A three-dimensional graphene-based wave-absorbing metamaterial substrate and preparation method thereof

A graphene-based, metamaterial technology, applied in the field of materials, can solve the problems of high density, large thickness, and the stealth technology needs to be improved, and achieve the effect of light weight and low density

Active Publication Date: 2022-03-04
LUOYANG INST OF CUTTING EDGE TECH +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because traditional wave-absorbing metamaterials have problems such as high density, large thickness, and stealth technology to be improved, the research and development of new wave-absorbing metamaterials such as graphene / 3D graphene has become more and more important.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A three-dimensional graphene-based wave-absorbing metamaterial substrate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] 0.1g three-dimensional graphene powder is added in 100g polyurethane, and add 2g dicumyl peroxide, 0.5g stearic acid and 0.5g silane coupling agent;

[0024] Put it into a 70°C internal mixer and mix evenly. After the mixture is obtained, put it into a hot press, press it at a pressure of 25MPa and a temperature of 170°C for 10 minutes, and dry it to obtain a three-dimensional graphene-based wave-absorbing metamaterial substrate. .

Embodiment 2

[0026] 1g of three-dimensional graphene powder is added to 100g of EPDM rubber, and 3g of dicumyl peroxide, 1.5g of stearic acid and 1.5g of silane coupling agent are added;

[0027] Put it into a 70°C internal mixer and mix evenly. After the mixture is obtained, put it into a hot press, press it at a pressure of 25MPa and a temperature of 170°C for 10 minutes, and dry it to obtain a three-dimensional graphene-based wave-absorbing metamaterial substrate. .

Embodiment 3

[0029] 3g three-dimensional graphene powder is added to 100g silicone rubber, and 4g dicumyl peroxide, 3g stearic acid and 3g silane coupling agent are added;

[0030] Put it into a 70°C internal mixer and mix evenly. After the mixture is obtained, put it into a hot press, press it at a pressure of 25MPa and a temperature of 180°C for 40 minutes, and dry it to obtain a three-dimensional graphene-based wave-absorbing metamaterial substrate. .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a three-dimensional graphene-based wave-absorbing metamaterial substrate and a preparation method thereof, the method comprising: adding three-dimensional graphene to raw rubber, adding a vulcanizing agent and an auxiliary agent; putting it into a banbury mixer and mixing evenly , to obtain a mixture; putting the mixture into a hot press machine for thermocompression molding, and drying to obtain a three-dimensional graphene-based wave-absorbing metamaterial substrate. The three-dimensional graphene-based wave-absorbing metamaterial substrate achieves a good dispersion of three-dimensional graphene powder in raw rubber, and the use of three-dimensional graphene can regulate the electromagnetic parameters of the wave-absorbing metamaterial substrate, which can realize the metamaterial substrate It has a wide frequency band and high absorption, and can be used as a potential application material for future stealth weapons and equipment.

Description

technical field [0001] The invention relates to the field of materials, more specifically, to a three-dimensional graphene-based wave-absorbing metamaterial substrate and a preparation method thereof. Background technique [0002] Absorbing metamaterials refer to a class of materials that can effectively absorb incident electromagnetic waves and make them scatter and attenuate. It converts incident electromagnetic waves into heat energy or other energy forms through various loss mechanisms of materials to achieve the purpose of absorbing waves. It has great application prospects in controlling electromagnetic pollution and manufacturing stealth materials. [0003] Three-dimensional (3D) graphene usually refers to a two-dimensional (2D) graphene assembly with a 3D structure, and is a new functional material in the field of graphene chemistry in recent years. Integrating 2D graphene sheets into an assembly with a 3D structure can effectively regulate the electrical, optical, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L75/04C08L23/16C08L83/04C08L23/22C08K13/04C08K7/24C08K5/14C08K5/09C09K3/00
CPCC09K3/00C08K5/09C08K5/14C08K7/24C08K13/04C08K2201/011C08L75/04C08L23/16C08L83/04C08L23/22
Inventor 不公告发明人
Owner LUOYANG INST OF CUTTING EDGE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products