A technology for wood and peat, which is applied in wood treatment, wood impregnation, wood impregnation, etc., can solve the problems of cumbersome operation steps, unenvironmental protection, unrealistic and other problems, and achieve the effect of reducing cost and simple operation process.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0025] The present embodiment provides a kind of wood coloring method, and this wood coloring method comprises:
[0026] (1) soak wood: soak wood in dye solution;
[0027] (2) Prepare wrapped peat: modify the peat in a constant temperature drying oven at 140°C, then soak the modified peat in a dye solution to obtain the wrapped peat;
[0028] (3) Baking and coloring: the wood is wrapped with peat, fixed with aluminum foil, dried, and the peat on the surface of the wood is removed to obtain the colored wood.
[0029] The initial density of wood is 0.5g / cm 3 .
[0030] In step (1), the temperature of the dye solution during soaking is 25° C., the soaking time is 30 minutes, and the wood is completely submerged in the dye solution during soaking.
[0031] In step (3), the thickness of the peat wrap is 8mm.
[0032] In the peat, the weight ratio of the peat with a particle size of 0.25-1 mm to the peat with a particle size of 1-2 mm is 3:1.
[0033] The baking temperature is ...
Embodiment 2
[0036] The present embodiment provides a kind of wood coloring method, and this wood coloring method comprises:
[0037] (1) soak wood: soak wood in dye solution;
[0038] (2) Prepare wrapped peat: modify the peat in a constant temperature drying oven at 130°C, then soak the modified peat in a dye solution to obtain the wrapped peat;
[0039] (3) Baking and coloring: the wood is wrapped with wrapped peat, and the wrapped peat is fixed with aluminum foil, dried, and the colored wood is obtained after removing the peat on the wood surface.
[0040] The initial density of wood is 0.4g / cm 3 .
[0041] In step (1), the temperature of the dye solution during soaking is 20° C., the soaking time is 20 minutes, and the wood is completely submerged in the dye solution during soaking.
[0042] In step (3), the thickness of the peat wrapping is 5mm.
[0043] In the peat, the weight ratio of the peat with a particle size of 0.25-1mm to the peat with a particle size of 1-2mm is 2:1.
...
Embodiment 3
[0047] The present embodiment provides a kind of wood coloring method, and this wood coloring method comprises:
[0048] (1) soak wood: soak wood in dye solution;
[0049] (2) Prepare wrapped peat: modify the peat in a constant temperature drying oven at 160°C, then soak the modified peat in a dye solution to obtain the wrapped peat;
[0050] (3) Baking and coloring: the wood is wrapped with peat, dried, and the peat on the surface of the wood is removed to obtain the colored wood.
[0051] The initial density of wood is 0.55g / cm 3 .
[0052] In step (1), the temperature of the dye solution during soaking is 30° C., the soaking time is 40 minutes, and the wood is completely submerged in the dye solution during soaking.
[0053] In step (3), the thickness of the peat wrap is 8mm.
[0054] In the peat, the weight ratio of the peat with a particle size of 0.25-1 mm to the peat with a particle size of 1-2 mm is 5:1.
[0055] In step (3), the coloring method further includes f...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction