Laser surface treatment method for improving thermal corrosion resistance of thermal barrier coating

A technology of laser surface treatment and thermal barrier coating, applied in the direction of coating, metal material coating process, melt spraying, etc., can solve the problems of surface hot corrosion and infiltration hot corrosion inhibition, etc., and achieve the degree of surface corrosion. The effect of reducing and improving heat-resistant corrosion resistance and prolonging service life

Active Publication Date: 2018-06-29
CHINA UNIV OF PETROLEUM (EAST CHINA)
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing laser remelting technology process is relatively simple, and the inhibition effect on surface thermal corrosion and infiltration thermal corrosion is not obvious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Laser surface treatment method for improving thermal corrosion resistance of thermal barrier coating
  • Laser surface treatment method for improving thermal corrosion resistance of thermal barrier coating
  • Laser surface treatment method for improving thermal corrosion resistance of thermal barrier coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A laser surface treatment method for improving the heat-resistant corrosion resistance of YSZ thermal barrier coatings includes the following steps:

[0040] Step S1: Use an ultrasonic instrument to ultrasonically clean the surface of the YSZ thermal barrier coating, and adjust the spot shape of the semiconductor laser to a rectangle with a spot size of 12mm×2mm;

[0041] Step S2: Adjust the laser power of the semiconductor laser to 400W, adjust the scanning speed of the semiconductor laser to 10mm / s, and obtain an energy density of 7.2J / mm 2 Using the low-energy density laser to perform self-preheating scanning on the YSZ thermal barrier coating processed in step S1;

[0042] Step S3: Adjust the laser power of the semiconductor laser to 1800W, adjust the scanning speed of the semiconductor laser to 20mm / s, and obtain an energy density of 12J / mm 2 Using the high-energy-density laser to perform remelting scanning on the YSZ thermal barrier coating processed in step S2;

[0043] S...

Embodiment 2

[0048] A laser surface treatment method for improving the heat-resistant corrosion resistance of YSZ thermal barrier coatings includes the following steps:

[0049] Step S1: Use an ultrasonic instrument to ultrasonically clean the surface of the YSZ thermal barrier coating, and adjust the spot shape of the semiconductor laser to a rectangle with a spot size of 12mm×2mm;

[0050] Step S2: Adjust the laser power of the semiconductor laser to 300W, adjust the scanning speed of the semiconductor laser to 8mm / s, and obtain an energy density of 7.7J / mm 2 Using the low-energy density laser to perform self-preheating scanning on the YSZ thermal barrier coating processed in step S1;

[0051] Step S3: Adjust the laser power of the semiconductor laser to 1500W, adjust the scanning speed of the semiconductor laser to 15mm / s, and obtain an energy density of 12.9J / mm 2 Using the high-energy-density laser to perform remelting scanning on the YSZ thermal barrier coating processed in step S2;

[0052] ...

Embodiment 3

[0057] A laser surface treatment method for improving the heat-resistant corrosion resistance of YSZ thermal barrier coatings includes the following steps:

[0058] Step S1: Use an ultrasonic instrument to ultrasonically clean the surface of the YSZ thermal barrier coating, and adjust the spot shape of the semiconductor laser to a rectangle with a spot size of 12mm×2mm;

[0059] Step S2: Adjust the laser power of the semiconductor laser to 500W, adjust the scanning speed of the semiconductor laser to 12mm / s, and obtain an energy density of 7.5J / mm 2 Using the low-energy density laser to perform self-preheating scanning on the YSZ thermal barrier coating processed in step S1;

[0060] Step S3: Adjust the laser power of the semiconductor laser to 2000W, adjust the scanning speed of the semiconductor laser to 28mm / s, and obtain an energy density of 12.8J / mm 2 Using the high-energy-density laser to perform remelting scanning on the YSZ thermal barrier coating processed in step S2;

[0061]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a laser surface treatment method for improving the thermal corrosion resistance of a thermal barrier coating, belonging to the technical field of treatment of thermal barrier coatings. The method comprises the following steps: S1, ultrasonically cleaning the surface of the thermal barrier coating, and adjusting the spot shape of a laser to a rectangular shape; S2, adjustingthe laser in the step S1 to emit low energy density laser, and carrying out self-preheating scanning on the thermal barrier coating treated in the step S1; S3, adjusting the laser in the step S1 to emit high energy density laser, and carrying out re-melting scanning on the thermal barrier coating treated in the step S2; S4, adjusting the laser in the step S1 to emit medium energy density laser, and performing a slow-cooling scanning on the thermal barrier coating treated in the step S3; S5, naturally cooling the thermal barrier coating treated in the step S4 to room temperature, and then using compressed air to remove impurities on the surface of the coating cooled to room temperature. After the coating is treated by using the method, the coating is smooth and dense, the thermal corrosionof corrosive salt is inhibited, and the service life of the coating is prolonged.

Description

Technical field [0001] The invention relates to the technical field of treatment of thermal barrier coatings, in particular to a laser surface treatment method for improving the thermal barrier coatings' heat-resistant corrosion performance. Background technique [0002] Thermal barrier coatings have comprehensive properties such as high melting point, low thermal conductivity, high fracture toughness and high thermal expansion coefficient, and are currently widely used in the manufacture of turbine blades for aero engines and gas turbines. There are many types of thermal barrier coating materials, among which YSZ(Y 2 O 3 Stable ZrO 2 ) Thermal barrier coating materials are the most mature and widely used, and are often obtained by thermal spraying methods. As one of the important applications, the YSZ thermal barrier coatings in gas turbines are often used in the harsh working conditions of thermal corrosion. The Na and V impurities in the fuel form Na in the high-temperature ga...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C24/10C23C4/18C23C4/11
CPCC23C4/11C23C4/18C23C24/10
Inventor 伊鹏战祥华尹晓丽贾德龙肖培发王志远桂文波刘衍聪
Owner CHINA UNIV OF PETROLEUM (EAST CHINA)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap