Preparation method of heat-not-burn reconstituted tobacco through roll-in method and application thereof

A heat-not-burn and reconstituted tobacco leaf technology, which is applied in the application, preparation of tobacco, and cigar manufacturing, can solve the problems of good processing resistance and achieve the effects of good processing resistance, increased surface area, and non-sticking surface

Inactive Publication Date: 2018-05-25
HUBEI CHINA TOBACCO IND
View PDF2 Cites 42 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] According to the above-mentioned deficiencies and defects, the object of the present invention is to provide a preparation method of heat-not-burn reconstituted tobacco leaves by rolling method and its application, and improve the process method on the basis of rolling method to solve the problem of adding a large proportion of atomizing agent , and use a food-grade adhesive to evenly disperse and solidify the atomizer into the tobacco material. The prepared heat-not-burn reconstituted tobacco leaves have an even distribution of the atomizer while the content of the atomizer is increased, and the surface is not sticky, and its fiber content is increased. Tensile strength, good processing resistance, uniform release of smoke when smoking, good sensory effect, good simulated smoking experience

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of heat-not-burn reconstituted tobacco through roll-in method and application thereof
  • Preparation method of heat-not-burn reconstituted tobacco through roll-in method and application thereof
  • Preparation method of heat-not-burn reconstituted tobacco through roll-in method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A method for preparing heated non-combustion reconstituted tobacco by rolling method, specifically including the following steps:

[0033] (1) Preparation of raw materials: prepare raw materials according to the mass percentage ratio: 48% of tobacco raw materials, 32% of atomizing agent, 5% of solid adhesive, 3% of tobacco flavor, 1% of fiber, and 11% of warm water;

[0034] (2) Dry material mixing and crushing: Put the tobacco leaf and solid adhesive (mixture of CMC, PAC and sodium alginate, the mass ratio is 1:1:1) into the crusher according to the proportion, and crush to 100 mesh. At this time, the dry materials After being crushed at high speed, it is evenly mixed;

[0035] (3) Wet material mixing and dispersing: fiber (wood pulp) and 30℃ warm water are poured into the material bucket in proportion, stirred at a high speed of 300r / min and mixed evenly, decomposed and dispersed, and then add the atomizing agent of the above step 1) mass ratio (Glycerol and propylene glyco...

Embodiment 2

[0039] A preparation method for heating and non-combustion reconstituted tobacco by rolling method, specifically comprising the following steps:

[0040] (1) Preparation of raw materials: prepare raw materials according to the mass percentage ratio: 55% of tobacco raw materials, 25% of atomizing agent, 8% of solid adhesive, 2% of tobacco flavor, 2% of fiber, and 8% of warm water;

[0041] Dry material mixing and crushing: Put the tobacco raw materials, solid adhesive (CMC, sodium alginate and egg curd, mass ratio 1:1:1) into the crusher according to the proportion, crush to 150 mesh, and then mix by high-speed crushing Evenly

[0042] (3) Mixing and dispersing of wet materials: fiber (tobacco fiber and wood pulp, mass ratio is 1:5) and 50℃ warm water are poured into the material bucket according to the proportion, 400r / min high-speed stirring and mixing uniformly, dissolve and disperse, and then add the above Step 1) The atomizing agent glycerin with the mass ratio, continue to mix ...

Embodiment 3

[0046] A method for preparing heated non-combustion reconstituted tobacco by rolling method, specifically including the following steps:

[0047] (1) Preparation of raw materials: prepare raw materials according to the mass percentage: 52% of tobacco raw materials, 25% of atomizers, 4% of solid adhesives, 4% of tobacco flavors, 3% of fibers, and 12% of warm water;

[0048] (2) Dry material mixing and crushing: Put the tobacco raw materials and solid adhesives (CMC, sodium alginate, ethyl cellulose, PAC, mass ratio 1:1:1:1) into the pulverizer according to the proportion, and pulverize to 200 At this time, it is pulverized at high speed and mixed evenly;

[0049] (3) Mixing and dispersing of wet materials: fiber (bamboo pulp and wood pulp, mass ratio 2:5) and 55℃ warm water are poured into the material bucket in proportion, stirred at a high speed of 500r / min and mixed evenly, dissolved and dispersed, and then added to the above Step 1) Atomizing agent with mass ratio (glycerol and e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of heat-not-burn reconstituted tobacco through a roll-in method and application thereof. On the basis of a roll-in method technology, a technical method isimproved, the heat-not-burn reconstituted tobacco is prepared, the problem of high-proportion addition of a fogging agent is solved, and a food-grade adhesive is used for evenly dispersing and solidifying the fogging agent into a tobacco material; the content of the fogging agent of the prepared heat-not-burn reconstituted tobacco is increased, the heat-not-burn reconstituted tobacco is evenly distributed at the same time, the surface is not sticky, the fiber content is increased, the tensile strength is improved, the machining resistance is good, smoke is evenly released during smoking, thesensory effect is good, and the simulated feeling of cigarette smoking is good.

Description

Technical field [0001] The invention relates to the field of heating and non-combustion new tobacco, in particular to a preparation method and application of heating non-combustion reconstituted tobacco by a rolling method. Background technique [0002] At present, new types of tobacco in the world are mainly divided into three categories, one is heat-not-burn tobacco products, the other is electronic cigarettes, and the third is smokeless tobacco products. Heat-not-burn tobacco products are also rich in various forms, such as Philip Morris' iQos, British American Tobacco's Glo, and Renault's carbon-heated cigarette Core. [0003] With the huge investment of the international tobacco giants, they have respectively formed their own heat-not-burn tobacco product technology. Generally speaking, the heat-not-burn materials are all reconstituted tobacco as the carrier, but the details are slightly different, which also forms their own Of craftsmanship. According to analysis, iQos ciga...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A24B3/14A24D1/00A24F47/00
CPCA24F47/008A24B3/14A24D1/00
Inventor 罗诚浩陈义坤唐向兵黄明刘华臣刘磊刘冰黄龙柯炜昌
Owner HUBEI CHINA TOBACCO IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com