.

[0025] Further, the preparation method of the modified filler includes the following operations:

[0026] a. Weigh 8 parts of corn straw, 5 parts of rape straw, 9 parts of rice straw, 2 parts of 2,4-dichlorophenoxyacetic acid, 4 parts of silicon dioxide, and 0.6 parts of carbendazim in high pressure In the tank, raise the temperature in the high-pressure tank to 102°C, the pressure to 0.23 MPa, and control the relative humidity to 85%. After maintaining the pressure for 2 minutes, quickly release the pressure to constant temperature and pressure, and then take out the mixture A for later use;

...

Embodiment 2

[0036] A plastic granule with stable mechanical properties, made of the following substances in parts by weight:

[0037] 115 parts of epoxy resin, 24 parts of butyl benzyl phthalate, 12 parts of lanthanum sulfate, 9 parts of samarium phosphate, 13 parts of tributyl phosphate, 8 parts of stearic acid, 10 parts of higher alcohol fatty acid ester complex, 29 parts of modified fillers.

[0038] Further, the preparation method of the modified filler includes the following operations:

[0039] a. Weigh 9 parts of corn stalks, 7 parts of rape stalks, 10 parts of rice straws, 2.5 parts of 2,4-dichlorophenoxyacetic acid, 4.5 parts of silicon dioxide, and 0.7 parts of carbendazim and put them under high pressure In the tank, raise the temperature in the high-pressure tank to 104°C, the pressure to 0.25 MPa, and control the relative humidity to 87%. After maintaining the pressure for 2-3 minutes, quickly release the pressure to constant temperature and pressure, and then take out the m...

Embodiment 3

[0049] A plastic granule with stable mechanical properties, made of the following substances in parts by weight:

[0050] 120 parts of epoxy resin, 25 parts of butyl benzyl phthalate, 14 parts of lanthanum sulfate, 10 parts of samarium phosphate, 14 parts of tributyl phosphate, 9 parts of stearic acid, 11 parts of higher alcohol fatty acid ester complex, 30 parts of modified fillers.

[0051] Further, the preparation method of the modified filler includes the following operations:

[0052] a. Weigh 10 parts of corn straw, 9 parts of rape straw, 11 parts of rice straw, 3 parts of 2,4-dichlorophenoxyacetic acid, 5 parts of silicon dioxide, and 0.8 parts of carbendazim in high pressure In the tank, raise the temperature in the high-pressure tank to 106°C, the pressure to 0.27MPa, and control the relative humidity to 89%. After maintaining the pressure for 3 minutes, quickly release the pressure to constant temperature and pressure, and then take out the mixture A for use;

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses modified plastic particles with stable mechanical properties. The plastic particles are prepared from the following substances: epoxy resin, butyl benzyl phthalate, lanthanum sulfate, samarium phosphate, tributyl phosphate, stearic acid, higher alcohol fatty acid ester compound and modified filler. Components of existing plastic particles are specially improved, and finallythe prepared plastic particles have stable performance, good wear resistance, corrosion resistance and tensile resistance, excellent comprehensive quality, long service life, and good popularizationand application value and market competitiveness.

Description

technical field [0001] The invention belongs to the technical field of plastic processing, and in particular relates to a modified plastic particle with stable mechanical properties and a preparation process. Background technique [0002] Plastic has the characteristics of light weight, no rust, good insulation and so on, so it is widely used in daily life. Epoxy plastic is a plastic based on epoxy resin. The molecular structure of epoxy resin is characterized by the active epoxy group in the molecular chain. The epoxy group can be located at the end, middle or part of the molecular chain. ring structure. Due to the active epoxy groups in the molecular structure, they can cross-link with various types of curing agents to form insoluble. A non-melting high polymer with a three-way network structure. Epoxy plastic is used for some computer keyboards and the bottom of toy cars. Although epoxy plastics have the advantages of strong adhesion, good chemical stability, and good...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L63/00C08L97/02C08K13/06C08K9/00C08K9/06C08K9/04C08K3/22C08K3/26C08K3/34C08K3/36C08K5/12C08K3/30C08K5/521C08K5/09C08K3/32
CPCC08K2003/2296C08K2003/265C08K2003/321C08L63/00C08L2201/02C08L2201/08C08L2205/025C08L2205/035C08L97/02C08K13/06C08K9/00C08K9/06C08K9/08C08K9/04C08K3/22C08K3/26C08K3/346C08K3/36C08K5/12C08K3/30C08K5/521C08K5/09C08K3/32
Inventor 肖殿业杨本宏饶保东
Owner 界首市鑫豪塑胶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap