Preparation method of water-resistant wallpaper

A technology for wallpaper and preparation steps, which is applied in the field of preparation of water-resistant wallpaper, which can solve the problems of poor fire-proof and flame-retardant effects and inability to effectively prevent fire, and achieve the effects of improving stability, improving water resistance, and high chemical stability

Inactive Publication Date: 2018-05-18
CHANGZHOU SIYU ENVIRONMENTAL PROTECTION MATERIAL SCI & TECH
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the fire-proof and flame-retardant effect of the prior art wallpaper is not good, and cannot meet the requirements of effective fire prevention.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of water-resistant wallpaper

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0025] Take soybeans and place them in a mortar and mash them for 30 minutes, soak the mashed soybeans with absolute ethanol for 2 hours, filter, remove the filter residue, and obtain soybean extracts. In parts by weight, take 50 parts of butyl acrylate, 15 parts of methyl Put hydroxyethyl acrylate and 30 parts of styrene in a beaker and stir for 15 minutes to obtain a mixed monomer; take 8 mL of soybean extract, 90 mL of deionized water and 40 mL of a mixed monomer and mix and stir for 10 minutes to obtain a monomer pre-emulsion, and another 4 mL Soybean extract and 40mL deionized water were added to the four-necked flask as the reaction bottom solution; 4.5g of ammonium persulfate was dissolved in 25mL of deionized water to obtain the initiator, and the above-mentioned four-necked flask was moved into a water bath at 80°C. Add two-fifths of the monomer pre-emulsion and one-third of the initiator into the four-necked flask, stir and react, and after the blue phase appears in t...

example 2

[0027] Get soybeans and place them in a mortar and mash them for 35 minutes, soak the mashed soybeans with absolute ethanol for 2.5 hours, filter, remove the filter residue, and obtain soybean extracts. In parts by weight, take 55 parts of butyl acrylate, hydroxyethyl acrylate and 35 parts of styrene were placed in a beaker and stirred for 17 minutes to obtain a mixed monomer; 9 mL of soybean extract, 95 mL of deionized water and 45 mL of a mixed monomer were mixed and stirred for 13 minutes to obtain a monomer pre-emulsion, and another Add 4.5mL of soybean extract and 45mL of deionized water into a four-necked flask as the reaction bottom solution; dissolve 4.7g of ammonium persulfate in 28mL of deionized water to obtain an initiator, and move the above-mentioned four-necked flask into a water bath at 83°C , add two-fifths of the monomer pre-emulsion and one-third of the initiator in the four-necked flask, stir the reaction, and after the blue phase appears in the reaction, ad...

example 3

[0029] Put the soybeans in a mortar and mash them for 40 minutes, soak the mashed soybeans with absolute ethanol for 3 hours, filter, remove the filter residue, and obtain the soybean extract. In parts by weight, take 60 parts of butyl acrylate, 20 parts of methyl Put hydroxyethyl acrylate and 40 parts of styrene in a beaker and stir for 20 minutes to obtain a mixed monomer; take 10 mL of soybean extract, 100 mL of deionized water and 50 mL of a mixed monomer and mix and stir for 15 minutes to obtain a monomer pre-emulsion, and another 5 mL Soybean extract and 50 mL of deionized water were added to a four-necked flask as the reaction bottom solution; 5.0 g of ammonium persulfate was dissolved in 30 mL of deionized water to obtain an initiator, and the above-mentioned four-necked flask was moved into a water bath at 85 °C, and Add two-fifths of the monomer pre-emulsion and one-third of the initiator in the four-necked flask, stir the reaction, and after the blue phase appears in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
thicknessaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of wallpaper preparation, in particular to a preparation method of water-resistant wallpaper. The method comprises the steps that a self-made soybean extraction solution and a self-made mixed monomer are mixed and dispersed to obtain a monomer pre-emulsion, the self-made soybean extraction solution is mixed with deionized water to obtain a reaction basesolution, and an initiating agent and the monomer pre-emulsion are subjected to two-step emulsification and polymerization to obtain a latex solution; dried paper pulp is treated to obtain modified paper fibers, the modified paper fibers, the deionized water and liquid paraffin are mixed to obtain mixed paper pulp, and the mixed paper pulp is treated to obtain the water-resistant wallpaper. According to the preparation method, water-repellent lecithin is used as an emulsifier, ethylene groups are introduced into latex solution polymers, cross-linking polymerization can be achieved, the stability of the latex solution is improved, the latex solution is dried and solidified to form latex film, the bonding performance and waterproof performance of the latex film can be improved, carboxyl inthe liquid paraffin can conduct an esterification reaction with hydroxyl, the hydrophily of the paper fibers is lowered, the water resistance of the wallpaper is improved accordingly, and the application prospect is wide.

Description

technical field [0001] The invention relates to the technical field of wallpaper preparation, in particular to a preparation method of water-resistant wallpaper. Background technique [0002] Wallpaper, also known as wallpaper, is a widely used interior decoration material. Because wallpaper has the characteristics of various colors, rich patterns, luxurious style, safety and environmental protection, convenient construction, and reasonable price, which are incomparable to many other interior decoration materials, it has been widely popularized in developed countries and regions such as Europe, America, Southeast Asia, and Japan. . Wallpapers are divided into many categories, such as coated wallpapers, laminated wallpapers, embossed wallpapers, etc. Usually bleached chemical wood pulp is used to produce base paper, and then processed by different processes, such as coating, printing, embossing or surface coating, and finally cut and packaged before leaving the factory. Be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/20D21F13/00D21H23/66D21H25/04D21H19/20C08F220/18C08F220/20C08F212/08C08F2/30
CPCC08F2/30C08F220/18C08F220/1804D21F13/00D21H19/20D21H23/66D21H25/04D21H27/20C08F220/20C08F212/08
Inventor 龙海燕何少雄张建初
Owner CHANGZHOU SIYU ENVIRONMENTAL PROTECTION MATERIAL SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com