Anti-vibration W-In-containing stainless steel kettle material for hot dip aluminum plating

A technology of hot-dip aluminum plating and stainless steel pots, which is applied in the field of alloys, can solve the problems of short service life, corrosion of iron pots, and large abnormal aluminum consumption, etc., to achieve improved corrosion and leakage, dense welds, and excellent welding performance Effect

Inactive Publication Date: 2018-08-17
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the serious chemical interaction between the aluminum liquid and the iron pot, the iron pot used for hot-dip aluminum plating is seriously corroded during work, the service life is extremely short, and the abnormal aluminum consumption is large.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A vibration-resistant stainless steel pot material containing W and In for hot-dip aluminum plating. In terms of weight percentage, the composition of the alloy is Rb:0.3wt.%, W:0.5wt.%, Cr:6.0wt.%, Al:5.0wt.%, Co:1.5wt.%, In:1.0wt.%. ,S:0.1wt.%, the balance is iron. The preparation method of the above-mentioned vibration-resistant stainless steel pot material containing W and In for hot-dip aluminum plating includes the following steps: adding the above-mentioned raw materials into an argon-protected induction furnace, and using a silicon carbide crucible; induction heating to 1500 Form the alloy solution at -1600 degrees, and use the electromagnetic stirring effect to fully stir for about 10 minutes; keep the alloy liquid at 1500-1600 degrees for 10 minutes and then cast it into the required round ingot. The obtained ingot is hot-rolled at 800 degrees, and the rolling reduction in each pass is 10-15%. After every two hot rollings, the intermediate annealing temperat...

Embodiment 2

[0020]A vibration-resistant stainless steel pot material containing W and In for hot-dip aluminum plating. In terms of weight percentage, the composition of the alloy is Rb: 0.5wt.%, W: 0.8wt.%, Cr: 8.0wt.%, Al: 6.0wt.%, Co: 3.0wt.%, In: 1.5wt.% ,S:0.2wt.%, the balance is iron. The preparation method of the above-mentioned vibration-resistant stainless steel pot material containing W and In for hot-dip aluminum plating includes the following steps: adding the above-mentioned raw materials into an argon-protected induction furnace, and using a silicon carbide crucible; induction heating to 1500 Form the alloy solution at -1600 degrees, and use the electromagnetic stirring effect to fully stir for about 10 minutes; keep the alloy liquid at 1500-1600 degrees for 10 minutes and then cast it into the required round ingot. The obtained ingot is hot-rolled at 800 degrees, and the rolling reduction in each pass is 10-15%. After every two hot rollings, the intermediate annealing temp...

Embodiment 3

[0023] A vibration-resistant stainless steel pot material containing W and In for hot-dip aluminum plating. In terms of weight percentage, the composition of the alloy is Rb:0.4wt.%, W:0.6wt.%, Cr:6.4wt.%, Al:5.8wt.%, Co:1.9wt.%, In:1.2wt.%. ,S:0.1wt.%, the balance is iron. The preparation method of the above-mentioned vibration-resistant stainless steel pot material containing W and In for hot-dip aluminum plating includes the following steps: adding the above-mentioned raw materials into an argon-protected induction furnace, and using a silicon carbide crucible; induction heating to 1500 Form the alloy solution at -1600 degrees, and use the electromagnetic stirring effect to fully stir for about 10 minutes; keep the alloy liquid at 1500-1600 degrees for 10 minutes and then cast it into the required round ingot. The obtained ingot is hot-rolled at 800 degrees, and the rolling reduction in each pass is 10-15%. After every two hot rollings, the intermediate annealing temperat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-vibration W-In-containing stainless steel kettle material for hot dip aluminum plating. The anti-vibration W-In-containing stainless steel kettle material comprises, byweight, 0.3-0.5 wt.% of Rb, 0.5-0.8 wt.% of W, 6.0-8.0 wt.% of Cr, 5.0-6.0 wt.% of Al, 1.5-3.0 wt.% of Co, 1.0-1.5 wt.% of In, 0.1-0.2 wt.% of S, and the balance Fe. According to the anti-vibration W-In-containing stainless steel kettle material for hot dip aluminum plating, the current situation that at present, technologies of materials for iron kettles in the hot dip aluminum plating field inChina is changed, through innovation and optimization of the material science, the development bottleneck of the production technology and equipment for hot dip aluminum plating steel plates in the high-end field in China is broken through, and in the near future, the iron kettle material is widely applied to the greatest extent.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to an iron alloy. Background technique [0002] Metal materials are damaged by the physical and chemical action of the surrounding medium, which is called metal corrosion. Metal rusting is the most common form of corrosion. During corrosion, a chemical or electrochemical heterogeneous reaction occurs at the interface of the metal, which turns the metal into an oxidized (ionic) state. This will significantly reduce the mechanical properties of metal materials such as strength, plasticity, and toughness, destroy the geometry of metal components, increase wear between parts, deteriorate electrical and optical physical properties, shorten the service life of equipment, and even cause disasters such as fire and explosion. sex accident. According to statistics, the annual loss of steel due to metal corrosion accounts for about 10-20% of the steel output of the year. The indirect losses ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/06C22C38/22C22C38/30C22C38/60C23C2/12
CPCC22C38/60C22C38/002C22C38/06C22C38/22C22C38/30C23C2/003C23C2/12
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products