Production method of antistatic silk quilt core
A production method and silk quilt technology, which are applied in cocoon cleaning/classification, silk fiber production, fiber chemical post-treatment, etc., can solve the problem of reducing silk quilt warmth and breathability, lack of anti-static effect, easy looseness of silk quilt core, etc. problem, to achieve the effect of firm rectangular wire mesh, firm screw connection and simple process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0024] A method for making an antistatic silk quilt core, comprising the following steps:
[0025] (1) Select the upper cocoons from the silkworm cocoons, and then put the upper cocoons into the screening machine for screening. In order to meet the size of the large cocoons and small cocoons, the diameter of the sieve hole of the screening machine can be selected as 3cm to obtain large cocoons and small cocoons. Cocoons, using the large cocoons as raw materials for silk quilt cores.
[0026] (2) Put the large cocoon in the above step (1) into a drier for drying. The drying is as follows: first, dry the large cocoon at 90°C for 6 minutes, and then dry the large cocoon at a temperature of 55°C Dry for 10 minutes to obtain dry cocoons.
[0027] (3) Soak the dried cocoons obtained in the above step (2) in a softening solution, the temperature of the softening solution is 85°C, and the softening solution is fatty alcohol polyoxyethylene ether, sodium bicarbonate and sodium perbora...
Embodiment 2
[0033] A method for making an antistatic silk quilt core, comprising the following steps:
[0034] (1) Select the upper cocoons from the silkworm cocoons, and then put the upper cocoons into the screening machine for screening. In order to meet the size of the large cocoons and small cocoons, the diameter of the sieve hole of the screening machine can be selected as 3cm to obtain large cocoons and small cocoons. Cocoons, using the large cocoons as raw materials for silk quilt cores.
[0035] (2) Put the large cocoons in the above step (1) into a dryer for drying. The drying is as follows: first, dry the large cocoons at 95°C for 8 minutes, and then dry the large cocoons at a temperature of 60°C Dry for 14 minutes to obtain dry cocoons.
[0036] (3) Soak the dried cocoons obtained in the above step (2) in a softening solution, the temperature of the softening solution is 90°C, and the softening solution is fatty alcohol polyoxyethylene ether, sodium bicarbonate and sodium perb...
Embodiment 3
[0042] A method for making an antistatic silk quilt core, comprising the following steps:
[0043] (1) Select the upper cocoons from the silkworm cocoons, and then put the upper cocoons into the screening machine for screening. In order to meet the size of the large cocoons and small cocoons, the diameter of the sieve hole of the screening machine can be selected as 3cm to obtain large cocoons and small cocoons. Cocoons, using the large cocoons as raw materials for silk quilt cores.
[0044] (2) Put the large cocoon in the above step (1) into a dryer for drying. The drying is as follows: first, dry the large cocoon at 100°C for 10 minutes, and then dry the large cocoon at a temperature of 65°C Dry for 15 minutes to obtain dry cocoons.
[0045] (3) Soak the dried cocoons obtained in the above step (2) in softening solution, the temperature of the softening solution is 92°C, and the softening solution is fatty alcohol polyoxyethylene ether, sodium bicarbonate and sodium perbora...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com