Insect-repellent PP woven bag material and preparation method thereof

A woven bag and woven bag technology, applied in the field of woven bags, can solve problems such as insect pests and rice insect breeding

Inactive Publication Date: 2018-10-12
浙江坤诚塑业有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In many cases, it is used in packaging, especially in the current packaging of rice. 90% of rice is packed in woven bags, whether in transportation or storage, but the transportation and storage of rice often encounter such problems , that is, insect pests, rice worms will breed in large numbers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A repellent PP woven bag material,

[0033] Including the following parts by weight:

[0034] Polypropylene: 100 parts

[0035] Pepper powder: 0.3 parts

[0036] Attapulgite powder: 5 servings

[0037] Silane coupling agent: 0.05 part.

[0038] The pepper powder is a 1200-mesh powder made from a pepper mill.

[0039] The attapulgite powder is 400 mesh.

[0040] Described polypropylene comprises following parts by weight:

[0041] PP powder: 20 parts

[0042] PP pellets: 80 parts.

[0043] The silane coupling agent is KH-550.

[0044] The method of preparing a woven bag,

[0045] Step 1: Weigh pepper powder, attapulgite powder, polypropylene, and silane coupling agent according to the ratio of the example formula;

[0046] Step 2: Add pepper powder and attapulgite powder into the grinder and grind for 3 minutes;

[0047] Step 3: Add the ground and mixed powder into a 1000-rpm high-speed mixer, then add a silane coupling agent and mix for 10 minutes;

[0048] ...

Embodiment 2

[0052] A repellent PP woven bag material,

[0053] Including the following parts by weight:

[0054] Polypropylene: 150 parts

[0055] Pepper powder: 0.5 parts

[0056] Attapulgite Powder: 2 parts

[0057] Silane coupling agent: 0.1 part.

[0058] The pepper powder is a 1200-mesh powder made from a pepper mill.

[0059] The attapulgite powder is 400 mesh.

[0060] Described polypropylene comprises following parts by weight:

[0061] PP powder: 20 parts

[0062] PP pellets: 80 parts.

[0063] The silane coupling agent is KH-550.

[0064] The method of preparing a woven bag,

[0065] Step 1: Weigh pepper powder, attapulgite powder, polypropylene, and silane coupling agent according to the ratio of the example formula;

[0066] Step 2: Add pepper powder and attapulgite powder into the grinder and grind for 3 minutes;

[0067] Step 3: Add the ground and mixed powder into a 1000-rpm high-speed mixer, then add a silane coupling agent and mix for 10 minutes;

[0068] Step...

Embodiment 3

[0072] A repellent PP woven bag material,

[0073] Including the following parts by weight:

[0074] Polypropylene: 200 parts

[0075] Pepper powder: 0.2 parts

[0076] Attapulgite powder: 3 servings

[0077] Silane coupling agent: 0.02 parts.

[0078] The pepper powder is a 1200-mesh powder made from a pepper mill.

[0079] The attapulgite powder is 400 mesh.

[0080] Described polypropylene comprises following parts by weight:

[0081] PP powder: 20 parts

[0082] PP pellets: 80 parts.

[0083] The silane coupling agent is KH-550.

[0084] The method of preparing a woven bag,

[0085] Step 1: Weigh pepper powder, attapulgite powder, polypropylene, and silane coupling agent according to the ratio of the example formula;

[0086] Step 2: Add pepper powder and attapulgite powder into the grinder and grind for 3 minutes;

[0087] Step 3: Add the ground and mixed powder into a 1000-rpm high-speed mixer, then add a silane coupling agent and mix for 10mi

[0088] Step 4...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an insect-repellent PP woven bag material which comprises the following components in parts by weight: 100-200 parts of polypropylene, 0.1-0.5 part of Chinese prickly ash powder, 1-5 parts of attapulgite powder, and 0.01-0.1 part of a silane coupling agent. Because attapulgite has a special layered structure, the effective insect repellent components of Chinese prickly ashcan be fully preserved in the mixing process of the Chinese prickly ash powder, and thus the product still has a good mosquito repellent effect in the case of long-term use. The effect cannot be achieved by single use of any kind of the attapulgite and Chinese prickly ash, and a synergistic effect is played with the combination of the attapulgite and Chinese prickly ash.

Description

technical field [0001] The invention relates to a woven bag, in particular to an insect repellent PP woven bag material and a preparation method thereof. Background technique [0002] Woven bag, also known as snakeskin bag. It is a kind of plastic bag, used for packaging, and its raw materials are generally various chemical plastic materials such as polyethylene and polypropylene. Weaving density refers to the number of warp and weft yarns in a 100mm×100mm braided fabric. [0003] The woven bag is made of polypropylene (English name pp) as the main raw material, which is extruded and stretched into a flat wire, and then woven, woven, and bag-made. [0004] In many cases, it is used in packaging, especially in the current packaging of rice. 90% of rice is packed in woven bags, whether in transportation or storage, but the transportation and storage of rice often encounter such problems , that is, insect pests, and rice worms will breed in large numbers. Contents of the i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08K13/02C08K3/34C08K5/544C08K5/00
CPCC08L23/12C08L2205/025C08K13/02C08K3/346C08K5/544C08K5/0058
Inventor 刘建平
Owner 浙江坤诚塑业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products