Antifogging hybridization composite membrane for food packaging and preparation method thereof

A food packaging and composite film technology, applied in chemical instruments and methods, packaging, wrapping paper, etc., can solve problems such as poor anti-fog performance, and achieve the effects of improved anti-fog performance, light color, and increased mechanical properties

Inactive Publication Date: 2018-04-24
CHANGDE JINDE NEW MATERIAL TECH CO LTD
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a new type of anti-fog hybrid composite film for fo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antifogging hybridization composite membrane for food packaging and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Raw materials: base material (a mixture of high-density polyethylene and methyl methacrylate-butadiene-styrene copolymer, in which high-density polyethylene and methyl methacrylate-butadiene-styrene copolymer The weight ratio is 3:0.8) 100 parts by weight; the modified anti-fogging and dripping agent is 1.2 parts by weight; the graft of the base material is 2.0 parts by weight; and the nano inorganic filler is 0.3 parts by weight.

[0050] Mix base material, modified anti-fogging and dripping agent, base material grafts and nano-inorganic fillers evenly, and then blow them into a film with a PLE-330 Brabender plastic film blow molding machine to obtain an anti-fogging film with a thickness of 0.05 mm. Fog hybrid composite film.

Embodiment 2

[0052] Raw materials: base material (a mixture of high-density polyethylene and methyl methacrylate-butadiene-styrene copolymer, in which high-density polyethylene and methyl methacrylate-butadiene-styrene copolymer The weight ratio is 3:0.8) 106 parts by weight; modified anti-fogging and dripping agent 1.3 parts by weight; grafts of the base material 2.3 parts by weight; nano inorganic filler 0.4 parts by weight;

[0053] Mix base material, modified anti-fogging and dripping agent, base material grafts and nano-inorganic fillers evenly, and then blow them into a film with a PLE-330 Brabender plastic film blow molding machine to obtain an anti-fogging film with a thickness of 0.05 mm. Fog hybrid composite film.

Embodiment 3

[0055] Raw materials: base material (a mixture of high-density polyethylene and methyl methacrylate-butadiene-styrene copolymer, in which high-density polyethylene and methyl methacrylate-butadiene-styrene copolymer The weight ratio is 3:0.8) 110 parts by weight; modified anti-fogging agent 1.5 parts by weight; base material graft 2.5 parts by weight; nano inorganic filler 0.5 parts by weight;

[0056] Mix base material, modified anti-fogging and dripping agent, base material grafts and nano-inorganic fillers evenly, and then blow them into a film with a PLE-330 Brabender plastic film blow molding machine to obtain an anti-fogging film with a thickness of 0.05 mm. Fog hybrid composite film.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel antifogging hybridization composite membrane for food packaging. The antifogging hybridization composite membrane comprises, by weight, 100-110 parts of base material,1.2-1.5 parts of modified antifogging agent, 2.0-2.5 parts of base-material graft and 0.3-0.5 part of nano inorganic filler, wherein the base material is the mixture formed by high-density polyethylene and methyl methacrylate-butadiene-styrene copolymer; the modified antifogging agent is obtained by subjecting polyethylene glycol-polyglutamic acid-polyalanine triblock copolymer to protoporphyrin IX Mn(III) chloride and sodium lauryl sulfonate modification; the base-material graft is graft copolymer obtained by grafting methacrylic acid to the main chain of the methyl methacrylate-butadiene-styrene copolymer under the effect of an initiator. The prepared novel antifogging hybridization composite membrane is excellent in antifogging effect and excellent in mechanical performance.

Description

technical field [0001] The invention belongs to the technical field of food packaging, and in particular relates to an anti-fog hybrid composite film for food packaging and a preparation method thereof. Background technique [0002] Vegetables, fruits, meat and frozen food, because of their high moisture content or the large temperature difference between the inside and outside of the packaging bag, usually produce a layer of opaque water mist in the packaging bag, and this layer of opaque water mist will prevent the user from seeing It is impossible to visually judge the quality of the product. In order to solve this problem, the outer packaging of the product is usually packaged with an anti-fog film that prevents water vapor from forming fog on the surface of the film. [0003] The anti-fog film can change the surface properties of the material, and its anti-fog principle can be roughly divided into two categories: the first type is a hydrophilic anti-fog film, which red...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08L51/04C08L87/00C08L51/06C08L51/00C08K13/06C08K5/42C08K9/06C08K3/32C08K3/34C08K5/00C08J5/18C09K3/18B65D65/38
CPCB65D65/38C08J5/18C08J2323/06C08J2451/04C08J2487/00C08K3/34C08K5/0091C08K5/42C08K9/06C08K13/06C08K2003/325C08K2201/011C09K3/18
Inventor 余赞田璐钟文罗臻韦雪雪
Owner CHANGDE JINDE NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap