Novel release paper and preparation method thereof

A kind of release paper, a new type of technology, applied in the field of release paper, can solve the problems of unfavorable environmental protection, large pollution, high energy consumption in papermaking, and achieve the effect of improving industrial production efficiency and shortening molding time

Inactive Publication Date: 2018-08-07
HUNAN FUTAI DIGITAL MATERIAL TECH
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The release paper produced by the existing technology requires a large amount of base paper, which is made of wood pulp. Since wood takes time to become a material, with the massive felling of wood, wood pulp will gradually be in short supply, so the cost of base paper will continue to increase. Rising, and papermaking consumes a lot of energy and pollutes a lot, which is not conducive to environmental protection
Moreover, normal release paper needs to go through three processes, and each process consumes a lot of energy. The production cost requires a large amount of silicone oil, which is more expensive, and most of the silicone oil is diluted with organic solvents. These organic solvents are volatile, toxic, It is difficult to completely recycle, which is not conducive to environmental protection
[0004] In addition, if the tension of the existing release paper is too high, the paper will be broken during the winding process; on the contrary, if the tension is too small, the winding will be loose and the edges will be irregular

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A new type of release paper, comprising the following components by weight: 23 parts of substrate, 10 parts of high molecular polymer, 1.7 parts of plasticizer, 0.5 part of anti-sticking agent, 1 part of lubricant, 0.1 part of foaming agent , 0.7 parts of active agent.

[0028] The base material comprises: 20 parts of straw powder and 3 parts of asbestos powder.

[0029] The high molecular polymer comprises: 5 parts of polyvinyl alcohol, 2 parts of polylactic acid and 3 parts of polyvinyl chloride.

[0030] The plasticizer includes: 1 part of hydroxyethyl cellulose, 0.3 part of 1,6-hexanediol, 0.3 part of triethanolamine, and 0.1 part of benzoic acid.

[0031] The anti-sticking agent is silicone oil.

[0032] The lubricant comprises: 0.5 part of chlorinated paraffin and 0.5 part of polyethylene wax.

[0033] The blowing agent is azodicarbonamide.

[0034] The active agent comprises: 0.5 part of cassava flour and 0.2 part of stearic acid.

[0035] A kind of novel re...

Embodiment 2

[0040] A new type of release paper, comprising the following components by weight: 35 parts of substrate, 15 parts of high molecular polymer, 3.7 parts of plasticizer, 1 part of anti-sticking agent, 2 parts of lubricant, 0.5 part of foaming agent , 1.5 parts of active agent.

[0041] The base material comprises: 30 parts of straw powder and 5 parts of asbestos powder.

[0042] The high molecular polymer comprises: 7 parts of polyvinyl alcohol, 3 parts of polylactic acid and 5 parts of polyvinyl chloride.

[0043] The plasticizer includes: 2 parts of hydroxyethyl cellulose, 0.7 part of 1,6-hexanediol, 0.7 part of triethanolamine, and 0.3 part of benzoic acid.

[0044] The anti-sticking agent is silicone oil.

[0045] The lubricant comprises: 1 part of chlorinated paraffin and 1 part of polyethylene wax.

[0046] The blowing agent is azodicarbonamide.

[0047] The active agent comprises: 1 part of cassava flour and 0.5 part of stearic acid.

[0048] A kind of novel release ...

Embodiment 3

[0053] A new type of release paper, comprising the following components by weight: 24 parts of substrate, 12 parts of high molecular polymer, 2.7 parts of plasticizer, 0.5-1 part of anti-sticking agent, 1.5 parts of lubricant, foaming agent 0.2 parts, active agent 1 part.

[0054] The base material comprises: 25 parts of straw powder and 4 parts of asbestos powder.

[0055] The high molecular polymer comprises: 6 parts of polyvinyl alcohol, 2.5 parts of polylactic acid and 3.5 parts of polyvinyl chloride.

[0056] The plasticizer includes: 1.5 parts of hydroxyethyl cellulose, 0.5 parts of 1,6-hexanediol, 0.5 parts of triethanolamine, and 0.2 parts of benzoic acid.

[0057] The anti-sticking agent is silicone oil.

[0058] The lubricant comprises: 0.7 part of chlorinated paraffin and 0.8 part of polyethylene wax.

[0059] The blowing agent is azodicarbonamide.

[0060] The active agent comprises: 0.7 parts of cassava flour and 0.3 parts of stearic acid.

[0061] A kind of no...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses novel release paper which comprises 23-35 parts of base material, 10-15 parts of high molecular polymer, 1.7-3.7 parts of plasticizer, 0.5-1 part of anti-bonding agent, 1-2 parts of lubricant, 0.1-0.5 part of foamer and 0.7-1.5 parts of activator. Tension of the novel release paper is improved; stearic acid is adopted to improve tenacity of the release paper, and the release paper is enabled to realize close fitting in the process of rolling, is free of displacement and cannot be broken by pulling.

Description

technical field [0001] The invention belongs to a release paper, in particular to a novel release paper and a preparation method thereof. Background technique [0002] Release paper, also known as release paper and anti-adhesive paper, is mainly pasted on the surface of the tape to protect the adhesive layer on the surface of the tape. The traditional release paper is composed of base paper, isolation layer and anti-adhesive layer. Its preparation process is to coat a layer of release agent (mainly polyethylene) on the surface of the bottom paper of the release paper, and then coat a layer of anti-sticking agent (mainly silicone oil) on the surface of the coating layer to obtain Release paper. [0003] The release paper produced by the existing technology requires a large amount of base paper, which is made of wood pulp. Since wood takes time to become a material, with the massive felling of wood, wood pulp will gradually be in short supply, so the cost of base paper will ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J7/40C08L29/04C08L67/04C08L27/06C08L1/28C08L83/04C08L91/06C08L23/06C08L3/02C08L1/00C08K13/06C08K9/00C08K7/12C08K5/053C08K5/17C08K5/09C08J5/18C08J9/10
CPCC08J5/18C08J9/0023C08J9/0028C08J9/0061C08J9/0066C08J9/0085C08J9/103C08J2203/04C08J2329/04C08J2427/06C08J2467/04C08K5/053C08K5/09C08K5/17C08K7/12C08K9/00C08K13/06C09J7/40
Inventor 沈宝善沈园园陈玲令
Owner HUNAN FUTAI DIGITAL MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com