Toilet manufacturing process

A manufacturing process and toilet technology, applied in the field of sanitary ware, can solve the problems of unavoidable leftover materials, waste of natural resources, high processing costs, etc., and achieve the effects of improving production economic benefits, high product density, and high product quality

Inactive Publication Date: 2018-11-06
安徽雅诺卫浴科技有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Marble stone will inevitably produce scraps during the cutting process. These scraps are rarely processed and utilized, some are directly transported out as garbage, and some are used as roadbed fillers, etc., resulting in a large waste of materials and high processing costs; As a non-renewable natural resource, marble should be fully utilized, and waste will be irresponsible for natural resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Toilet manufacturing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A manufacturing process for a toilet, prepared through the following steps:

[0031] S1: According to the shape and size of the toilet seat, liner and base, make a toilet seat FRP mold, liner FRP mold and base wooden mold, and make artificial stone toilet seat, artificial stone liner and PVC base according to the mold;

[0032] S2: Connect the seat ring of the toilet seat with the inner tank by casting, and connect the water channel of the toilet seat to the water tank with the inner tank;

[0033] S3: After connecting the base with the toilet seat, connect the sewer pipe with the drain hole of the liner, then seal the lower opening of the base through the PVC plate, and make the sewer pipe pass through the PVC plate at the bottom of the base;

[0034] S4: After assembling the flush assembly in the water tank of the toilet seat, assemble the water tank cover on the water tank, and then hinge the seat cover and the seat of the toilet seat;

[0035] Wherein, the manufact...

Embodiment 2

[0049] The content of embodiment 2 is basically the same as the content of embodiment 1, and the same part will not be repeated. The difference is: by weight, unsaturated epoxy resin is added to account for 2% of unsaturated epoxy resin in plasticizing agent, specifically the plasticizer is selected from phthalate esters, which account for 0.2% of the anti-aging agent of unsaturated epoxy resin, and the anti-aging agent is a derivative of tetramethyl and pentamethyl, stirring evenly, The stirring speed is 85 rev / min, then add the luminescent filler and modified water-based polyurethane accounting for 60% of the unsaturated epoxy resin, and the crosslinking agent accounting for 1.5% of the unsaturated epoxy resin, the crosslinking agent is ethylene The base derivative was continuously stirred at a stirring speed of 110 rpm and a stirring time of 120 minutes to obtain the filler.

Embodiment 3

[0051] The contents of this embodiment and Example 1 are basically the same, the difference is that by weight ratio, 30% of the unsaturated epoxy resin is added with a plasticizer accounting for 3% of the unsaturated epoxy resin, and the specifically described plasticizer is selected Phthalic acid ester compound accounts for 0.4% antiaging agent of unsaturated epoxy resin, and described antiaging agent is the derivative of tetramethyl and pentamethyl, stirs evenly, and stirring speed is 90 revs / min, then Add 80% of unsaturated epoxy resin luminous filler and modified water-based polyurethane, and 1.9% of unsaturated epoxy resin cross-linking agent, the cross-linking agent is a vinyl derivative of benzene, continuous stirring, stirring speed The stirring time is 120 rev / min and the stirring time is 120 minutes to obtain the filling material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of sanitary appliances and in particular relates to a toilet manufacturing process. The process comprises the following steps: S1, making a toilet seat glass fiber reinforced plastic mold, a liner glass fiber reinforced plastic mold and a wooden base mold according to the shape and size of the toilet seat, a liner and a base, and making an artificial stone toilet seat, an artificial stone liner and a PVC (Polyvinyl Chloride) base according to the molds; S2, connecting the seat ring of the toilet seat and the liner in a casting manner. Thus, the toilet prepared by utilizing a filling material provided by the invention has high glossiness, moisture resistance and excellent aging resistance. Moreover, since a luminous filler is arranged in the filling material, the prepared toilet has a luminous function, light storage is saturated by irradiating in the light for 5-20 minutes only, the toilet starts to give light when a light source does not exist, and the lighting time can reach 6-15 hours. After the toilet absorbs enough light in the daytime, a user can go to the toilet at night without turning on the light. The toilet has illuminating and indicating effects. Meanwhile, since the light does not need to be turned on, the energy-saving effect is achieved.

Description

Technical field: [0001] The invention relates to the technical field of sanitary ware, in particular to a manufacturing process of a toilet. Background technique: [0002] The current human living environment is that the natural environment is becoming more and more polluted, and coal, natural gas, and land resources are becoming more and more scarce. Protecting the environment and saving resources have become the common responsibility of mankind. As a kind of sanitary ware, toilet is all more and more general to its application no matter city or country. Existing toilet adopts high-quality porcelain clay to form through high-temperature baking, promptly forms ceramic toilet. Porcelain clay is a non-renewable resource, and the use of porcelain clay to produce toilets is likely to cause waste of resources; marble originally refers to white limestone with black patterns produced in Dali, Yunnan Province, and its section can form a natural ink landscape painting. Marble is us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08L75/04C08K5/12E03D11/02B29C45/17
CPCC08L63/00B29C45/17E03D11/02C08L75/04C08K5/12
Inventor 马士永
Owner 安徽雅诺卫浴科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com