Low-crack sensitive pipe fitting steel plate used under low temperature condition and manufacturing method thereof

A technology of low temperature conditions and manufacturing methods, applied in the metallurgical field, can solve problems such as poor weldability, and achieve the effects of low cold crack sensitivity coefficient, good low temperature toughness, and refinement of austenite grain size

Active Publication Date: 2018-05-15
JIANGYIN XINGCHENG SPECIAL STEEL WORKS CO LTD
View PDF8 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional steel for pipe fittings is usually designed with medium-high carbon + alloy composition to improve hardenability to ensure the performance requirements after heat treatment. For example, patent announcement number CN102011064 proposes a X80 grade low-temperature pipe fitting steel and its preparation and application, which can meet -46 The use of steel for pipe fittings with a thickness of 30-70mm under the condition of ℃, the range of C is 0.12-0.16%, which does not belong to the easily weldable steel, and the weldability of the material is obviously deteriorated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-crack sensitive pipe fitting steel plate used under low temperature condition and manufacturing method thereof
  • Low-crack sensitive pipe fitting steel plate used under low temperature condition and manufacturing method thereof
  • Low-crack sensitive pipe fitting steel plate used under low temperature condition and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-2

[0031] According to the scope of chemical composition and manufacturing method of the present invention, pretreatment of molten iron by KR—converter smelting—LF refining—RH vacuum degassing—continuous casting of 370-450mm thick continuous casting slab—continuous casting slab with cover and slow cooling—continuous casting slab inspection Cleaning—slab heating—high pressure water descaling—rolling—ACC cooling—air cooling—straightening—offline tempering process steps to manufacture steel plates for low crack sensitivity pipe fittings used under low temperature conditions of -60°C.

[0032] The specific process of the above-mentioned heating, rolling and slow cooling stages is: the 450mm thick continuous casting slab is heated to 1200°C and kept for 200 minutes (Example 1 and 2), and the continuous casting slab is descaled with high-pressure water after it is released from the furnace; then two-stage rolling is carried out , the first stage is rough rolling, the starting rolling temp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Grain sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a low-crack sensitive pipe fitting steel plate used under a low temperature condition. The mechanical component (wt%) of the steel plate comprises 0.03-0.08 of C, 0.2-0.35 of Si, 0.9-1.6 of Mn, 0.02-0.04 of Al, 0.01-0.07 of Nb, 0.01-0.07 of V, 0.01-0.02 of Ti, less than or equal to 0.15% of Nb+V+Ti, less than or equal to 0.5 of Cr, less than or equal to 0.5 of Ni, less than or equal to 0.4 of Mo, less than or equal to 0.3 of Cu, less than or equal to 0.18 of Pcm and the balance Fe and inevitable impurities. The method sequentially comprises the steps of KR molten iron pretreatment, converter smelting, LF refining, RH vacuum degassing, 370-450 mm thickness continuous casting blank continuous casting, continuous casting blank capping slow cooling, continuous casting blank checking and cleaning, casting blank heating, high-pressure water descaling, rolling, cooling, straightening and offline tempering. The steel plate structure is controlled to be a single tempered bainite structure, the grain size is within the range of 3-6 microns, and the steel plate has very excellent low-temperature toughness and can meet the use requirements of X70 pipeline steel underthe low-temperature condition of -60 DEG C.

Description

technical field [0001] The invention belongs to the technical field of metallurgy and relates to a steel plate for low crack sensitivity pipe fittings used under low temperature conditions and a manufacturing method. Background technique [0002] In long-distance pipeline engineering projects, in order to meet the requirements of long-distance transmission, it is necessary to build many compressor stations, gas transmission and distribution stations and other facilities. Therefore, a large amount of steel for station pipe fittings is required. In some alpine regions, especially for station pipe fittings used in low-temperature environments such as the China-Russia East Line, the limit temperature of the station is between -30°C and -50°C. On the basis of conventional pipe fitting steel, more Good low temperature performance. At the same time, during the entire manufacturing process of pipe fittings, the weldability of materials has a great influence on the low-temperature p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/12C22C38/14C22C38/16C22C38/08C22C38/38C22C38/28C22C38/26C22C38/24C22C38/22C22C38/20C22C38/58C22C38/50C22C38/48C22C38/46C22C38/44C22C38/42C21D8/02
CPCC21D8/0226C21D2211/002C22C38/02C22C38/04C22C38/06C22C38/08C22C38/12C22C38/14C22C38/16C22C38/20C22C38/22C22C38/24C22C38/26C22C38/28C22C38/38C22C38/42C22C38/44C22C38/46C22C38/48C22C38/50C22C38/58
Inventor 孙宪进许峰石艾来张明王小双方寿玉芦莎
Owner JIANGYIN XINGCHENG SPECIAL STEEL WORKS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products