Interior-exterior wall putty powder with high water resistance as well as preparation method and application thereof

A technology of interior and exterior walls and putty powder, which is applied in the direction of filling slurry, etc., can solve the problems of affecting market promotion, putty powder is not environmentally friendly, and poor water resistance, and achieves excellent environmental protection performance, long storage time, and reduced complexity Effect

Active Publication Date: 2018-07-24
朱路军
View PDF10 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The putty powder in the prior art is not environmentally friendly, low in strength, poor in water resistance, etc., which affects its further marketing efforts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Interior-exterior wall putty powder with high water resistance as well as preparation method and application thereof
  • Interior-exterior wall putty powder with high water resistance as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-5

[0042] The concrete formula of this interior and exterior wall putty powder carries out batching according to following table 1:

[0043] Table 1 specific formula

[0044] Component (kg)

Example 1

Example 2

Example 3

Example 4

Example 5

Sulphoaluminate cement

750

800

770

780

775

black cement

20

10

18

12

16

80 mesh quartz sand

100

200

120

180

160

calcium chloride

14

12

14

13

13

lithium chloride

8

7

7.5

7

7

Talc powder

7

4

6

5

5

Zinc stearate

4

8

5

7

6

Hydroxypropylmethylcellulose

7

4

5

6

6

UNF-4 early strength superplasticizer

4

8

7

5

6

wollastonite powder

5

3

4

5

4.5

Titanium dioxide

1

2

1.2

1.5

1.3

Hexametaphosphate

5

12

10

7

8 ...

Embodiment 6-8

[0049] The concrete formula of this interior and exterior wall putty powder carries out batching according to following table 2:

[0050] Table 2 specific formula

[0051] Component (kg)

Example 6

Example 7

Example 8

Sulphoaluminate cement

770

790

770

black cement

15

12

18

80 mesh quartz sand

120

180

170

calcium chloride

13

12

14

lithium chloride

8

7

7.5

Talc powder

7

4

6

Zinc stearate

4

8

5

Hydroxypropylmethylcellulose

7

4

5

FD-N-S early strength superplasticizer

4

8

7

wollastonite powder

5

3

4

Titanium dioxide

1

2

1.2

Hexametaphosphate

5

12

10

heavy calcium powder

70

80

75

double fly powder

40

50

48

rubber powder

2

3

2.2

Ash calcium powder

10

5

8

Di...

Embodiment 9

[0056] Concrete formula is consistent with embodiment 8, just preparation method carries out according to the following steps:

[0057] 1) First mix sulfoaluminate cement, 80 mesh quartz sand, talcum powder, zinc stearate, wollastonite powder, titanium dioxide, black cement, heavy calcium powder, double fly powder, rubber powder, lime calcium powder, diatom mud , Add the magnetic filler into the stirring tank, control the stirring rate at 500rpm while stirring, and stir for 12h;

[0058] 2) Add calcium chloride, lithium chloride, hydroxypropyl methylcellulose, water reducer, and sodium hexametaphosphate to the mixing tank in sequence, and control the stirring rate at 400rpm while stirring, and mix and stir for 10-20min. Pack it into a finished product of 10kg / bag, and store it in a dry place at normal temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides interior-exterior wall putty powder with high water resistance. The interior-exterior wall putty powder is mainly prepared from the following ingredients in parts by mass: 750 to 800 parts of sulphate aluminum cement, 10 to 20 parts of black cement, 100 to 200 parts of 80-mesh quartz sand, 12 to 14 parts of calcium chloride, 7 to 8 parts of lithium chloride, 4 to 7 parts oftalcum powder, 4 to 8 parts of zinc stearate, 4 to 7 parts of hydroxypropyl methyl cellulose, 4 to 8 parts of water reducing agent, 3 to 5 parts of wollastonite powder, 1 to 2 parts of titanium dioxide, 5 to 12 parts of sodium hexametaphosphate, 70 to 80 parts of coarse whiting powder, 40 to 50 parts of heavy calcium carbonate powder, 2 to 3 parts of gelatin powder and 5 to 10 parts of ash calciumpowder. According to the interior-exterior wall putty powder disclosed by the embodiment of the invention, all kinds of raw materials are organically combined and scientifically processed; thus, theinterior-exterior wall putty powder can be utilized as exterior wall putty powder and also can be utilized as interior wall putty powder.

Description

technical field [0001] The invention relates to the field of decoration and decoration, in particular to an interior and exterior wall putty powder with high water resistance and a preparation method and application thereof. Background technique [0002] Putty powder is a kind of building decoration material, the main components are talcum powder and glue. Putty is a kind of base material for leveling the wall, which lays a good foundation for future decoration (painting and wallpaper). Putty is divided into two kinds: putty inside wall and putty on exterior wall. External wall putty can resist wind and sun, so it has good gelation, high strength and low environmental index. The comprehensive index of putty in the inner wall is good, and it is hygienic and environmentally friendly. Therefore, the inner wall is not for external use and the outer wall is not for internal use. Putties are usually based on gypsum or cement, so rough surfaces are easier to bond firmly. However...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 朱路军
Owner 朱路军
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More