High-performance flame-retardation material

A flame-retardant material and high-performance technology, applied in the field of flame-retardant materials, can solve the problems of the decline of mechanical properties of flame-retardant composite parts, poor adhesion between flame-retardant fillers and matrix resin, and uneven distribution of flame-retardant fillers. High output, large flame retardant range, good flame retardant effect

Inactive Publication Date: 2019-01-01
黄冈昌耀电力器材有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The problems of the above composite methods mainly include: 1. the distribution of flame retardant fillers in the product is often uneven, so that the flame retardant performance of the finished product is inconsistent; 2. the adhesion between the flame retardant filler and the matrix resin is generally weak Poor, especially when the flame retardant filler content is high
However, if the bonding between the flame retardant filler and the matrix resin is not good, the mechanical properties of the molded flame retardant composite parts will be greatly reduced.
High filling levels also lead to environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A high-performance flame-retardant material, its formula is as follows:

[0036] 11 parts of silicone resin, 10 parts of polyurethane resin, 2 parts of initiator, 3 parts of inorganic flame retardant, 2 parts of organic flame retardant, 20 parts of solvent.

[0037] The silicone resin is polymethyl silicone resin.

[0038] The polyurethane resin adopts water-based polyurethane resin.

[0039] The initiator adopts methyl ethyl ketone peroxide.

[0040] The inorganic flame retardant uses composite phosphorus / magnesium.

[0041] The organic flame retardant uses ammonium polyphosphate.

[0042] The solvent is an aqueous alcohol solution, and the alcohol content in the aqueous alcohol solution is 50%.

[0043] A method for preparing a high-performance flame-retardant material, the steps of which are as follows:

[0044] Step 1, adding silicone resin and polyurethane resin to 80% solvent and stirring evenly;

[0045] In step 2, the initiator is added to the solvent in s...

Embodiment 2

[0054] A high-performance flame-retardant material, its formula is as follows:

[0055] 15 parts of silicone resin, 13 parts of polyurethane resin, 4 parts of initiator, 7 parts of inorganic flame retardant, 5 parts of organic flame retardant, 25 parts of solvent.

[0056] The silicone resin adopts polyethyl silicone resin.

[0057] The polyurethane resin adopts water-based polyurethane resin.

[0058] The initiator adopts cyclohexanone peroxide.

[0059] The inorganic flame retardant uses composite phosphorus / aluminum.

[0060] The organic flame retardant uses pentaerythritol.

[0061] The solvent is an aqueous alcohol solution, and the alcohol content in the aqueous alcohol solution is 80%.

[0062] A method for preparing a high-performance flame-retardant material, the steps of which are as follows:

[0063] Step 1, adding silicone resin and polyurethane resin to 80% solvent and stirring evenly;

[0064] In step 2, the initiator is added to the solvent in step 1, and ...

Embodiment 3

[0073] A high-performance flame-retardant material, its formula is as follows:

[0074] 14 parts of silicone resin, 12 parts of polyurethane resin, 3 parts of initiator, 6 parts of inorganic flame retardant, 4 parts of organic flame retardant, 23 parts of solvent.

[0075] The silicone resin is polymethyl silicone resin.

[0076] The polyurethane resin adopts water-based polyurethane resin.

[0077] The initiator adopts methyl ethyl ketone peroxide.

[0078] The inorganic flame retardant uses composite phosphorus / graphite.

[0079] The organic flame retardant is triphenyl phosphate.

[0080] The solvent is an aqueous alcohol solution, and the alcohol content in the aqueous alcohol solution is 75%.

[0081] A method for preparing a high-performance flame-retardant material, the steps of which are as follows:

[0082] Step 1, adding silicone resin and polyurethane resin to 80% solvent and stirring evenly;

[0083] In step 2, the initiator is added to the solvent in step 1,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-performance flame-retardation material. The high-performance flame-retardation material comprises 11 to 15 parts of silicone resin, 10 to 13 parts of polyurethane resin,2 to 4 parts of an initiator, 3 to 7 parts of an inorganic flame retardant, 2 to 5 parts of an organic flame retardant, and 20 to 25 parts of a solvent. The high-performance flame-retardation material has good processing performance and mechanical property, good flame retarding effect, and large flame retardant range.

Description

technical field [0001] The invention belongs to the technical field of flame-retardant materials, and in particular relates to a high-performance flame-retardant material. Background technique [0002] Composite flame retardant polymer material refers to a multi-phase composite material with flame retardant function composed of polymers and various flame retardants through different composite processes. It not only has flame retardant function, but also has the properties of polymer materials Superiority. Compared with general-purpose flame-retardant polymer materials, it has the characteristics of less flame retardant, stable and durable flame-retardant performance, better process control, easy industrial continuous production, non-toxic and non-corrosive, and low manufacturing cost. , electrical, communications, coal mines, oil fields, construction, entertainment and other industries have a wide range of application prospects. Various flame retardant fillers include: amm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L83/04C08L75/04C08K3/32C08K5/053C08K5/523
CPCC08L83/04C08K2003/323C08L2201/02C08L75/04C08K3/32C08K5/053C08K5/523
Inventor 黄青华
Owner 黄冈昌耀电力器材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com