Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Non-phosphorus and non-halogen flame-retardance polyester sheet material and preparation method thereof

A flame-retardant polyester and polyester sheet technology, applied in coatings, fire-resistant coatings, etc., can solve problems such as high environmental hazards, water pollution, and eutrophication of water quality, and achieve reduced production costs, good flame-retardant performance, and increased The effect of humidity

Inactive Publication Date: 2018-09-21
SUZHOU WILLOCK ELECTRONICS TECH CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The flame retardant effect of halogen or phosphorus is obvious, but it is also relatively harmful to the environment. For example, dioxins are produced when halogen-containing flame retardant materials are burned, which can exist in the environment for many years, and even accumulate in organisms for life; phosphorus will cause water quality deterioration. Eutrophication, serious water pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The invention provides a phosphorus-free and halogen-free flame-retardant polyester sheet, the composition of the sheet substrate is as follows (percentage by weight):

[0021] Polyethylene terephthalate accounts for 78%, polybutylene terephthalate accounts for 18%, glass fiber accounts for 1%, antioxidant 1010 accounts for 1%, ethylene-vinyl acetate copolymer accounts for 0.5%, octadecane Dimethyl quaternary ammonium nitrate accounted for 0.9%, benzophenone accounted for 0.6%.

[0022] The surface of the polyester sheet substrate is coated with a coating containing a phosphorus-free and halogen-free flame retardant, and the coating contains 15% (by weight) of a phosphorus-free and halogen-free flame retardant, 83% (by weight) of And 2% (weight percent) of MF dispersant. Among them, the phosphorus-free and halogen-free flame retardant is composed of 40% (weight percent) sodium polyacrylate and 60% (weight percent) polypropylene carbonate. Sodium polyacrylate has a netw...

Embodiment 2

[0027] The invention provides a phosphorus-free and halogen-free flame-retardant polyester sheet, the composition of the sheet substrate is as follows (percentage by weight):

[0028] Polyethylene terephthalate accounts for 82%, polybutylene terephthalate accounts for 12%, glass fiber accounts for 2%, antioxidant 1076 accounts for 1.5%, ethylene-vinyl acetate copolymer accounts for 1%, triethanol Methyl quaternary ammonium methosulfate accounted for 0.5%, salicylate accounted for 1%.

[0029] The surface of the polyester sheet substrate is coated with a coating containing a phosphorus-free and halogen-free flame retardant, and the coating contains 20% (weight percent) of a phosphorus-free and halogen-free flame And 1.5% (weight percent) of MF dispersant. Among them, the phosphorus-free and halogen-free flame retardant is composed of 30% (weight percent) sodium polyacrylate and 70% (weight percent) polypropylene carbonate. Sodium polyacrylate has a network molecular structure,...

Embodiment 3

[0034] The invention provides a phosphorus-free and halogen-free flame-retardant polyester sheet, the composition of the sheet substrate is as follows (percentage by weight):

[0035] Polyethylene terephthalate accounts for 80%, polybutylene terephthalate accounts for 15%, glass fiber accounts for 1.5%, antioxidant 1010 accounts for 0.5%, ethylene-vinyl acetate copolymer accounts for 1%, triethanol Methyl quaternary ammonium methosulfate accounted for 0.5%, benzophenone accounted for 1.5%.

[0036] The surface of the polyester sheet substrate is coated with a coating containing a phosphorus-free and halogen-free flame retardant, and the coating contains 11% (weight percent) of a phosphorus-free and halogen-free flame And 1% (by weight) of MF dispersant. Among them, the phosphorus-free and halogen-free flame retardant is composed of 70% (weight percent) sodium polyacrylate and 30% (weight percent) polypropylene carbonate. Sodium polyacrylate has a network molecular structure, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a non-phosphorus and non-halogen flame-retardance polyester sheet material. The material comprises a polyester base material and a flame-retardance coating which coats the surface of the polyester base material. The material is characterized in that the flame-retardance coating comprises, by weight, 11-25% of non-phosphorus and non-halogen flame retardant and 74.5-88% of polyacrylate. The non-phosphorus and non-halogen flame retardant is composed of sodium polyacrylate and poly propylene carbonate. Sodium polyacrylate is of a network molecular structure and can achievethe moisture absorption and moisture preservation effects, the temperature of the surrounding environment of the polyester sheet material is lowered to a certain extent, the humidity is increased, and the flame retardance of the polyester sheet material is improved; propylene carbonate can be heated and decomposed to generate a large amount of carbon dioxide under the burning condition, the oxygen concentration in the surrounding environment of the polyester sheet material is lowered, and the flame retardance aim is achieved. The flame retardant does not contain halogen or phosphorus, and theproblem of environmental pollution is solved. Meanwhile, a surface coating method is adopted, the preparation technology is easier and more convenient to use, and the method helps to improve the working efficiency and lower the production cost.

Description

technical field [0001] The invention relates to the field of polyester sheets, in particular to a phosphorus-free and halogen-free flame-retardant polyester sheet and a preparation method thereof. Background technique [0002] Polyester sheet (PET) uses polyethylene terephthalate as the main raw material and is a material with relatively comprehensive properties. It has good transparency and high gloss. Compared with ordinary sheets, polyester sheets have better mechanical properties. Polyester sheet also has excellent electrical insulation properties, weak acid resistance and oil resistance, and also has the advantages of non-toxicity, good stability against chemicals, and low water absorption. Polyester sheet is used as various food, medicine, non-toxic and sterile packaging materials because of its many advantages; high-grade packaging materials for textiles, precision instruments, electrical components; audio tapes, video tapes, film films, computer floppy disks, metal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J7/04C08L67/02C08L23/08C08K13/04C08K7/14C09D133/12C09D133/08C09D125/14C09D5/18
CPCC08J7/0427C08J2367/02C08J2425/14C08J2433/08C08J2433/12C08L67/02C08L2201/02C08L2201/22C08L2205/02C08L2205/025C08L2205/03C08L2205/06C09D5/18C09D125/14C09D133/08C09D133/12C08L23/0853C08K13/04C08K7/14C08L33/02C08L69/00
Inventor 何建平
Owner SUZHOU WILLOCK ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com