A kind of polymer hydrogel fire extinguishing agent

A technology of polymer hydrogel and fire extinguishing agent, which is applied in the direction of fire prevention equipment, etc., can solve the problem that the fire extinguishing performance cannot be further improved, and achieve the effects of improving fire extinguishing performance, good flame retardant performance, and improved flame retardant performance

Active Publication Date: 2021-10-26
山东水击环保科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem mainly solved by the present invention is: aiming at the shortcomings that the fire extinguishing performance of the traditional polymer hydrogel fire extinguishing agent cannot be further improved, a polymer hydrogel fire extinguishing agent is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polymer hydrogel fire extinguishing agent

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0033]Put sodium alginate and water in a No. 1 beaker at a mass ratio of 1:95, stir with a glass rod for 30 minutes, and let it swell for 5 hours. ℃, the rotation speed is 500r / min, heat and stir to dissolve for 60min to obtain sodium alginate solution; put chitosan and water in a No. 2 beaker with a mass ratio of 1:100, stir and mix with a glass rod for 20min, Let stand to swell for 4 hours, then add chitosan enzyme with 0.08 times the mass of chitosan, and place the No. After stirring the enzymolysis for 5 hours, raise the temperature to 95°C, keep warm for 15 minutes to inactivate the enzyme, and wait for natural cooling to room temperature to obtain the modified chitosan liquid; place the aluminum nitride whiskers in a ball mill for ball milling, and pass through a 100-mesh sieve to obtain a refined chitosan solution. Aluminum nitride whiskers, put aluminum nitride whiskers and paraffin wax in a ball mill at a mass ratio of 1:10, mix and ball mill them, and pass through a ...

example 2

[0035] Put sodium alginate and water in a No. 1 beaker at a mass ratio of 1:95, stir with a glass rod for 30 minutes, and let it swell for 5 hours. ℃, the rotation speed is 500r / min, heat and stir to dissolve for 60min to obtain sodium alginate solution; put chitosan and water in a No. 2 beaker with a mass ratio of 1:100, stir and mix with a glass rod for 20min, Let stand to swell for 4 hours, then add chitosan enzyme with 0.08 times the mass of chitosan, and place the No. After stirring the enzymolysis for 5 hours, raise the temperature to 95°C, keep warm for 15 minutes to inactivate the enzyme, and wait for natural cooling to room temperature to obtain the modified chitosan liquid; place the aluminum nitride whiskers in a ball mill for ball milling, and pass through a 100-mesh sieve to obtain a refined chitosan solution. Aluminum nitride whiskers, put aluminum nitride whiskers and paraffin wax in a ball mill at a mass ratio of 1:10, mix and ball mill them, and pass through a...

example 3

[0037] Put sodium alginate and water in a No. 1 beaker at a mass ratio of 1:95, stir with a glass rod for 30 minutes, and let it swell for 5 hours. ℃, the rotation speed is 500r / min, heat and stir to dissolve for 60min to obtain sodium alginate solution; put chitosan and water in a No. 2 beaker with a mass ratio of 1:100, stir and mix with a glass rod for 20min, Let stand to swell for 4 hours, then add chitosan enzyme with 0.08 times the mass of chitosan, and place the No. After stirring the enzymolysis for 5 hours, raise the temperature to 95°C, keep warm for 15 minutes to inactivate the enzyme, and wait for natural cooling to room temperature to obtain the modified chitosan liquid; place the aluminum nitride whiskers in a ball mill for ball milling, and pass through a 100-mesh sieve to obtain a refined chitosan solution. Aluminum nitride whiskers, put aluminum nitride whiskers and paraffin wax in a ball mill at a mass ratio of 1:10, mix and ball mill them, and pass through a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polymer hydrogel fire extinguishing agent, which belongs to the technical field of fire safety. According to parts by weight, the present invention comprises 20-30 parts of modified chitosan liquid, 10-20 parts of starch, 10-20 parts of bacterial cellulose, 8-10 parts of sodium bicarbonate, 8-10 parts of carbomer, 10-20 parts of water, 8-10 parts of konjac mannose, 8-10 parts of pretreated aluminum nitride whiskers, 8-10 parts of phospholipids, 8-10 parts of protein powder and 8-10 parts of modified gelatin powder Stir and mix for 30-50 minutes in a mixer at a rotational speed of 600-800 r / min to obtain a polymer hydrogel fire extinguishing agent. The polymer hydrogel fire extinguishing agent provided by the invention has excellent fire extinguishing performance.

Description

technical field [0001] The invention discloses a polymer hydrogel fire extinguishing agent, which belongs to the technical field of fire safety. Background technique [0002] Generally speaking, foam fire extinguishing agents and dry powder fire extinguishing agents are mainly used in simple fire extinguishers such as public places, laboratories, factories, etc., to quickly extinguish the fire source at the initial stage of the fire to prevent further expansion of the fire. However, in large-scale fires, most of them use clear water as the fire extinguishing agent; for some airtight environments such as ships and airplanes that cannot be evacuated, water mist fire fighting systems and Halons (Halons) fire fighting systems are generally used to extinguish fires. And other fire extinguishing agents often have some toxicity, even high toxicity and have been greatly restricted. [0003] Water fire extinguishing is an ancient and widely used natural fire extinguishing agent, whi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A62D1/00A62D1/06
CPCA62D1/0064A62D1/06
Inventor 何治伟兰梅菊
Owner 山东水击环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com