Transfer coating and preparation method thereof

A technology for transferring coatings and raw materials, applied in the direction of conductive coatings, coatings, etc., can solve the problems of transfer paper surface damage, increase production costs, electrostatic mutual adhesion, etc., achieve easy separation, improve production quality, and improve the effect of mutual adhesion

Active Publication Date: 2020-07-21
常德洛恩全息材料科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] During the processing and transportation of transfer paper, it is often necessary to stack multiple sheets of transfer paper, but the general transfer paper is prone to electrostatic adhesion when stacked, and it needs to be carefully separated during subsequent processing or use, otherwise improper operation It is easy to cause damage to the surface of the transfer paper and be scrapped, which greatly reduces the production efficiency and increases the production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transfer coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] The preparation method of the above-mentioned transfer coating according to one embodiment of the present invention includes the following steps S1-S3:

[0029] S1. Weigh each raw material according to the parts by mass.

[0030] S2. Put the solvent, cellulose resin, polyacrylic resin and polyaniline into the reaction kettle, and stir at 60° C. to 80° C. for 1 to 2 hours.

[0031] Specifically, the stirring speed is 800rpm-1000rpm.

[0032] S3. Put the remaining raw materials into the reaction kettle, continue to stir for 1-2 hours, and obtain the transfer coating after filtering.

[0033] Specifically, the stirring speed is 450rpm-600rpm, and a 300-mesh filter is used for filtration.

[0034] The preparation method of the above-mentioned transfer coating is simple in process and easy to realize. The obtained transfer coating is used to prepare the transfer layer of the transfer paper, which can reduce the accumulation of static electricity on the transfer paper, and ...

Embodiment 1

[0037] Weigh each raw material according to the following parts by mass: 10 parts of cellulose resin, 8 parts of polyacrylic resin, 6 parts of polyaniline, 0.9 part of tin tetrachloride, 3 parts of tetraacicular zinc oxide whiskers, 0.2 part of polypyrrole, 0.3 part of sodium styrene sulfonate, 0.1 part of multilayer graphene, 0.5 part of defoamer (BYK-054), 0.5 part of leveling agent, 0.5 part of wetting agent, 0.5 part of cosolvent and 60 parts of n-propyl acetate. Put n-propyl acetate, cellulose resin, polyacrylic resin and polyaniline into the reaction kettle, heat the reaction kettle to 70°C, start the stirring device at 900rpm and stir for 1.5 hours. Then put the remaining raw materials into the reaction kettle, continue stirring at 500rpm for 1.5 hours, cool to 25°C and filter through a 300-mesh filter to obtain the transfer coating.

Embodiment 2

[0039] The experimental procedure of Example 2 is basically the same as that of Example 1, except that the raw material does not include tetraacicular zinc oxide whiskers.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a transfer coating and a preparation method thereof. The transfer coating is mainly prepared from the raw materials in parts by mass: 8 to 12 parts of cellulsic resin, 6 to 10parts of polyacrylic resin, 5 to 8 parts of polyaniline, 0.2 to 1.5 parts of stannic chloride, 0.5 to 4 parts of auxiliary agents and 55 to 65 parts of a solvent. The transfer coating provided by theinvention is used for preparing a transfer layer of transfer paper and can reduce accumulation of static electricity on the transfer paper, so that the problem that the transfer paper adheres to eachother because of static electricity when the transfer paper is stacked is solved; therefore, the transfer paper is easier to separate in a processing process, and meanwhile, paper surface damage andscrap caused by improper separation are also avoided; the production efficiency is effectively improved; the production cost is reduced; the market application prospect is broad.

Description

technical field [0001] The invention relates to the technical field of packaging, in particular to a transfer coating and a preparation method thereof. Background technique [0002] At present, in the packaging industry, transfer paper is widely used in tobacco, wine, tea and cosmetics because of its good performance in terms of gloss, smoothness, flexibility, environmental protection, printing adaptability and beautiful anti-counterfeiting effects. Packaging of high-end goods, especially tobacco products. [0003] During the processing and transportation of transfer paper, it is often necessary to stack multiple sheets of transfer paper, but the general transfer paper is prone to electrostatic adhesion when stacked, and it needs to be carefully separated during subsequent processing or use, otherwise improper operation It is easy to cause the surface of the transfer paper to be damaged and scrapped, which greatly reduces the production efficiency and increases the producti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D101/12C09D101/18C09D133/00C09D179/02C09D5/24C09D7/61C09D7/65
CPCC08L2201/04C08L2205/035C09D5/24C09D101/12C09D101/18C08L33/00C08L79/02C08K13/04C08K3/16C08K13/02
Inventor 余赞黄世水韦雪雪陈伟刘冬罗臻张勇军杜建军
Owner 常德洛恩全息材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap