Water-based UV curving vacuum electroplating finishing coating, preparation method and electroplating method thereof

A vacuum electroplating and water-based technology, applied in the field of chemical coatings, can solve the problems of poor adhesion, easy friction, scratches and scratches of metal coatings, and achieve the effect of solving poor adhesion, simple construction and good adhesion

Inactive Publication Date: 2018-06-01
CHUZHOU JINQIAO TEXAS NEW MATERIALS CO LTD
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a water-based UV curing vacuum electroplating topcoat on the basis of the prior art, which can solve the problems of poor adhesion to the metal coating, easy friction, scratching, and scratching, and provide a certain resistance sex and barrier

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0046] The preparation method of water-based UV curing vacuum electroplating finish provided by the invention, it may further comprise the steps:

[0047] (1) Add water-based acrylate, trimethylolpropane triacrylate, co-solvent, and leveling agent into the disperser according to the formula ratio and stir at a speed of 400~500r / min for 5~15min;

[0048] (2) Add water-based urethane acrylate, photoinitiator, and water to the mixture in step (1) in turn and stir at a speed of 900~1100r / min for 5~10min.

[0049] The water-based UV curing vacuum electroplating topcoat provided by the invention carries out the method for electroplating, and it comprises the following steps:

[0050] (1) Material Handling:

[0051] a) Topcoat treatment: Filter the topcoat with a 600-mesh filter for later use;

[0052] b) Pretreatment: Wipe the substrate with alcohol to remove oil stains and dust on the substrate, spray the primer, and the air pressure of the spray gun is 2.0~3.0kg / cm 2 , the dist...

Embodiment 1

[0057] A water-based UV curing vacuum electroplating topcoat, which includes the following components and parts by mass:

[0058] Water-based polyurethane acrylate (Hefei Polymerization Radiation 709T) 50 parts;

[0059] 25 parts of water-based acrylate (BASF 7602LV);

[0060] 3 parts of trimethylolpropane triacrylate;

[0061] Leveling agent (EFKA 3777) 1.2 parts;

[0062] Photoinitiator (phenyl bis (2.4.6-trimethylbenzoyl) phosphine oxide) 6 parts;

[0063] Co-solvent (ethylene glycol butyl ether) 18 parts;

[0064] 45 parts of water.

[0065] The preparation method of this coating comprises the following steps:

[0066] (1) Add water-based acrylate, trimethylolpropane triacrylate, co-solvent, and leveling agent according to the formula ratio into the disperser and stir at a speed of 480 r / min for 12 minutes;

[0067] (2) Add water-based urethane acrylate, photoinitiator, and water to the mixture in step (1) in sequence and stir at a speed of 950 r / min for 6 min.

Embodiment 2

[0069] A water-based UV curing vacuum electroplating topcoat, which includes the following components and parts by mass:

[0070] Water-based polyurethane acrylate (Hefei Polymerization Radiation HF800) 30 parts;

[0071] Water-based acrylate (BASF 7601LV) 15 parts;

[0072] 7.5 parts of trimethylolpropane triacrylate;

[0073] Leveling agent (BYK 346) 0.3 parts;

[0074] Leveling agent (BYK 333) 0.5 parts;

[0075] Photoinitiator (2-hydroxy-2-methyl-1-phenyl-1-propanone) 3 parts;

[0076] Co-solvent (isopropanol) 12 parts;

[0077] 55 parts of water.

[0078] The preparation method of this coating comprises the following steps:

[0079] (1) Add water-based acrylate, trimethylolpropane triacrylate, co-solvent, and leveling agent according to the formula ratio into the disperser and stir at a speed of 450 r / min for 10 min;

[0080] (2) Add water-based urethane acrylate, photoinitiator, and water to the mixture in step (1) in turn and stir at a speed of 1000r / min for 8 mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a water-based UV curving vacuum electroplating finishing coating, a preparation method and an electroplating method thereof, and belongs to the field of the chemical coating. The coating is prepared from the following components in parts by mass: 10-60 parts of water-based polyurethane acrylate, 5-30 parts of water-based acrylate, 2.5-15 parts of trimethylolpropane triacrylate, 0.1-1.5 parts of flatting agent, 1-8 parts of photoinitiator, 8-20 parts of cosolvent, and 40-70 parts of water. The water-based finishing coating provided by the invention coats on the plastic aluminizing surface through vacuum electroplating, the paint film has good adhesive force, wear-resisting property, poach-resistance, and sweat resistance and the like. Furthermore, the finishing coating is the environment-friendly coating, and has the features of being convenient for operation, simple in construction and extensive in applicability and the like.

Description

technical field [0001] The invention belongs to the field of chemical coatings, and specifically relates to a water-based UV-curable vacuum electroplating topcoat; in addition, the invention also relates to a preparation method and an electroplating method of the water-based UV-curable vacuum electroplating topcoat. Background technique [0002] With the improvement of people's living standards, the use of portable electronic products such as mobile phones, digital cameras, digital video cameras, MP3, MP4, etc. is becoming more and more common. The shells of these products all need to have fashionable decorative effect and anti-fouling, wear-resistant and anti-scratch properties, especially the shells of mobile phones need electronic shielding and anti-radiation functions, and the vacuum coating process makes these all possible. [0003] Vacuum plating is a physical deposition phenomenon. That is, argon gas is injected in a vacuum state, and the argon gas hits the target ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/14C09D133/04B05D3/02B05D7/00B05D7/14
CPCC09D175/14B05D3/0254B05D7/14B05D7/54B05D2202/25B05D2320/00B05D2502/00B05D2503/00C09D133/04
Inventor 王景泉
Owner CHUZHOU JINQIAO TEXAS NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap