A kind of finishing method of machine-washable wool fabric

A technology for washing wool and fabrics, applied in the finishing field of machine-washable wool fabrics, can solve the problems of reducing the unidirectional movement and entanglement of fibers, damage to the mechanical properties of wool fabrics, damage to the structure of wool scales, etc. Weak, easy-to-operate effect

Active Publication Date: 2020-10-30
ZHONGYUAN ENGINEERING COLLEGE
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are two main methods of anti-felting finishing technology: one is the oxidation method, which mainly damages the structure of wool scales, reduces its directional friction effect, and reduces the one-way movement and entanglement ability of fibers. This method is easy to affect the mechanical properties of wool fabrics Damage, affecting the performance of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of finishing method of machine-washable wool fabric
  • A kind of finishing method of machine-washable wool fabric
  • A kind of finishing method of machine-washable wool fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A finishing method of "machine washable" woolen fabric, the steps are as follows:

[0021] a. Wool fabric preparation: Wash the wool fabric and then dry it at 20°C.

[0022] b. Weight reduction pretreatment: soak the washed woolen fabric in a solution of 30% hydrogen peroxide (3g / L) and sodium silicate (1g / L) for 30min at a bath ratio of 1:30 at a temperature of 40°C; After washing, the wool fabric was treated in a solution of 1% (o.w.f) acetic acid and 2% (o.w.f) sodium bisulfite for 20 min at a temperature of 40°C and a bath ratio of 1:30.

[0023] c. Restorative increase treatment: soak the wool fabric after weight reduction treatment in 1% keratin solution at a bath ratio of 1:30, and treat for 45 minutes at a temperature of 50°C.

[0024] d. Preparation of 1% keratin solution: Dissolve wool in an aqueous solution containing 3% sodium sulfide, 7mol / L urea and 1% SDS at a bath ratio of 1:20, react at 50°C for 10 hours, and measure It is obtained by filtering throug...

Embodiment 2

[0029] A finishing method of "machine washable" woolen fabric, the steps are as follows:

[0030] a. Wool fabric preparation: Wash the wool fabric and then dry it at 20°C.

[0031] b. Weight reduction pretreatment: soak the washed woolen fabric in a solution of 30% hydrogen peroxide (3g / L) and sodium silicate (1g / L) for 30min at a bath ratio of 1:30 at a temperature of 40°C; After washing, the wool fabric was treated in a solution of 1% (o.w.f) acetic acid and 2% (o.w.f) sodium bisulfite for 20 min at a temperature of 40°C and a bath ratio of 1:30.

[0032] c. Restorative increase treatment: soak the wool fabric after weight reduction treatment in 2% keratin solution at a bath ratio of 1:30, and treat for 45 minutes at a temperature of 50°C.

[0033] d. Preparation of 2% keratin solution: Dissolve wool in an aqueous solution containing 3% sodium sulfide, 7mol / L urea and 1% SDS at a bath ratio of 1:20, react at 50°C for 10 hours, and measure It is obtained by filtering throug...

Embodiment 3

[0038] A finishing method of "machine washable" woolen fabric, the steps are as follows:

[0039] a. Wool fabric preparation: Wash the wool fabric and then dry it at 20°C.

[0040] b. Weight reduction pretreatment: soak the washed woolen fabric in a solution of 30% hydrogen peroxide (3g / L) and sodium silicate (1g / L) for 30min at a bath ratio of 1:30 at a temperature of 40°C; After washing, the wool fabric was treated in a solution of 1% (o.w.f) acetic acid and 2% (o.w.f) sodium bisulfite for 20 min at a temperature of 40°C and a bath ratio of 1:30.

[0041] c. Restorative increase treatment: soak the wool fabric after weight reduction treatment in 3% keratin solution at a bath ratio of 1:30, and treat for 45 minutes at a temperature of 50°C.

[0042] d. Preparation of 3% keratin solution: Dissolve wool in an aqueous solution containing 3% sodium sulfide, 7mol / L urea and 1% SDS at a bath ratio of 1:20, react at 50°C for 10 hours, and measure by mesh It is obtained by filterin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for finishing machine washable wool fabrics. The method comprises the following steps: performing reduced pretreatment on wool fabrics by adopting an oxidizing agent todamage the scale layer of wool fibers to a certain degree, so that the orientation friction effect of the wool fibers is further reduced, and the felting shrinkage of the fabrics is reduced; performing repair incremental treatment with a keratin solution under a certain conditions, and forming a coating effect on the surface of the wool fibers, so that the apparent structure of the wool fibers isfurther smoothened, the differential friction phenomenon is improved, and the felting shrinkage of the product is reduced; drying to obtain the wool fabric, wherein the felting shrinkage is less than5%, and the 'machine washable' standard can be reached. The wool fabric finished by the technology is small in mechanical property damage, is weak in influence of performances such as hand feeling, moisture permeation, breathability and the like, and has wide application value.

Description

technical field [0001] The invention relates to the technical field of textile functional finishing, in particular to a finishing method for machine-washable wool fabrics. Background technique [0002] Wool fabric is repeatedly extruded by mechanical external force under the action of damp heat and chemical reagents, and the fiber aggregate gradually shrinks and interpenetrates and entangles with each other to become felted, which is called fluffing. Flocking gives wool fabrics excellent warmth retention, bulkiness, and elasticity, and at the same time, it is easy to cause wool fabrics to shrink during washing, which in turn affects their wearing performance. How to keep woolen fabrics with excellent properties without feeling shrunk during washing (i.e. "shrinkproof finishing of woolen fabrics") has become a hotspot in the wool spinning industry. [0003] At present, there are two main methods of anti-felting finishing technology: one is the oxidation method, which mainly ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M11/50D06M11/79D06M11/54D06M13/188D06M15/15D06M11/53D06M13/432D06M101/12
CPCD06M11/50D06M11/53D06M11/54D06M11/79D06M13/188D06M13/432D06M15/15D06M2101/12D06M2200/45D06M2200/50
Inventor 刘让同李亮刘淑萍李淑静
Owner ZHONGYUAN ENGINEERING COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com