Fireproof wear-resistant environment-friendly material and preparation method thereof

An environmentally friendly material and thermoplastic technology, applied in the field of fire-resistant and wear-resistant environmental protection materials and their preparation, can solve the problems of poor flame retardant performance, perishable, expansion deformation, etc., and achieve improved mechanical stability, high production stability, and arbitrary color. The effect of adjustment

Inactive Publication Date: 2018-12-11
徐州涌新环保科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the problems of wood-plastic composite materials or other wood-plastic foam products are easy to rot and expand and deform after absorbing water and damp in humid and wet environments have become increasingly prominent; however, poor flame retardancy in high-temperature and dry environments is even more serious. Hidden danger

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A fireproof and wear-resistant environment-friendly material, comprising: 20% polypropylene; 40% calcium carbonate; 15% flame-retardant polyether; 10% sodium carbonate; 4% epoxy soybean oil; cyclic acid anhydride (MAH ) compounds 4%; zinc stearate 5%; calcium zinc stabilizer 2%.

[0024] A kind of preparation method of fireproof wear-resisting environmental protection material, comprises the steps: with polypropylene 20%; Calcium carbonate 40%; Flame-retardant polyether 15%; Sodium carbonate 10%; Epoxy soybean oil 4%; 4% compound; 5% zinc stearate; 2% calcium zinc stabilizer, mixed at 600 rpm, heated and stirred, cooled the mixture, and then plasticized the cooled mixture by plasticizing granulation process Granulating, and cutting the plasticized granulation into particles by cutting process, the diameter of the cut particles is 2mm, extruding the particles through extrusion process, cooling and forming.

Embodiment 2

[0026] A fireproof and wear-resistant environment-friendly material, comprising: 25% polyethylene; 35% calcium carbonate; 14% flame-retardant polyether; 9% sodium carbonate; 5% epoxy soybean oil; cyclic anhydride (MAH ) compounds 5%; zinc stearate 5%; calcium zinc stabilizer 2%.

[0027] A kind of preparation method of fireproof wear-resisting environmental protection material, comprises the steps: polyethylene 25%; Calcium carbonate 35%; Flame retardant polyether 14%; Sodium carbonate 9%; Epoxy soybean oil 5%; 5% of analogue compound; 5% of zinc stearate; 2% of calcium zinc stabilizer, mixed at 650 rpm, heated and stirred, cooled the mixture, and then plasticized the cooled mixture by plasticizing granulation process Granulating, and cutting the plasticized granulation into particles by cutting process, the diameter of the cut particles is 4mm, extruding the particles through extrusion process, cooling and forming.

Embodiment 3

[0029] A fireproof and wear-resistant environmental protection material, comprising: 20% polypropylene; 50% calcium carbonate; 15% flame retardant polyether; 8% sodium carbonate; 2% epoxy soybean oil; cyclic acid anhydride (MAH ) compounds 2%; zinc stearate 2%; calcium zinc stabilizer 1%.

[0030] A kind of preparation method of fireproof wear-resisting environmental protection material, comprises the steps: with polypropylene 20%; Calcium carbonate 50%; Flame-retardant polyether 15%; Sodium carbonate 8%; Epoxy soybean oil 2%; 2% of analogue compound; 2% of zinc stearate; 1% of calcium zinc stabilizer, mixed at 700 rpm, heated and stirred, cooled the mixture, and then plasticized the cooled mixture by plasticizing granulation process Granulating, and cutting the plasticized granulation into particles by cutting process, the diameter of the cut particles is 6mm, extruding the particles through extrusion process, cooling and forming.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a fireproof wear-resistant environment-friendly material and a preparation method thereof, and belongs to the technical field of novel environment-friendly materials. The preparation method comprises the following steps: mixing 20 to 30 percent of thermoplastic, 30 to 60 percent of calcium carbonate, 10 to 15 percent of flame retarding polyether, 5 to 10 percent of sodium carbonate, 2 to 5 parts of a plasticizer, 1 to 5 parts of a compatibilizer, 1 to 5 percent of a lubricant and 1 to 5 percent of a stabilizer, heating and stirring, and cooling the mixture; plasticizingand pelletizing the cooled mixture with a plasticizing-pelletizing process; cutting the plasticized particles into particles with a cutting process; extruding the particles with an extrusion process;cooling and molding. The environment-friendly material has the advantages of higher fire resistance, higher wear resistance, high production stability, optional adjustment of color, high product attractiveness, no pollution, environmental friendliness, energy conservation, resource recycling and the like. By adopting the method, the mechanical stability, size accuracy and machining speed of the environment-friendly material can be improved effectively.

Description

technical field [0001] The invention relates to the technical field of environmentally friendly new materials, in particular to a fireproof, wear-resistant and environmentally friendly material and a preparation method thereof. Background technique [0002] At present, the problems of wood-plastic composite materials or other wood-plastic foam products are easy to rot and expand and deform after absorbing water and damp in humid and wet environments have become increasingly prominent; however, poor flame retardancy in high-temperature and dry environments is even more serious. Hidden danger. In public places with a large flow of people, the requirements for wear resistance are extremely high. The new composite environmental protection material of the present invention can effectively solve the problems of fire prevention and wear resistance. That is to say, whether it is a composite profile of wood-plastic or other materials, as long as the product is made of thermoplastic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/06C08L71/00C08L91/00C08K13/02C08K3/26C08K5/098
CPCC08K2003/262C08K2003/265C08L23/06C08L23/12C08L2201/02C08L2205/03C08L71/00C08L91/00C08K13/02C08K3/26C08K5/098
Inventor 李庆龙
Owner 徐州涌新环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com