Rake tooth brick without grain defect and preparation process thereof

A preparation process and technology of rake-toothed bricks, which are applied in the field of architectural ceramics, can solve the problems of reducing the decorative effect of rake-toothed bricks, uneven texture distribution, and reduced to defective products, and achieve good density, good sintering degree and anti-corrosion The effect of folding strength and process is simple and convenient

Active Publication Date: 2018-03-30
FOSHAN HENGTAI HONGSHI CERAMIC CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the existing rake-toothed bricks usually use the mud billet raw material in the extrusion molding process, and use the rake-tooth device to scrape the surface of the formed mud billet to form the rake-toothed texture. However, due to the existing mud billet raw materials The clinker particles are usually fired ceramic or sintered brick waste particles such as ceramic waste particles, smoked brick waste particles, split brick waste particles or frosted brick waste particles, to ensure that the strength of the bricks can meet the requirements of the process , but it often leads to the granular polar raw materials formed in the green body after sintering, which are extremely easy to form broken lines and uneven texture distribution when scratching the rake tooth lines, and overlap defects occur, which greatly reduces The decorative effect of the rake-toothed brick surface is finally reduced to a problem of defective products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rake tooth brick without grain defect and preparation process thereof
  • Rake tooth brick without grain defect and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1-a kind of preparation technology of the rake-tooth brick without grain defect, comprises the following steps:

[0022] 1. Preparation of ceramic brick plain mud:

[0023] Carry out weighing according to the proportioning of mud billet raw material as follows:

[0024] raw material

plastic clay

vitrified clinker particles

High alumina clay

Flux

Pigment for billet

Proportion

50％

15％

6％

20％

9％

[0025] Among them, vitrified clinker particles are vitrified clinker particles formed by mixing 30% of 20-40 mesh particles, 50% of 50-70 mesh particles and 20% of 80-100 mesh particles;

[0026] Mix the above raw materials with water and knead evenly to make mud, the amount of water added is 17-20% of the weight of the mud, and after aging the mud for 24-48 hours, use a screen granulator to make mud granules;

[0027] 2. Preparation of finished rake tooth bricks:

[0028] (1) Extrude the mud particles into a v...

Embodiment 2

[0030] Embodiment 2-a kind of preparation technology of the rake-tooth brick without grain defect, comprises the following steps:

[0031] 1. Preparation of ceramic brick plain mud:

[0032] Carry out weighing according to the proportioning of mud billet raw material as follows:

[0033] raw material

plastic clay

vitrified clinker particles

High alumina clay

Flux

Pigment for billet

Lithium feldspar

Proportion

60％

10％

4％

18％

6％

2％

[0034] Among them, vitrified clinker particles are vitrified clinker particles mixed with 15% of 20-40 mesh particles, 65% of 50-70 mesh particles and 20% of 80-100 mesh particles; The diameter is 200 mesh;

[0035] Mix the above raw materials with water and knead evenly to make mud, the amount of water added is 17-20% of the weight of the mud, and after aging the mud for 24-48 hours, use a screen granulator to make mud granules;

[0036] 2. Preparation of finished rake tooth bricks: ...

Embodiment 3

[0039] Embodiment 3-a kind of preparation technology of the rake tooth brick without grain defect, comprises the following steps:

[0040] 1. Preparation of ceramic brick plain mud:

[0041] Carry out weighing according to the proportioning of mud billet raw material as follows:

[0042] raw material

plastic clay

vitrified clinker particles

High alumina clay

Flux

Pigment for billet

Lithium feldspar

Attapulgite

Proportion

55％

12.5％

5％

15％

6％

1.5％

5％

[0043]Among them, vitrified clinker particles are vitrified clinker particles mixed with 15% of 20-40 mesh particles, 50% of 50-70 mesh particles and 35% of 80-100 mesh particles; The diameter is 300 mesh;

[0044] Mix the above raw materials with water and knead evenly to make mud, the amount of water added is 17-20% of the weight of the mud, and after aging the mud for 24-48 hours, use a screen granulator to make mud granules;

[0045] 2. Preparation of fin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a rake tooth brick without a grain defect and a preparation process thereof. The rake tooth brick comprises the following mud billet raw materials: 50-60 percent by weight ofa plastic clay material, 10-15 percent by weight of vitrified clinker particle, 4-6 percent by weight of high-aluminum clay, 10-20 percent by weight of solvent and 0-10 percent by weight of billet pigment. The rake tooth brick without the grain defect and the preparation process thereof, provided by the invention, have the benefit that not only is the prepared rake tooth brick high in sintering degree and breaking strength, but also continuous, even and dense rake tooth textures can be formed on the brick surface of the rake tooth brick.

Description

technical field [0001] The invention relates to the technical field of architectural ceramics, in particular to a rake-tooth brick without texture defects and a preparation process thereof. Background technique [0002] At present, the existing rake-toothed bricks usually use the mud billet raw material in the extrusion molding process, and use the rake-tooth device to scrape the surface of the formed mud billet to form the rake-toothed texture. However, due to the existing mud billet raw materials The clinker particles are usually fired ceramic or sintered brick waste particles such as ceramic waste particles, smoked brick waste particles, split brick waste particles or frosted brick waste particles, to ensure that the strength of the bricks can meet the requirements of the process , but it often leads to the granular polar raw materials formed in the green body after sintering, which are extremely easy to form broken lines and uneven texture distribution when scratching th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/132
CPCC04B33/1324C04B2235/3201C04B2235/3203C04B2235/3208C04B2235/3472C04B2235/3481C04B2235/656C04B2235/96Y02P40/60
Inventor 陈锦豪
Owner FOSHAN HENGTAI HONGSHI CERAMIC CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com